Recent Research on the Deformation Behavior of Particle Reinforced Magnesium Matrix Composite: A Review

  • Published:
Acta Metallurgica Sinica (English Letters) Aims and scope

Abstract

Particle reinforced magnesium matrix composite (PMMC) possesses the merits of high specific strength, high specific modulus, better dimensional stability, good wear resistance and lower production cost, which is thought as a promising material in the field of aerospace, automobile, electronic communication, etc. To eliminate the casting defect, the PMMC is usually experienced hot deformation process. The present paper mainly focuses on the deformation behavior of PMMCs. First, the development of PMMCs based on particle size is introduced. Then, the hot deformation technology and deformation mechanism of PMMCs at elevated temperature are given and analyzed, respectively. After reviewing the dynamic recrystallization and texture of PMMCs, its future development is suggested based on the current research progress.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1

Reproduced from [67], with permission from Elsevier

Fig. 2

Reproduced from [92], with permission from Elsevier

Fig. 3

Reproduced from [96], with permission from Elsevier

Fig. 4

Reproduced from [101], with permission from Elsevier

Fig. 5

Reproduced from [56], with permission from Elsevier

Fig. 6

Reproduced from [92], with permission from Elsevier

Similar content being viewed by others

References

  1. F.S. Pan, M.B. Yang, X.H. Chen, J. Mater. Sci. Technol. 32, 1211 (2016)

    Article  Google Scholar 

  2. X.J. Wang, D.K. Xu, R.Z. Wu, X.B. Chen, Q.M. Penge, L. Jin, Y.C. Xing, Z.Q. Zhang, Y. Liu, X.H. Cheng, G. Chen, K.K. Deng, H.Y. Wang, J. Mater. Sci. Technol. 34, 245 (2018)

