Effects of zinc borate loading on thermal stability, flammability, crystallization properties of magnesium oxide/(90/10) mLLDPE/(NR/ENR-50) blends

  • Original Paper
  • Published:
Iranian Polymer Journal Aims and scope Submit manuscript

Abstract

Effects of different zinc borate (ZB) loadings on thermal, flammability and crystallinity properties of blends of 10 % rubber (9/1) natural rubber (NR)/epoxidised natural rubber (ENR)/metallocene linear low density polyethylene/N,N-m-phenylenebismaleimide/MgO were investigated. Fourier transform infrared spectroscopy revealed that –C=O and –OH groups appeared while C–O–C and C=C groups disappeared in all blend samples. ZB increased the activation of HVA-2 by changing the reaction mechanism and increasing the concentration of the –C=O groups in the blends due to the peak at 1,714–1,718 cm−1. The crystallinity of all blends was increased by ZB loading increase; therefore, it played the heterogeneous nucleation center and maximum crystallinity was observed at 6 phr ZB blend. The thermal stability of NR improved with increase of zinc borate loading and the highest thermal stability was determined for 8 phr ZB blend. Good compatibilization between the two rubbers (NR/ENR-50) was achieved in the presence of ZB, which was revealed by the presence of only one peak for their decomposition. The limiting oxygen index value of mLLDPE was decreased by two rubbers loading increase, while it was increased by ZB loading increase to provide fire barriers to protect flammable materials from thermal damage. It was concluded that ZB has a synergistic effect on the LOI values of flame retardant mLLDPE/rubber containing MgO.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5

Similar content being viewed by others

References

  1. Han SJ, Gross LH (2007) Crosslinking and electrical characterization of metallocene linear low density polyethylene. Electrl Insul Conf Electr Manufact Expo: 22–24. doi:10.1109/EEIC.2007.4562593

  2. Müller M, Kulikov O, Hornung K, Wagner MH (2010) The use of thermoplastic elastomers as polymer processing aids in processing of linear low density polyethylene. Polym Sci A 52:1163–1170

    Article  Google Scholar 

  3. Tkáč A (1991) Free radicals in the gas phase. ESR investigation of flame and microwave plasma of atomized gases. A contribution to flame retardation and polymer erosion mechanisms. Polym Degrad Stab 33:171–206

    Article  Google Scholar 

  4. Jiao C, Wang Z, Chen X, Yu B, Hu Y (2006) Irradiation crosslinking and halogen-free flame retardation of EVA using hydrotalcite and red phosphorus. Radiat Phys Chem 75:557–563

    Article  CAS  Google Scholar 

  5. Wang J, Feng D, Wu W, Zeng M, Li Y (1991) An investigation of the flame retardation mechanism of polypropylene containing a chlorine flame retardant system by XPS (ESCA). Polym Degrad Stab 31:129–140

    Article  CAS  Google Scholar 

  6. Kılınç M, Çakal GÖ, Yeşil S, Bayram G, Eroğlu İ, Özkar S (2010) Scale-up synthesis of zinc borate from the reaction of zinc oxide and boric acid in aqueous medium. J Cryst Growth 312:3361–3366

    Article  Google Scholar 

  7. Li S, Long B, Wang Z, Tian Y, Zheng Y, Zhang Q (2010) Synthesis of hydrophobic zinc borate nanoflakes and its effect on flame retardant properties of polyethylene. J Solid State Chem 183:957–962

    Article  CAS  Google Scholar 

  8. Innes A, Innes J (2011) Flame retardants. In: Kutz M (ed) Applied plastics engineering handbook. William Andrew Publishing, Oxford

    Google Scholar 

  9. Garrett DE (1998) Borates: handbook of deposits, processing, properties, and use. Academic Press, San Diego, Ch 9

  10. Wang S, Fujita M, Tanimoto G, Ajda F, Fujiwara Y (1996) Development of insulation material for DC cables-space charge properties of metallocene catalyzed polyethylene. IEEE Int Sympos Electr Insulat, Montreal, Quebec, Canada, 16–19 Jun, 2: 657–660

