Preparation and rheology characterization of branched polypropylene during reactive extrusion process

  • Original Paper
  • Published:
Iranian Polymer Journal Aims and scope Submit manuscript

Abstract

The aim of this study was to compare the rheological behavior of branched polypropylene and linear PP by reactive extrusion process. Samples were modified in the presence of a peroxide initiator, i.e., 2,5-dimethyl-2,5(tert-butyl peroxy) hexane which was dispersed at 45 wt% in \({\text{CaCo}}_{3}\) (DHBP45), multi-functional monomer trimethylol propane triacrylate (TMPTA) as a graft monomer, and co-agent tetraethyl thiuram disulfide (TETDS) as a co-reactant, in an internal mixer. Rheological measurements and thermal analysis were used to characterize the structure of the modified PP samples. Using PP powder instead of PP granule, it was concluded that the elastic response of branched PP at low frequency was enhanced in comparison with linear PP. Rheological properties, such as increasing the G′ at low frequency, plateau in tanδ–ω plot, deviating from linear PP in Han plot and upturning at high viscosity in Cole–Cole plot, promoted the branching in PP backbone. Moreover, the results showed that by decreasing the amount of initiator, the chain scission can be controlled. TETDS could efficiently control side reactions, decrease the concentration of active free radicals simultaneously in system and improve the branching. When the quantity of TETDS decreased from moderate quantity, the functionality remained unchanged and failed to improve the branching.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Scheme 1
Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

References

  1. Zhang Z, Wan D, Xing H, Zhang Z, Wang L, Zheng J, An Y, Tang T (2012) A new grafting monomer for synthesizing long chain branched polypropylene through melt radical reaction. Polymer 53:121–129

    Article  CAS  Google Scholar 

  2. Lagendijk RP, Hogt AH, Gotsis AD (2001) Peroxydicarbonate modification of polypropylene and extensional flow properties. Polymer 42:10035–10043

    Article  CAS  Google Scholar 

  3. Borsig E, Van Duin M, Gotsis AD, Picchioni F (2008) Long chain branching on linear polypropylene by solid state reaction. Eur Polym J 44:200–212

    Article  CAS  Google Scholar 

  4. Mousavi SA, Frounchi M, Dadbin S, Augier S, Passaglia E, Ciardelli F (2007) Modification of isotactic polypropylene by free-radical grafting of 1,1,1-trimethylol propane trimetacrylate. J Appl Polym Sci 104:950–958

    Article  Google Scholar 

  5. Auhl D, Stange J, Munstedt H (2004) Long-chain branched polypropylene by electron beam irradiation and their rheological properties. Macromolecules 37:9465–9472

    Article  CAS  Google Scholar 

  6. Cheng S, Phillips ED, Parks L (2010) Processability improvement of polyolefins through radiation-induced branching. Radiat Phys Chem 79:329–334

    Article  CAS  Google Scholar 

  7. Weng W, Hu W, Dekmezian A, Ruff CJ (2002) Long chain branched isotactic polypropylene. Macromolecules 35:3838–3843

    CAS  Google Scholar 

  8. Xing H, Jiang Z, Zhang Z, Qiua J, Wanga Y, Maa L, Tanga T (2012) Effect of leaving group in dithiocarbamates on mediating melt radical reaction during preparing long chain branched polypropylene. Polym J 53:947–955

    Article  CAS  Google Scholar 

  9. Langston J, Colby R, Chung TC (2007) Synthesis and characterization of long chain branched isotactic polypropylene via metallocene catalyst and t-reagent. Macromolecules 40:2712–2720

    Article  CAS  Google Scholar 

  10. Scott Parent J, Bodsworth A, Sengupta S, Kontopoulou M, Chaudhary B, Poche D, Cousteaux S (2009) Structure-rheology relationships of long-chain branched polypropylene: comparative analysis of acrylic and allylic coagent chemistry. Polymer 50:85–94

    Article  Google Scholar 

  11. Lu B, Chung TC (1999) Synthesis of long chain branched polypropylene with relatively well-defined molecular structure. Macromoleculase 32:8678–8680

    Article  CAS  Google Scholar 

  12. Pivokonsky R, Zatloukal M, Filip P, Tzoganakis C (2009) Rheological characterization and modeling of linear and branched metallocene polypropylene prepared by reactive processing. J Non-Newtonian Fluid Mech 156:1–6