    Article  Google Scholar 

  3. S.H. You, Y.D. Huang, K.U. Kainer, N. Hort, J. Magnes. Alloy. 5, 239 (2017)

    Article  CAS  Google Scholar 

  4. K.K. Alaneme, E.A. Okotete, J. Magnes. Alloy. 5, 460 (2017)

    Article  CAS  Google Scholar 

  5. X.J. Wang, X.S. Hu, W.Q. Liu, J.F. Du, K. Wu, Y.D. Huang, Mater. Sci. Eng. A. 682, 491 (2017)

    Article  CAS  Google Scholar 

  6. M. Haghshenas, J. Magnes. Alloy. 5, 189 (2017)

    Article  CAS  Google Scholar 

  7. X.J. Wang, K.B. Nie, X.J. Sa, X.S. Hu, K. Wu, M.Y. Zheng, Mater. Sci. Eng. A 534, 60 (2012)

    Article  CAS  Google Scholar 

  8. Q.C. Jiang, H.Y. Wang, B.X. Ma, Y. Wang, F. Zhao, J. Alloys Compd. 386, 177 (2005)

    Article  CAS  Google Scholar 

  9. M.K. Habibi, A.M.S. Hamouda, M. Gupta, Compos. Sci. Technol. 72, 290 (2012)

    Article  CAS  Google Scholar 

  10. X.Q. Zhang, H.W. Wang, L.H. Liao, X.Y. Teng, N.H. Ma, Mater. Lett. 59, 2105 (2005)

    Article  CAS  Google Scholar 

  11. C.F. Zhang, T.Y. Fan, W. Cao, J. Ding, D. Zhang, Compos. Sci. Technol. 69, 2688 (2009)

    Article  CAS  Google Scholar 

  12. H.Z. Ye, X.Y. Liu, J. Mater. Sci. 39, 6153 (2004)

    Article  CAS  Google Scholar 

  13. H. Hu, J. Mater. Sci. 33, 1579 (1998)

    Article  CAS  Google Scholar 

  14. A. Luo, Metall. Mater. Trans. A 26A, 2445 (1994)

    Google Scholar 

  15. X.J. Wang, K. Wu, D.L. Peng, H.F. Zhang, M.Y. Zheng, W.X. Wang, Trans. Nonferrous Met. Soc. China 16, 1840 (2006)

    CAS  Google Scholar 

  16. L.Q. Chen, Y.T. Yao, Acta Metall. Sin. (Engl. Lett.) 27, 762 (2014)

    Article  CAS  Google Scholar 

  17. Y. Cai, M.J. Tan, G.J. Shen, H.Q. Su, Mater. Sci. Eng. A 282, 232 (2000)

    Article  Google Scholar 

  18. X.J. Wang, K. Wu, W.X. Huang, H.F. Zhang, M.Y. Zheng, D.L. Peng, Compos. Sci. Technol. 67, 2253 (2007)

    Article  CAS  Google Scholar 

  19. S.A. Sajjadi, H.R. Ezatpour, M.P. Torabi, Mater. Des. 34, 106 (2012)

    Article  CAS  Google Scholar 

  20. X.J. Wang, N.Z. Wang, L.Y. Wang, X.S. Hu, K. Wu, Y.Q. Wang, Y.D. Huang, Mater. Des. 57, 638 (2014)

    Article  CAS  Google Scholar 

  21. A.R. Vaidya, J.J. Lewandoowski, Mater. Sci. Eng. A 220, 85 (1996)

    Article  Google Scholar 

  22. T.J. Chen, X.D. Jiang, Y. Ma, Y.D. Li, Y. Hao, J. Alloys Compd. 496, 218 (2010)

    Article  CAS  Google Scholar 

  23. Z. Zhang, D.L. Chen, Scripta Mater. 54, 1321 (2006)

    Article  CAS  Google Scholar 

  24. K.B. Nie, K.K. Deng, X.J. Wang, W.M. Gan, F.J. Xu, K. Wu, M.Y. Zheng, J. Alloys Compd. 622, 1018 (2015)

    Article  CAS  Google Scholar 

  25. S.F. Hassan, M. Gupta, Mater. Sci. Eng. A 392, 163 (2005)

    Article  CAS  Google Scholar 

  26. S.C. Tjong, Adv. Eng. Mater. 9, 639 (2007)

    Article  CAS  Google Scholar 

  27. L.Y. Chen, D. Weiss, Manuf. Lett. 2, 62 (2013)

    Article  CAS  Google Scholar 

  28. L.Y. Chen, J.Y. Peng, Scripta Mater. 69, 634 (2013)

    Article  CAS  Google Scholar 

  29. K.B. Nie, X.J. Wang, K. Wu, X.S. Hu, M.Y. Zheng, L. Xu, Mater. Sci. Eng. A 528, 8709 (2011)

    Article  CAS  Google Scholar 

  30. M. Habibnejad-Korayem, R. Mahmudi, W.J. Poole, Mater. Sci. Eng. A 519, 198 (2009)

    Article  CAS  Google Scholar 

  31. C.S. Goh, J. Wei, L.C. Lee, M. Gupta, Acta Mater. 55, 5115 (2007)