  11. Taniguchi Y, Kaneko K, Mizutani T, Ishioka M (2001) Space charge behaviors of various low density polyethylene, (ISEIM 2001). Proc Int Sympos Electr Insulat Mater, 440–443

  12. Zurina M, Ismail H, Ratnam CT (2008) The effect of HVA-2 on properties of irradiated epoxidized natural rubber (ENR-50), ethylene vinyl acetate (EVA), and ENR-50/EVA blend. Polym Test 27:480–490

    Article  CAS  Google Scholar 

  13. Guo B, Cao Y, Jia D, Qiu Q (2004) Thermoplastic elastomers derived from scrap rubber powder/LLDPE blend with LLDPE-graft-(epoxidized natural rubber) dual compatibilizer. Macromol Mater Eng 289:360–367

    Article  CAS  Google Scholar 

  14. Noriman NZ, Ismail H, Rashid AA (2010) Characterization of styrene butadiene rubber/recycled acrylonitrile-butadiene rubber (SBR/NBRr) blends: the effects of epoxidized natural rubber (ENR-50) as a compatibilizer. Polym Test 29:200–208

    Article  CAS  Google Scholar 

  15. Poh BT, Ismail H, Tan KS (2002) Effect of filler loading on tensile and tear properties of SMR L/ENR 25 and SMR L/SBR blends cured via a semi-efficient vulcanization system. Polym Test 21:801–806

    Article  CAS  Google Scholar 

  16. Awang M, Ismail H (2008) Preparation and characterization of polypropylene/waste tyre dust blends with addition of DCP and HVA-2 (PP/WTDP-HVA2). Polym Test 27:321–329

    Article  CAS  Google Scholar 

  17. Jayasree TK, Predeep P, Thomas S, Laladas KP (2003) Tearing and glass transition behavior of thermoplastic elastomeric blends of high density polyethylene/styrene butadiene rubber: influence of blend ratio, morphology and dynamic crosslinking. J Polym Mater 20(3):227–236

    CAS  Google Scholar 

  18. Hassan A, Wahit MU, Chee CY (2003) Mechanical and morphological properties of PP/NR/LLDPE ternary blend—effect of HVA-2. Polym Test 22:281–290

    Article  CAS  Google Scholar 

  19. Andritsch T, Kochetov R, Morshuis PHF, Smit JJ (2010) Dielectric properties and space charge behavior of MgO-epoxy nanocomposites. 10th IEEE Int Conf Solid Dielectr, Potsdam, Germany, 4–9 July, 1–4

  20. Murata Y, Sekiguchi Y, Inoue Y, Kanaoka M (2005) Investigation of electrical phenomena of inorganic-filler/LDPE nanocomposite material. Proc Int Sympos Electri Insulat Mater, 5–9 June, 3: 650–653

  21. Takada T, Hayase Y, Tanaka Y (2008) Space charge trapping in electrical potential well caused by permanent and induced dipoles for LDPE/MgO nanocomposite. IEEE Trans Dielectr Electr Insul 15:152–160

    Article  CAS  Google Scholar 

  22. Murakami Y, Nemoto M, Okuzumi S, Masuda S, Nagao S, Hozumi N, Sekiguchi Y (2008) DC conduction and electrical breakdown of MgO/LDPE nanocomposite. IEEE Trans Dielectr Electr Insul 15:33–39

    Article  CAS  Google Scholar 

  23. Ishimoto K, Kanegae E, Ohki Y, Tanaka T, Sekiguchi Y, Murata Y, Reddy C (2009) Superiority of dielectric properties of LDPE/MgO nanocomposites over microcomposites. IEEE Trans Dielectr Electr Insul 16:1735–1742

    Article  CAS  Google Scholar 

  24. Alwaan IM, Hassan A, Jawaid M (2013) Effect of natural rubber/epoxidized natural rubber (90/10) on mechanical and thermal properties of linear low density polyethylene. J Polym Mater 30:117–130

