The overarching goal of present study is to investigate the effects of Ir and Pd additions on the oxidation behaviour of PtAl coatings. Prior to depositing standard PtAl coating, Ir layer was electroplated by IrBr3 aqueous solution while Pd layer was prepared using electroless deposition. Comparing with normal PtAl coating, cyclic oxidation tests were carried out on both the Ir- and Pd-modified aluminide coatings. The results showed that Ir-modified PtAl coating exhibited better oxidation resistance than both Pd-modified and normal PtAl coatings because Ir partly served as diffusion barrier to reserve Al while Pd did not.
This is a preview of subscription content, access via your institution.
Buy single article
Instant access to the full article PDF.
Tax calculation will be finalised during checkout.
D.K. Das, Prog. Mater. Sci. 58, 151 (2013)
R.R. Adharapurapu, J. Zhu, V.S. Dheeradhada, D.M. Lipkin, T.M. Pollock, Acta Mater. 77, 379 (2014)
S.J. Hong, G.H. Hwang, W.K. Han, S.G. Kang, Intermetallics 17, 381 (2009)
M.J. Li, X.F. Sun, H.R. Guan, X.X. Jiang, Z.Q. Hu, Surf. Coat. Technol. 185, 172 (2004)
C. Huang, K. Nishida, Y. Yamabe-Mitarai, H. Harada, Intermetallics 10, 893 (2002)
F.R. Lamastra, I. Cacciotti, A. Bellucci, F. Nanni, Intermetallics 22, 241 (2012)
G. Fisher, W.Y. Chan, P.K. Datta, J.S. Burnell-Gray, Plat. Met. Rev. 43, 59 (1999)
A. Suzuki, Y. Wu, A. Yamaguchi, H. Murakam, C.M.F. Rae, Oxid. Met. 68, 53 (2007)
A. Yamaguchi, H. Murakami, S. Kuroda, H. Imai, Mater. Trans. 48, 2422 (2007)
Y.N. Wu, A. Yamaguchi, H. Murakami, S. Kuroda, J. Mater. Res. 22, 206 (2011)
C. Rao, D. Trivedi, Coord. Chem. Rev. 249, 613 (2005)
G. Sheela, M. Pushpavanam, S. Pushpavanam, Bull. Electrochem. 15, 208 (1999)
G. Sheela, M. Pushpavanam, S. Pushpavanam, Tran. Inst. Met. Finish. 78, 191 (2000)
F. Pearlstein, R.F. Weightman, U.S. Patent 3,754,939, 28 August 1973
N.N. Greenwood, A. Earnshaw, Chemistry of the Elements, 2nd edn. (Butterworth-Heinemann, Oxford; Boston, 1997).
F. Wu, H. Murakami, Y. Yamabe-Mitarai, H. Harada, H. Katayama, Y. Yamamoto, Surf. Coat. Technol. 184, 24 (2004)
S. Bose, High Temperature Coatings (Elsevier Butterworth-Heinemann, Amsterdam; Boston, 2007).
Z.B. Bao, H. Murakami, Y. Yamabe-Mitarai, Corros. Sci. 53, 1224 (2011)
M. Ode, T. Abe, H. Murakami, Y.Y. Mitarai, T. Hara, K. Nagashio, C. Kocer, H. Onodera, Intermetallics 16, 1171 (2008)
Metals Handbook, Metals Park, Ohio: ASM, 8th edn. (1973)
This work was sponsored by the ‘Liaoning BaiQianWan Talents’ Program and partly supported by the R & D Program in Key Fields of Guangdong Province (No. 2019B010936001).
Available online at http://link.springer.com/journal/40195.
About this article
Cite this article
Qian, LY., Wang, J., Guo, YS. et al. Influences of Iridium and Palladium on Oxidation Resistance of PtAl Coating. Acta Metall. Sin. (Engl. Lett.) (2021). https://doi.org/10.1007/s40195-020-01185-y
- Thermal barrier coating
- PtAl coating
- Oxidation resistance