Abstract
A 2.5-mm Fe72.5B15.6Si7.8Nb1.7Zr1.7Cu0.7 glassy rod was successfully fabricated using copper mold casting. The introduction of Cu resulted in the formation of large quantities of α-Fe nanoparticles embedded in the glassy matrix after isothermal annealing. The Fe72.5B15.6Si7.8Nb1.7Zr1.7Cu0.7 nanocrystalline alloy exhibited high saturation magnetization (~ 1.26 T) and a low coercive force (~ 0.8 A/m) after annealing at 833 K for 15 min due to the precipitation of ~ 15-nm-sized α-Fe nanoparticles in the glassy matrix. The structural evolution of the FeBSiNbZrCu amorphous alloy during the annealing process was discussed using a dual-cluster model.
Similar content being viewed by others
References
Y. Yoshizawa, S. Oguma, K. Yamauchi, J. Appl. Phys. 64, 6044 (1988)
K. Suzuki, A. Makino, A. Inoue, T. Masumoto, J. Appl. Phys. 74, 3316 (1993)
M.A. Willard, M.Q. Haung, D.E. Laughlin, M.E. Mchenry, J.O. Cross, V.G. Harris, C. Franchetti, J. Appl. Phys. 85, 4421 (1999)
A. Makino, H. Men, K. Yubuta, K. Yubuta, A. Inoue, J. Appl. Phys. 105, 07A308 (2009)
M.J. Shi, R. Li, J.F. Wang, Z.Q. Liu, X.K. Luo, T. Zhang, Philos. Mag. 93, 2182 (2013)
G. Herzer, Acta Mater. 61, 718 (2013)
Y.H. Li, X.J. Jia, Y.Q. Xu, C.T. Chang, G.Q. Xie, W. Zhang, J. Alloys Compd. 722, 859 (2017)
A. Inoue, B.L. Shen, J. Mater. Res. 18, 2799 (2003)
T.S. Chin, C.Y. Lin, M.C. Lee, R.T. Huang, S.M. Huang, Intermetallics 16, 52 (2008)
A. Urata, H. Matsumoto, S. Sato, A. Makino, J. Appl. Phys. 105, 07A324 (2009)
X. Li, H. Kato, K. Yubuta, A. Makino, A. Inoue, Mater. Sci. Eng. A 527, 2598 (2010)
J.E. Gao, H.X. Li, Z.B. Jiao, Y. Wu, Y.H. Chen, T. Yu, Z.P. Lu, Appl. Phys. Lett. 99, 052504 (2011)
Z.Z. Li, A.D. Wang, C.T. Chang, Y.G. Wang, B.S. Dong, S.X. Zhou, Intermetallics 54, 225 (2014)
Z.Z. Li, S.X. Zhou, G.Q. Zhang, C.L. Zhao, L. Xue, R. Xiang, Prog. Nat. Sci. Mater. Interfaces 25, 263 (2015)
T.H. Noh, M.B. Lee, H.J. Kim, I.K. Kang, J. Appl. Phys. 67, 5568 (1990)
K. Hono, D.H. Ping, M. Ohnuma, H. Onodera, Acta Mater. 47, 997 (1999)
M.E. Mchenry, M.A. Willard, D.E. Laughlin, Prog. Mater. Sci. 44, 291 (1999)
M. Ohta, Y. Yoshizawa, Appl. Phys. Exp. 2, 023005 (2013)
Y. Wu, H.X. Li, J.E. Gao, H. Wang, X.J. Liu, M.K. Miller, H. Bei, Y.F. Gao, Z.P. Lu, J. Alloys Compd. 688, 822 (2016)
S. Jafari, A. Beitollahi, B.E. Yekta, T. Ohkubo, V. Budinsky, M. Marsilius, G. Herzer, K. Hono, J. Alloys Compd. 674, 136 (2016)
Y.X. Geng, Y.M. Wang, J.B. Qiang, C. Dong, H.B. Wang, O. Tegus, Acta Metall. Sin. 52, 1459 (2016)
Y.X. Geng, Y.M. Wang, J.B. Qiang, G.F. Zhang, C. Dong, O. Tegus, Intermetallics 67, 138 (2015)
Y.X. Geng, Y.M. Wang, Z.R. Wang, J.B. Qiang, H.B. Wang, C. Dong, O. Tegus, Mater. Des. 106, 69 (2016)
Y.X. Geng, K.M. Han, Y.M. Wang, J.B. Qiang, C. Dong, G.F. Zhang, O. Tegus, P. Häussler, Acta Metall. Sin. 51, 1017 (2015)
Y.X. Geng, Y.M. Wang, J.B. Qiang, G.F. Zhang, C. Dong, P. Häussler, J. Non-Cryst. Solids 432, 453 (2016)
Y.X. Geng, Z.J. Zhang, Z.R. Wang, Y.M. Wang, J.B. Qiang, C. Dong, H.B. Wang, O. Tegus, J. Non-Cryst. Solids 450, 1 (2016)
Y.X. Geng, X. Lin, J.B. Qiang, Y.M. Wang, C. Dong, Acta Metall. Sin. 53, 833 (2017)
S.S. Shin, H.K. Kim, J.C. Lee, I.M. Park, Acta Metall. Sin. (Engl. Lett.) 31, 273 (2018)
Z.Q. Zhang, P. Sharma, A. Makino, J. Appl. Phys. 112, 103902 (2012)
G. Herzer, J. Magn. Magn. Mater. 294, 99 (2005)
A. Takeuchi, A. Inoue, Mater. Trans. 46, 2817 (2005)
P.B. Chen, T. Liu, F.Y. Kong, A.D. Wang, C.Y. Yu, G. Wang, C.T. Chang, X.M. Wang, J. Mater. Sci. Technol. 34, 793 (2018)
Y.P. Ma, D.D. Dong, C. Dong, L.J. Luo, Q. Wang, J.B. Qiang, Y.M. Wang, Sci. Rep. 5, 17880 (2015)
G.J. Naz, D.D. Dong, Y.X. Geng, Y.M. Wang, C. Dong, Sci. Rep. 7, 9150 (2017)
Acknowledgements
This work was financially supported by the National Key R&D Program of China (No. 2016YFB1100103), the National Natural Science Foundation of China (No. 51801079), the Natural Science Foundation for Young Scientists of Jiangsu, China (Nos. BK20180985 and BK20180987), and the Natural Science Foundation in Higher Education of Jiangsu, China (No. 18KJB430011).
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Geng, YX., Ding, HY., Wang, DP. et al. Formation and Structural Evolution of Fe72.5B15.6Si7.8Nb1.7Zr1.7Cu0.7 Nanocrystalline Alloy. Acta Metall. Sin. (Engl. Lett.) 33, 313–318 (2020). https://doi.org/10.1007/s40195-019-00924-0
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-019-00924-0