    CAS  Google Scholar 

  25. Alwaan IM, Hassan A (2013) The effects of magnesium oxide on the thermal, morphological, and crystallinity properties of metallocene linear low-density polyethylene/rubbers composite. J Polym Eng 33:229–238

    Google Scholar 

  26. ExxonMobil chemical (2011) Metallocene Polyethylene resin Exceed 1018CA. www.exxonmobilpe.com. Accessed 10 June 2012

  27. Queensland Magnesia. magnesium oxide Grade EMAG® 1000. http://www.qmag.com.au/pdf/EMAG1000.pdf. Accessed 30 June 2013

  28. Firebrake® ZB (2013). http://www.borax.com/product/firebrake-zb.aspx. Accessed 20 June 2013

  29. Wang X, He HQ, Tu DM, Lei C, Du QG (2008) Dielectric properties and crystalline morphology of low density polyethylene blended with metallocene catalyzed polyethylene. IEEE Trans Dielectr Electr Insul 15:319–326

    Article  CAS  Google Scholar 

  30. Ferreto HFR, Oliveira ACF, Lima LFCP, Parra DF, Lugäo AB (2012) Thermal, tensile and rheological properties of linear low density polyethylene (LLDPE) irradiated by gamma-ray in different atmospheres. Radiat Phys Chem 81:958–961

    Article  CAS  Google Scholar 

  31. Gao X, Guo Y, Tian Y, Li S, Zhou S, Wang Z (2011) Synthesis and characterization of polyurethane/zinc borate nanocomposites. Colloid Surface A 384:2–8

    Article  CAS  Google Scholar 

  32. Köytepe S, Vural S, Seçkin T (2009) Molecular design of nanometric zinc borate-containing polyimide as a route to flame retardant materials. Mater Res Bull 44:369–376

    Article  Google Scholar 

  33. Guzmán M, Vega B, Agulló N, Giese U, Borrós S (2012) Zinc oxide versus magnesium oxide revisited Part 1. Rub Chem Technol 85:38–55. doi:10.5254/1.3672428

    Article  Google Scholar 

  34. Chokanandsombat Y, Sirisinha C (2013) MgO and ZnO as reinforcing fillers in cured polychloroprene rubber. J Appl Polym Sci 128:2533–2540

    Article  CAS  Google Scholar 

  35. Pretsch E, Bühlmann P, Badertscher M (2009) Structure determination of organic compounds: tables of spectral data, 4th edn. Springer, Berlin

    Google Scholar 

  36. Dahlan HM, Zaman MDK, Ibrahim A (2002) The morphology and thermal properties of liquid natural rubber (LNR)-compatibilized 60/40 NR/LLDPE blends. Polym Test 21:905–911

    Article  CAS  Google Scholar 

  37. Wang Z, Qu B, Fan W, Hu Y, Shen X (2002) Effects of PE-g-DBM as a compatiblizer on mechanical properties and crystallization behaviors of magnesium hydroxide-based LLDPE blends. Polym Degrad Stab 76:123–128

    Article  Google Scholar 

  38. Wu M, Yang G, Wang M, Wang W, Zhang W-D, Feng J, Liu T (2008) Nonisothermal crystallization kinetics of ZnO nanorod filled polyamide 11 composites. Mater Chem Phys 109:547–555

    Article  CAS  Google Scholar 

  39. Jiang J, Li G, Ding Q, Mai K (2012) Ultraviolet resistance and antimicrobial properties of ZnO-supported zeolite filled isotactic polypropylene composites. Polym Degrad Stab 97:833–838

    Article  CAS  Google Scholar 

  40. Liu WG, Zhang X-C, Li H-Y, Liu Z (2012) Effect of surface modification with 3-aminopropyltriethyloxy silane on mechanical and crystallization performances of ZnO/poly(butylenesuccinate) composites. Compos Part B Eng 43:2209–2216

