Abstract
Porous Si3N4-Si3N4 composite ceramics were fabricated by 3D printing combined with low-pressure chemical vapor infiltration (CVI). This technique could effectively improve the designability of porous Si3N4 ceramics and optimize the mechanical and dielectric properties. The effects of process parameters including the deposition time and heat treatment on the microstructure and properties of porous Si3N4-Si3N4 composite ceramics were studied. The study highlights following: When CVI processing time was increased from 0 to 12 h, the porosity decreased from 68.65% to 26.07% and the density increased from 0.99 to 2.02 g/cm3. At the same time, the dielectric constant gradually increased from 1.72 to 3.60; however, the dielectric loss always remained less than 0.01, indicating the excellent electromagnetic (EM) wave-transparent performance of porous Si3N4-Si3N4 composite ceramics. The maximum flexural strength of 47±2 MPa was achieved when the deposition time attained 6 h. After heat treatment, the porosity increased from 26.07% to 36.02% and the dielectric constant got a slight increase from 3.60 to 3.70 with the dielectric loss still maintaining lower than 0.01. It has been demonstrated that the porous Si3N4-Si3N4 composite ceramics are a promising structural and EM wave-transparent material suitable for high temperature service.
References
Li XM, Zhang LT, Yin XW. Fabrication and properties of porous Si3N4 ceramic with high porosity. J Mater Sci Technol 2012, 28: 1151–1156.
Ding SQ, Zeng YP, Jiang DL. Oxidation bonding of porous silicon nitride ceramics with high strength and low dielectric constant. Mater Lett 2007, 61: 2277–2280.
Wang HJ, Yu JL, Zhang J, et al. Preparation and properties of pressureless-sintered porous Si3N4. J Mater Sci 2010, 45: 3671–3676.
Wan T, Yao DX, Yin JW, et al. The microstructure and mechanical properties of porous silicon nitride ceramics prepared via novel aqueous gelcasting. Int J Appl Ceram Technol 2015, 12: 932–938.
Guo SQ, Hirosaki N, Yamamoto Y, et al. Hot-pressed silicon nitride ceramics with Lu2O3 additives: Elastic moduli and fracture toughness. J Eur Ceram Soc 2003, 23: 537–545.
Barta J, Manela M, Fischer R. Si3N4 and Si2N2O for high performance radomes. Mater Sci Eng 1985, 71: 265–272.
Yu JL, Wang HJ, Zeng H, et al. Effect of monomer content on physical properties of silicon nitride ceramic green body prepared by gelcasting. Ceram Int 2009, 35: 1039–1044.
Yin XW, Travitzky N, Greil P. Near-net-shape fabrication of Ti3AlC2-based composites. Int J Appl Ceram Technol 2007, 4: 184–190.
Seitz H, Rieder W, Irsen S, et al. Three-dimensional printing of porous ceramic scaffolds for bone tissue engineering. J Biomed Mater Res 2005, 74B: 782–788.
Zhao X, Evans JRG, Edirisinghe MJ, et al. Ceramic freeforming using an advanced multinozzle ink-jet printer. J Mater Synth Proces 2001, 9: 319–327.
Tay By, Evans JRG, Edirisinghe MJ. Solid freeform fabrication of ceramics. Int Mater Rev 2003, 48: 341–370.
Blazdell PF, Evans JRG, Edirisinghe MJ, et al. The computer aided manufacture of ceramics using multilayer jet printing. J Mater Sci Lett 1995, 14: 1562–1565.
Song JH, Nur HM. Defects and prevention in ceramic components fabricated by inkjet printing. J Mater Process Technol 2004, 155-156: 1286–1292.
Li XM, Zhang LT, Yin XW. Effect of chemical vapor deposition of Si3N4, BN and B4C coatings on the mechanical and dielectric properties of porous Si3N4 ceramic. Scr Mater 2012, 66: 33–36.
Naslain R. Design, preparation and properties of non-oxide CMCs for application in engines and nuclear reactors: An overview. Compos Sci Technol 2004, 64: 155–170.
Ma YZ, Yin XW, Fan XM, et al. Near-net-shape fabrication of Ti3SiC2-based ceramics by three-dimensional printing. Int J Appl Ceram Technol 2015, 12: 71–80.
Luo H, Tan YQ, Li Y, et al. Modeling for high-temperature dielectric behavior of multilayer Cf/Si3N4 composites in X-band. J Eur Ceram Soc 2017, 37: 1961–1968.
Acknowledgements
This work was supported by the Chinese National Foundation for Natural Sciences under Contract (Nos. 51602258 and 51672217) and 111 Project of China (B08040).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Cheng, Z., Ye, F., Liu, Y. et al. Mechanical and dielectric properties of porous and wave-transparent Si3N4-Si3N4 composite ceramics fabricated by 3D printing combined with chemical vapor infiltration. J Adv Ceram 8, 399–407 (2019). https://doi.org/10.1007/s40145-019-0322-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40145-019-0322-8
Keywords
- porous Si3N4 ceramics
- Si3N4-Si3N4 composite ceramics
- mechanical property
- electromagnetic (EM) wave transparent performance
- 3D printing
- chemical vapor infiltration (CVI)