Abstract
In this study, 3-mm-thick hot-extruded plates of Al-12.7Si-0.7Mg alloy were used to fabricate the joints welded by gas metal arc welding. Effects of the post-weld heat treatment include solid solution treatment, water quenching, and artificial aging treatment on the microstructure, and mechanical properties of the weld joints have been investigated. Results showed that the welded joints after solid solution and artificial aging exhibited the increases in yield strength of 166 MPa and ultimate tensile strength of 148 MPa, respectively. Based on the microstructural observations, the associated mechanisms were discussed.
Similar content being viewed by others
References
M. Franco, T.H. Krishna, A.M. Pillai, A. Rajendra, A.K. Sharma, Acta Metall. Sin. (Engl. Lett.) 26, 647 (2013)
Z.Y. Ma, S.R. Sharma, R.S. Mishra, Mater. Sci. Eng. A 433, 269 (2006)
K.Z. He, F.X. Yu, D.Z. Zhao, L. Zuo, Trans. IIM 62, 367 (2009)
L. Zuo, F.X. Yu, G. Zhao, X. Zhao, Y.L. Yang. Y. Li, U.S. Patent 0,126,639, 27 May 2010
F. Liu, F.X. Yu, D.Z. Zhao, L. Zuo, Mater. Sci. Eng. A 528, 3786 (2011)
X.P. Ding, H. Li, L.J. Yang, Y. Gao, Acta Metall. Sin. (Engl. Lett.) 26, 265 (2013)
K. Lee, Y.N. Kwon, S. Lee, J. Alloys Compd. 461, 532 (2008)
J.H. Peng, X.L. Tang, J.T. He, D.Y. Xu, Trans. Nonferrous Met. Soc. China 21, 1950 (2011)
Q.G. Wang, C.H. Caceres, J.R. Griffiths, Metall. Mater. Trans. A 34, 2901 (2003)
Y.F. Bai, H.D. Zhao, Mater. Des. 31, 4237 (2010)
Z.Y. Ma, S.R. Sharma, R.S. Mishra, Metall. Mater. Trans. A 37, 3323 (2006)
A.M. Kliauga, M. Ferrante, Acta Mater. 53, 345 (2005)
A. Jaafar, A. Rahmat, Z. Hussain, I. Zainol, J. Alloys Compd. 509, 8632 (2011)
W.F. Miao, D.E. Laughlin, Metall. Mater. Trans. A 31, 361 (2000)
M. Murayama, K. Hono, Acta Mater. 47, 1537 (1999)
W.F. Miao, D.E. Laughlin, Scr. Mater. 40, 873 (1999)
S.J. Andersen, H.W. Zandbergen, J. Jansen, C. Traeholt, U. Tundal, O. Reiso, Acta Mater. 46, 3283 (1998)
K. Matsuda, T. Naoi, K. Fujii, Y. Uetani, T. Sato, A. Kamio, S. Ikeno, Mater. Sci. Eng. A 262, 232 (1999)
S.K. Son, S. Matsumura, K. Fukui, M. Takeda, J. Alloys Compd. 509, 241 (2011)
Acknowledgments
This work was financially supported by the Project of National Science & Technology Pillar Program (Nos. 2009BAG12A07-B02 and 2009BAE80B01) and National Natural Science Foundation of China (No. 51071040). The authors gratefully acknowledge Dr. Wang Xinli, from Northeastern Univ., for assistance with guidance for this paper writing.
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Wang, D., He, C., Wang, H. et al. Effects of Post-Weld Heat Treatment on Microstructure and Mechanical Properties of Al-12.7Si-0.7Mg Alloy Welded Joints by GMAW. Acta Metall. Sin. (Engl. Lett.) 27, 245–252 (2014). https://doi.org/10.1007/s40195-014-0052-4
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-014-0052-4