    Article  CAS  Google Scholar 

  32. Y. Radi, R. Mahmudi, Mater. Sci. Eng. A 527, 2764 (2010)

    Article  CAS  Google Scholar 

  33. S. Hwang, C. Nishimura, Scripta Mater. 44, 2457 (2001)

    Article  CAS  Google Scholar 

  34. S.F. Hassan, M. Gupta, J. Alloys Compd. 457, 244 (2008)

    Article  CAS  Google Scholar 

  35. K.K. Deng, K. Wu, Y.W. Wu, K.B. Nie, M.Y. Zheng, J. Alloys Compd. 504, 542 (2010)

    Article  CAS  Google Scholar 

  36. H. Ferkel, B.L. Mordike, Mater. Sci. Eng. A 298, 193 (2001)

    Article  Google Scholar 

  37. K.K. Deng, J.Y. Shi, C.J. Wang, X.J. Wang, Y.W. Wu, K.B. Nie, K. Wu, Compos. A 43, 1280 (2012)

    Article  CAS  Google Scholar 

  38. M.J. Shen, X.J. Wang, M.F. Zhang, X.S. Hu, M.Y. Zheng, K. Wu, Mater. Sci. Eng. A 601, 58 (2014)

    Article  CAS  Google Scholar 

  39. S. Sankaranarayanan, R.K. Sabat, S. Jayalakshmi, S. Suwas, M. Gupta, J. Alloys Compd. 575, 207 (2013)

    Article  CAS  Google Scholar 

  40. S. Sankaranarayanan, S. Jayalakshmi, M. Gupta, J. Magnes. Alloy 2, 13 (2014)

    Article  CAS  Google Scholar 

  41. A. Mallicka, K.S. Tun, M. Gupta, Mater. Sci. Eng. A 551, 222 (2012)

    Article  CAS  Google Scholar 

  42. M.Y. Zheng, X.G. Qiao, S.W. Xu, K. Wu, S. Kamado, Y. Kojima, Mater. Sci. Forum 488, 589 (2005)

    Article  Google Scholar 

  43. Y.C. Yuan, M. Aibin, X.F. Gou, J.H. Jiang, A. Godfred, D. Song, H. Liu, Mater. Sci. Eng. A 677, 125 (2016)

    Article  CAS  Google Scholar 

  44. J. Suh, J. Victoria-Hernández, D. Letzig, R. Golle, W. Volk, Mater. Sci. Eng. A 699, 159 (2016)

    Article  CAS  Google Scholar 

  45. M.R. Barnett, Z. Keshavarz, A.G. Beer, D. Atwell, Acta Mater. 52, 5093 (2004)

    Article  CAS  Google Scholar 

  46. A. Yamashita, Z. Horita, T.G. Langdon, Mater. Sci. Eng. A 300, 142 (2000)

    Article  Google Scholar 

  47. K. Matsubara, Y. Miyahara, Z. Horita, T.G. Langdon, Acta Mater. 51, 3073 (2003)

    Article  CAS  Google Scholar 

  48. T. Mukai, M. Yamanoi, H.W. Watanabe, K. Higashi, Scripta Mater. 45, 89 (2001)

    Article  CAS  Google Scholar 

  49. W.J. Kim, C.W. An, Y.S. Kim, S.I. Hong, Scripta Mater. 47, 39 (2002)

    Article  CAS  Google Scholar 

  50. E. Dogan, S. Wang, M.W. Vaughan, I. Karaman, Acta Mater. 116, 1 (2016)

    Article  CAS  Google Scholar 

  51. S. Ferrasse, V.M. Segal, S.R. Kalidindi, F. Alford, Mater. Sci. Eng. A 368, 28 (2004)

    Article  CAS  Google Scholar 

  52. A.A. Mohamed, Y.C. Wang, P.H.R. Pereira, Y.W. Wang, S.K. Li, Y.H. Terence, G. Langdon, Mater. Sci. Eng. A 712, 146 (2018)

    Article  CAS  Google Scholar 

  53. M. Peter, V. Jozef, K. Robert, B. Jan, K. Jiří, J. Miloš, S. Jitka, Mater. Sci. Eng. A 708, 193 (2017)

    Article  CAS  Google Scholar 

  54. J.H. Jia, W. Liang, F.Y. Han, H.X. Wang, D. Zhao, Rare Metal Mater. Eng. 42, 1268 (2013)

    CAS  Google Scholar 

  55. W.M. Gan, K. Wu, M.Y. Zheng, X.J. Wang, H. Chang, H.G. Brokmeier, Mater. Sci. Eng. A 516, 283 (2009)

    Article  CAS  Google Scholar 

  56. K.K. Deng, K. Wu, X.J. Wang, Y.W. Wu, X.S. Hu, M.Y. Zheng, W.M. Gan, H.G. Brokmeier, Mater. Sci. Eng. A 527, 1630 (2010)

    Article  CAS  Google Scholar 

  57. K.K. Deng, X.J. Wang, W.M. Gan, Y.W. Wu, K.B. Nie, K. Wu, M.Y. Zheng, H.G. Brokmeier, Mater. Sci. Eng. A 528, 1707 (2011)

