Abstract
Different additions of B4C were introduced into TC4 to alter the microstructure and mechanical properties. The morphologies of reinforcements are related to the solidification paths. The refinement of lamellar spacing λ is based on the precipitation pattern of β-phases. Microhardness, compression elastic modulus (E c), and elastic modulus of the matrix (E m) appear non-linear relationships with B4C additions. Due to the refinement of lamellar spacing with Hall–Petch-type relationships, and the solution strengthening of C on the α + β matrix, the effect of reinforcements on the mechanical properties will be more efficient when the additions of B4C are no more than 0.19 wt%. When the additions of B4C are more than 0.19 wt%, the efficiency will decrease.
Similar content being viewed by others
References
S. Ranganath, M. Vijayakumar, J. Subrahmanyan, Mater. Sci. Eng. A 149, 253 (1992)
X. Zhang, W. Lü, D. Zhang, R. Wu, Y. Bian, P. Fang, Scr. Mater. 41, 39 (1999)
B.J. Choi, Y.J. Kim, Mater. Trans. 52, 1926 (2011)
J. Lu, J. Qin, W. Lu, D. Zhang, H. Hou, Z. Li, Mater. Sci. Eng. A 500, 1 (2009)
E. Yun, K. Lee, S. Lee, Surf. Coat. Technol. 184, 74 (2004)
W. Lu, D. Zhang, X. Zhang, S.L. Guo, R.J. Wu, Trans. Nonferrous Met. Soc. China 11, 67 (2001)
W. Lu, D. Zhang, X. Zhang, R. Wu, T. Sakata, H. Mori, J. Alloys Compd. 327, 240 (2001)
W. Lu, D. Zhang, X. Zhang, R. Wu, T. Sakata, H. Mori, J. Alloys Compd. 327, 248 (2001)
J. Zhu, A. Kamiya, T. Yamada, W. Shi, K. Naganuma, Mater. Sci. Eng. A 339, 53 (2003)
P. Villars, A. Prince, H. Okamoto, Handbook of ternary alloy phase diagrams, vol. 5 (ASM International, Materials Park, 1995)
R. Srinivasan, S. Tamirisakandala, Scr. Mater. 63, 1244 (2010)
I. Sen, S. Tamirisakandala, D. Miracle, U. Ramamurty, Acta Mater. 55, 4983 (2007)
B. Mordyuk, M. Iefimov, G. Prokopenko, T. Golub, M. Danylenko, Surf. Coat. Technol. 204, 1590 (2010)
Y. Yang, H. Lu, C. Yu, J. Chen, J. Alloys Compd. 485, 542 (2009)
F.C. Wang, Z. Zhang, J. Luo, C.C. Huang, S.K. Lee, Compos. Sci. Technol. 69, 2682 (2009)
C. Schuh, T. Nieh, H. Iwasaki, Acta Mater. 51, 431 (2003)
A. Suzuki, N.D. Saddock, L. Riester, E. Lara-Curzio, J. Jones, T. Pollock, Metall. Mater. Trans. A 38, 420 (2007)
Ø. Ryen, B. Holmedal, O. Nijs, E. Nes, E. Sjölander, H.-E. Ekström, Metall. Mater. Trans. A 37, 1999 (2006)
Y. Mishima, S. Ochiai, N. Hamao, M. Yodogawa, T. Suzuki, Jpn Inst. Met. Trans. 27, 656 (1986)
Acknowledgments
This work was financially supported by the National Basic Research Program of China (No. 2012CB619600), Shanghai Academy of Spaceflight-Joint Research Centre of Shanghai Jiaotong University advanced aerospace technology (No. USCAST2012-14), Shanghai Science and Technology Committee (No. 12XD1402800), and the Dawn Program of Shanghai Education Commission (No. 10SG15).
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Wang, J., Guo, X., Xiao, L. et al. Effect of B4C on the Microstructure and Mechanical Properties of As-Cast TiB+TiC/TC4 Composites. Acta Metall. Sin. (Engl. Lett.) 27, 205–210 (2014). https://doi.org/10.1007/s40195-014-0035-5
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-014-0035-5