    Article  CAS  Google Scholar 

  13. Zhang Z, Wan D, An Y, Liu F, Xing H, Wang L, Jiang Z (2011) Controlling the evolution of polypropylene microstructure during melt free radical modification using zinc dithiocarbamate with different N-substituted. Polym Degrad Stabil 96:653–659

    Article  CAS  Google Scholar 

  14. Serena C, Augier S, Pinzino C, Passaglia E (2010) Control of degradation of polypropylene during its radical functionalisation with furan and thiophene derivatives. Polym Degrad Stabil 95:298–305

    Article  Google Scholar 

  15. Mousavi SA, Dadbin S, Frounchi M, Venerus DC, Medina TG (2010) Comparison of rheological behavior of branched polypropylene prepared by chemical modification and electron beam irradiation under air and N2. Radiat Phys Chem 79:1088–1094

    Article  Google Scholar 

  16. Mabrouk EL, Scott K, Parent J, Chaudhary BI (2009) Chemical modification of pp architecture: strategies for introducing long-chain branching. Polymer 50:5390–5397

    Article  Google Scholar 

  17. Graebling D (2002) Synthesis of branched polypropylene by a reactive extrusion process. Macromolecules 35:4602–4610

    Article  CAS  Google Scholar 

  18. Zhang Z, Xing H, Qiu J, Jiang Z, Yu H, Du X, Wang Y, Ma L, Tang T (2010) Controlling melt reactions during preparing long chain branched polypropylene using copper N,N-dimethyldithiocarbamate. Polymer 51:1593–1598

    Article  CAS  Google Scholar 

  19. Tian J, Yu W, Zhou C (2006) The preparation and rheology characterization of long chain branching polypropylene. Polymer 47:7962–7969

    Article  CAS  Google Scholar 

  20. Lugao AB, Artel BWH, Yoshiga A, Lima LFCP, Parra DF, Bueno JR, Liberman S, Farrah M, Tercariol WR, Otaguro H (2007) Production of high melt strength polypropylene by gamma irradiation. Radiat Phys Chem 76:1691–1695

    Article  CAS  Google Scholar 

  21. Li S, Xiao M, Wei D, Xiao H, Hu F, Zheng A (2009) The melt grafting preparation and rheological characterization of long chain branching polypropylene. Polymer 50:6121–6128

    Article  CAS  Google Scholar 

  22. Breuer G, Schausberger A (2011) Recovery of shear modification of polypropylene melts. Rheol Acta 50:461–468

    Article  CAS  Google Scholar 

  23. Zhao W, Wu G, Yang Q (2012) Controlling the transition of long-and short-chain branching polypropylene. Polym Plast Technol Eng 51:716–723

    Article  CAS  Google Scholar 

  24. Tian J, Yu W, Zhou C (2006) Crystallization kinetics of linear and long-chain branched polypropylene. J Macromol Sci Phys 45:969–985

    Article  CAS  Google Scholar 

  25. Zhao W, Huang Y, Liao X, Yang Q (2013) The molecular structure characteristics of long chain branched polypropylene and its effects on non-isothermal crystallization and mechanical properties. Polymer 54:1455–1462

    Article  CAS  Google Scholar 

  26. Razavi Nouri M (2006) Effect of annealing and pressure on structure and melting of a polypropylene random copolymer. Iran Polym J 15:121–126

    CAS  Google Scholar 

  27. Jahani Y, Barikani M (2005) Effect of side chain branched PP, EPDM and HDPE as a third component on melt extensional behaviour of ternary blends. Iran Polym J 14:693–704

    CAS  Google Scholar 

  28. Azizi H, Ghasemi I (2005) Investigation on influence of peroxide degradation process on rheological properties of polypropylene. Iran Polym J 14:465–471

    CAS  Google Scholar 

Download references

Acknowledgments

The kind assistance of Tarbiat Modares University is greatly acknowledged.

Author information

Authors and Affiliations

  1. Polymer Engineering Department, Chemical Engineering Faculty, TarbiatModares University, P.O. Box 14115-114, Tehran, Iran

    Kimia Mohebbi & Nadereh Golshan Ebrahimi

Authors
  1. Kimia Mohebbi
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Nadereh Golshan Ebrahimi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Nadereh Golshan Ebrahimi.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Mohebbi, K., Ebrahimi, N.G. Preparation and rheology characterization of branched polypropylene during reactive extrusion process. Iran Polym J 24, 309–316 (2015). https://doi.org/10.1007/s13726-015-0323-6

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s13726-015-0323-6

Keywords

Search

Navigation