    Article  CAS  Google Scholar 

  58. K.B. Nie, K.K. Deng, X.J. Wang, T. Wang, K. Wu, Mater. Charact. 124, 14 (2017)

    Article  CAS  Google Scholar 

  59. W.J. Liao, B. Ye, L. Zhang, H. Zhou, W. Guo, Q.D. Wang, W.Z. Li, Mater. Sci. Eng. A 642, 49 (2015)

    Article  CAS  Google Scholar 

  60. W. Guo, Q.D. Wang, W.Z. Li, H. Zhou, L. Zhang, W.J. Liao, J. Compos. Mater. 51, 681 (2016)

    Article  CAS  Google Scholar 

  61. W. Guo, Q.D. Wang, W.Z. Li, H. Zhou, L. Zhang, W.J. Liao, J. Alloys Compd. 552, 409 (2013)

    Article  CAS  Google Scholar 

  62. X.J. Wang, X.S. Hu, K.B. Nie, K. Wu, M.Y. Zheng, Trans. Nonferrous Met. Soc. China 22, 1912 (2012)

    Article  CAS  Google Scholar 

  63. X.J. Wang, X.S. Hu, K. Wu, L.Y. Wang, Y.D. Huang, Mater. Sci. Eng. A 636, 138 (2015)

    Article  CAS  Google Scholar 

  64. X.J. Wang, K.B. Nie, X.S. Hu, Y.Q. Wang, X.J. Sa, K. Wu, J. Alloys Compd. 532, 78 (2012)

    Article  CAS  Google Scholar 

  65. X. Zhang, K.K. Deng, W.J. Li, H.X. Wang, K.B. Nie, F.J. Xu, W. Liang, Mater. Sci. Eng. A 647, 15 (2015)

    Article  CAS  Google Scholar 

  66. S.J. Shang, K.K. Deng, K.B. Nie, J.C. Li, S.S. Zhou, F.J. Xu, J.F. Fan, Mater. Sci. Eng. A 610, 243 (2014)

    Article  CAS  Google Scholar 

  67. X.F. Sun, C.J. Wang, K.K. Deng, K.B. Nie, X.C. Zhang, X.Y. Xiao, J. Alloys Compd. 732, 328 (2018)

    Article  CAS  Google Scholar 

  68. K.B. Nie, X.J. Wang, L. Xu, K. Wu, X.S. Hu, M.Y. Zheng, J. Alloys Compd. 512, 355 (2012)

    Article  CAS  Google Scholar 

  69. W.Q. Liu, X.S. Hu, X.J. Wang, K. Wu, M.Y. Zheng, Mater. Des. 93, 194 (2016)

    Article  CAS  Google Scholar 

  70. X.J. Wang, W.Q. Liu, X.S. Hu, K. Wu, Mater. Sci. Eng. A 715, 49 (2018)

    Article  CAS  Google Scholar 

  71. H.L. Wang, G.Q. Wu, D.C. Zhang, J.G. Lin, L.J. Gong, M. Ma, Q. Peng, Mater. Charact. 104, 86 (2015)

    Article  CAS  Google Scholar 

  72. Z. Horita, K. Matsubara, K. Makii, T.G. Langdon, Scripta Mater. 47, 255 (2002)

    Article  CAS  Google Scholar 

  73. J. Stráská, M. Janeček, J. Čížek, J. Stráský, B. Hadzima, Mater. Charact. 94, 69 (2014)

    Article  CAS  Google Scholar 

  74. T. Ying, J.P. Huang, M.Y. Zheng, K. Wu, Trans. Nonferrous Met. Soc. China 22, 1896 (2012)

    Article  CAS  Google Scholar 

  75. K. Wu, K.K. Deng, K.B. Nie, Y.W. Wu, X.J. Wang, X.S. Hu, M.Y. Zheng, Mater. Des. 31, 3929 (2010)

    Article  CAS  Google Scholar 

  76. K.K. Deng, C.J. Wang, X.J. Wang, K. Wu, M.Y. Zheng, Mater. Des. 38, 110 (2012)

    Article  CAS  Google Scholar 

  77. X.G. Qiao, T. Yinga, M.Y. Zheng, E.D. Wei, K. Wu, X.S. Hu, W.M. Gan, H.G. Brokmeier, I.S. Golovin, Mater. Charact. 121, 222 (2016)

