Abstract
In pressurized water reactor, fretting corrosion has become the main reason for the failure of 690TT heat exchanger tubes. The effect of temperature on the fretting corrosion behavior between 690TT tube and 405 stainless steel (SS) bar has been studied during 106 fretting cycles. The overall average coefficient of friction (COF) values descends with an increase in test temperature, while the width of worn scar becomes wider. The severest fretting corrosion happens when the test temperature is at 100 °C. The wear mechanism differs at different test temperatures, from adhesive wear at room temperature to abrasive wear and delamination at 100 °C, to abrasive wear at 200 °C. Deformation slips, high residual strain concentration, and micro-cracks are found which are disadvantageous for the further service performance of the tubes.
Similar content being viewed by others
References
R.S. Dutta, R. Tewari, P.K. De, Corros. Sci. 49, 303 (2007)
J. Benson, Overview of steam generator operating experience. Paper presented at the 4th international symposium on materials and reliability in nuclear power plants, Shenyang, China, 21 September 2015
P. Sherburne, Stress Corrosion cracking of alloy 600 &690 steam generator tubing. Paper presented at international seminar on welding and non-destructive examination in nuclear power plants, Suzhou, China, 27 June 2009
H.J. Connors, Nucl. Technol. 55, 311 (2017)
M.H. Attia, Tribol. Int. 39, 1294 (2006)
S.H. Jeong, C.W. Cho, Y.Z. Lee, Tribol. Int. 38, 283 (2005)
J. Li, B.B. Yang, Y.H. Lu, L. Xin, Z.H. Wang, T. Shoji, Tribol. Int. 116, 147 (2017)
J.K. Hong, I.S. Kim, C.Y. Park, E.S. Kim, Wear 259, 349 (2005)
X. Mi, Z.B. Cai, X.M. Xiong, H. Qian, L.C. Tang, Y.C. Xie, J.F. Peng, M.H. Zhu, Tribol. Int. 100, 400 (2016)
Z.H. Wang, Y.H. Lu, J. Li, T. Shoji, Tribol. Int. 95, 162 (2016)
J. Li, B. Yang, Y. Lu, L. Xin, Z. Wang, T. Shoji, Mater. Charact. 131, 224 (2017)
J. Li, Y.H. Lu, Wear 304, 223 (2013)
L. Xin, B.B. Yang, Z.H. Wang, J. Li, Y. Lu, T. Shoji, Wear 368, 210 (2016)
X. Guo, P. Lai, L. Tang, J. Wang, L. Zhang, Tribol. Int. 116, 155 (2017)
L. Xin, Y.H. Lu, Y. Otsuka, Y. Mutoh, Z.H. Wang, T. Shoji, Mater. Charact. 134, 260 (2017)
J.Y. Yun, M.C. Park, G.S. Shin, J.H. Heo, D.I. Kim, S.J. Kim, Wear 313, 83 (2014)
L. Xin, Y. Lu, T. Shoji, Mater. Charact. 131, 157 (2017)
H. Sun, X. Wu, E.H. Han, Corros. Sci. 51, 2840 (2012)
I. Betova, M. Bojinov, V. Karastoyanov, P. Kinnunen, T. Saario, Corros. Sci. 58, 20 (2012)
Z.M. Zhang, J.Q. Wang, E.H. Han, W. Ke, Corros. Sci. 53, 3623 (2011)
J.B. Huang, X.H. Liu, E.H. Han, X.Q. Wu, Corros. Sci. 53, 3254 (2011)
W.J. Kuang, X.Q. Wu, E.H. Han, Corros. Sci. 63, 259 (2012)
J.Y. Yun, H.S. Lee, D.H. Hur, W.S. Kang, C.H. Bae, S.J. Kim, Wear 368, 344 (2016)
X. Guo, P. Lai, L. Tang, J. Lu, J. Wang, L. Zhang, Wear 400–401, 119 (2018)
S.M. Hong, I.S. Kim, Wear 259, 356 (2005)
H.L. Ming, X.C. Liu, Z.M. Zhang, J.Q. Wang, E.H. Han, Tribol. Int. 126, 133 (2018)
Z.R. Zhou, L. Vincent (eds.), Fretting Wear (Science Press, Beijing, 2002)
Q. Luo, Q.S. Wu, Q. Xu, J. Li, Phys. Exam. Test 32, 3 (2014)
J.Z. Wang, J.Q. Wang, H.L. Ming, Z.M. Zhang, E.H. Han, J. Mater. Sci. Technol. 34, 1419 (2018)
P. Lai, X. Gao, L. Tang, X. Guo, L. Zhang, Nucl. Eng. Des. 327, 51 (2018)
W.J. Kuang, X.Q. Wu, E.H. Han, J.C. Rao, Corros. Sci. 53, 3853 (2011)
L. Xin, Z. Wang, J. Li, Y. Lu, T. Shoji, Mater. Charact. 115, 32 (2016)
F. Huang, J.Q. Wang, E.H. Han, W. Ke, J. Mater. Sci. Technol. 28, 562 (2012)
D. Chen, E.H. Han, X. Wu, Corros. Sci. 111, 518 (2016)
L. Xin, B. Yang, J. Li, Y. Lu, T. Shoji, Corros. Sci. 123, 116 (2017)
H.L. Ming, Z.M. Zhang, P.Y. Xiu, J.Q. Wang, E.H. Han, W. Ke, Acta Metall. Sin. (Engl. Lett.) 29, 848 (2016)
X.Q. Wu, S. Xu, E.H. Han, W. Ke, Acta Metall. Sin. (Engl. Lett.) 47, 790 (2011)
Acknowledgements
This work is supported by the National Natural Science Foundation of China (No. 51771211), the Large-scale advanced PWR major projects (No. 2017ZX06002006), the Liaoning Provincial Natural Science Foundation of China (No. 20180540076), and the open-ended fund of the CAS Key laboratory of Nuclear Materials and Safety Assessment (Institute of Metal Research, Chinese Academy of Sciences, China) (Nos. 2019NMSAKF02 and 2017NMSAKF04). The authors are grateful for the help of 3D surface morphology analysis from Dr. Hui Feng at IMR, CAS.
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Liu, XC., Ming, HL., Zhang, ZM. et al. Effects of Temperature on Fretting Corrosion Between Alloy 690TT and 405 Stainless Steel in Pure Water. Acta Metall. Sin. (Engl. Lett.) 32, 1437–1448 (2019). https://doi.org/10.1007/s40195-019-00929-9
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-019-00929-9