    Article  CAS  Google Scholar 

  78. Y.V.R.K. Prasad, K.P. Rao, M. Gupta, Compos. Sci. Technol. 69, 1070 (2009)

    Article  CAS  Google Scholar 

  79. H. Li, H. Wang, M. Zeng, X. Liang, H. Liu, Compos. Sci. Technol. 71, 925 (2011)

    Article  CAS  Google Scholar 

  80. L. Qi, Z. Wang, J. Zhou, L. Su, H. Li, Compos. Sci. Technol. 71, 955 (2011)

    Article  CAS  Google Scholar 

  81. M. Srinivasan, C. Loganathan, R. Narayanasamy, V. Senthilkumar, Q.B. Nguyen, M. Gupta, Mater. Des. 47, 449 (2013)

    Article  CAS  Google Scholar 

  82. T. Zhong, K.P. Rao, Y.V.R.K. Prasad, F. Zhao, M. Gupta, Mater. Sci. Eng. A 589, 41 (2014)

    Article  CAS  Google Scholar 

  83. C.J. Wang, K.K. Deng, W. Liang, J. Mater. Res. 33, 1723 (2018)

    Article  CAS  Google Scholar 

  84. X.J. Wang, X.S. Hu, K. Wu, K.K. Deng, W.M. Gan, C.Y. Wang, M.Y. Zheng, Mater. Sci. Eng. A 492, 481 (2008)

    Article  CAS  Google Scholar 

  85. X.J. Wang, X.S. Hu, Y.Q. Wang, K.B. Nie, K. Wu, M.Y. Zheng, Mater. Sci. Eng. A 559, 139 (2013)

    Article  CAS  Google Scholar 

  86. T. Wang, K.B. Nie, K.K. Deng, W. Liang, J. Mater. Res. 31, 3437 (2016)

    Article  CAS  Google Scholar 

  87. H.J. Frost, M.E. Ashby, Deformation mechanism maps (Pergamon Press, Oxford, 1982)

    Google Scholar 

  88. K.B. Nie, X.K. Kang, K.K. Deng, T. Wang, Y.C. Guo, H.X. Wang, Nanomaterials 8, 82 (2018)

    Article  CAS  Google Scholar 

  89. H. Watanabe, T. Mukai, Scripta Mater. 42, 249 (2000)

    Article  CAS  Google Scholar 

  90. R.D. Doherty, D.A. Hughes, F.J. Humphreys, J. Juul Jonas, D.J. Jensen, M.E. Kassner, W.E. King, T.R. Mcnelley, H.J. McQueen, A.D. Rollett, Mater. Sci. Eng. A 238, 219 (1997)

    Article  Google Scholar 

  91. J.D. Robson, D.T. Henry, B. Davis, Acta Mater. 57, 2739 (2009)

    Article  CAS  Google Scholar 

  92. X.F. Sun, C.J. Wang, K.K. Deng, J.W. Kang, Y. Bai, K.B. Nie, S.J. Shang, J. Alloys Compd. 727, 1263 (2017)

    Article  CAS  Google Scholar 

  93. E.A. Ball, P.B. Prangnell, Scr. Metall. Mater. 31, 111 (1994)

    Article  CAS  Google Scholar 

  94. G.W. Lorimer, L.W.F. Mackenzie, F.J. Humphreys, T. Wilks, Mater. Sci. Forum 448, 99 (2005)

    Article  Google Scholar 

  95. K.K. Deng, Y.W. Wu, X.J. Wang, X.S. Hu, K. Wu, W.M. Gan, Mater. Sci. Eng. A 543, 158 (2012)

    Article  CAS  Google Scholar 

  96. X.J. Wang, X.S. Hu, K.B. Nie, K.K. Deng, K. Wu, M.Y. Zheng, Mater. Sci. Eng. A 545, 38 (2012)

    Article  CAS  Google Scholar 

  97. C.J. Wang, K.K. Deng, S.S. Zhou, W. Liang, Acta Metall. Sin. (Engl. Lett.) 29, 527 (2016)

    Article  CAS  Google Scholar 

  98. H. Chang, C.J. Wang, K.K. Deng, K. Su, L. Liao, H.X. Wang, L.B. Tong, Rare Metal Mater. Eng. 47, 1377 (2018)

    Article  Google Scholar 

  99. J.D. Robson, D.T. Henry, B. Davis, Mater. Sci. Eng. A 528, 4239 (2011)

    Article  CAS  Google Scholar 

  100. H.M. Chan, F.J. Humphreys, Acta Mater. 32, 235 (1984)

    Article  CAS  Google Scholar 

  101. K.K. Deng, X.J. Wang, M.Y. Zheng, K. Wu, Mater. Sci. Eng. A 560, 824 (2013)

    Article  CAS  Google Scholar 

  102. W. Bleck, H.J. Bunge, Acta Mater. 29, 1401 (1981)

    Article  CAS  Google Scholar 

  103. F. Habiby, F.J. Humphreys, Scripta Mater. 30, 787 (1994)

    Article  CAS  Google Scholar 

  104. R. Orsund, E. Nes, Scripta Mater. 22, 671 (1988)

    Article  Google Scholar 

  105. N. Stanford, M. Barnett, Scripta Mater. 58, 179 (2008)

    Article  CAS  Google Scholar 

  106. C.J. Wang, K.K. Deng, K.B. Nie, S.J. Shang, Mater. Sci. Eng. A 656, 102 (2016)

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Natural Science Foundation of China (Grant Nos. 51771128 and 51201112), the Projects of International Cooperation in Shanxi (Grant No. 201703D421039) and the Natural Science Foundation of Shanxi (Grant No. 201601D011034). The authors also thank the Support from Program for the Outstanding Innovative Teams of Higher Learning Institutions of Shanxi.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Kun-Kun Deng.

Additional information

Available online at http://link.springer.com/journal/40195

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Deng, KK., Wang, CJ., Nie, KB. et al. Recent Research on the Deformation Behavior of Particle Reinforced Magnesium Matrix Composite: A Review. Acta Metall. Sin. (Engl. Lett.) 32, 413–425 (2019). https://doi.org/10.1007/s40195-019-00872-9

Download citation

  • Received:

  • Revised:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s40195-019-00872-9

Keywords

Navigation