    Article  CAS  Google Scholar 

  41. Ma Y-L, Hu G-S, Ren X-L, B-b Wang (2007) Non-isothermal crystallization kinetics and melting behaviors of nylon 11/tetrapod-shaped ZnO whisker (T-ZnOw) composites. Mater Sci Eng A 460–461:611–618

    Article  Google Scholar 

  42. Ning N, Deng H, Luo F, Wang K, Zhang Q, Chen F, Fu Q (2011) Effect of whiskers nucleation ability and shearing function on the interfacial crystal morphology of polyethylene (PE)/raw whiskers composites. Compos Part B Eng 42:631–637

    Article  Google Scholar 

  43. Gao Y, Ren K, Ning N, Fu Q, Wang K, Zhang Q (2012) Stretching-induced interfacial crystalline structures and relevant mechanical properties in melt-spun polypropylene/whisker composite fibers. Polymer 53:2792–2801

    Article  CAS  Google Scholar 

  44. Ning N, Fu S, Zhang W, Chen F, Wang K, Deng H, Zhang Q, Fu Q (2012) Realizing the enhancement of interfacial interaction in semicrystalline polymer/filler composites via interfacial crystallization. Prog Polym Sci 37:1425–1455

    Article  CAS  Google Scholar 

  45. Moly KA, Radusch HJ, Androsh R, Bhagawan SS, Thomas S (2005) Nonisothermal crystallisation, melting behavior and wide angle X-ray scattering investigations on linear low density polyethylene (LLDPE)/ethylene vinyl acetate (EVA) blends: effects of compatibilisation and dynamic crosslinking. Eur Polym J 41:1410–1419

    Article  CAS  Google Scholar 

  46. Tesoro GC (1978) Chemical modification of polymers with flame-retardant compounds. J Polym Sci Macromol Rev 13:283–353

    Article  CAS  Google Scholar 

  47. Najib NN, Ismail H, Azura AR (2009) Thermoplastic elastomer composites of palm ash-filled ethylene vinyl acetate/natural rubber blends: effects of palm ash loading and size. Polym Plast Technol Eng 48:1062–1069

    Article  CAS  Google Scholar 

  48. Ramesan MT (2004) Thermogravimetric analysis, flammability and oil resistance properties in natural rubber and dichlorocarbene modified styrene butadiene rubber blends. React Funct Polym 59:267–274

    Article  CAS  Google Scholar 

  49. Ramesan MT, Alex R, Khanh NV (2005) Studies on the cure and mechanical properties of blends of natural rubber with dichlorocarbene modified styrene–butadiene rubber and chloroprene rubber. React Funct Polym 62:41–50

    Article  CAS  Google Scholar 

  50. Wang Z, Hu Y, Gui Z, Zong R (2003) Halogen-free flame retardation and silane crosslinking of polyethylenes. Polym Test 22:533–538

    Article  CAS  Google Scholar 

  51. Dogan M, Yılmaz A, Bayraml E (2010) Synergistic effect of boron containing substances on flame retardancy and thermal stability of intumescent polypropylene composites. Polym Degrad Stab 95:2584–2588

    Article  CAS  Google Scholar 

  52. Baltaci B, Çakal GÖ, Bayram G, Eroglu I, Özkar S (2013) Surfactant modified zinc borate synthesis and its effect on the properties of PET. Powder Technol 244:38–44

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Faculty of Chemical Engineering, Universiti Teknologi Malaysia, Johor, Malaysia

    I. M. Alwaan

  2. Faculty of Engineering, University of Kufa, Najaf, Iraq

    I. M. Alwaan & A. Hassan

Authors
  1. I. M. Alwaan
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. A. Hassan
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to A. Hassan.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Alwaan, I.M., Hassan, A. Effects of zinc borate loading on thermal stability, flammability, crystallization properties of magnesium oxide/(90/10) mLLDPE/(NR/ENR-50) blends. Iran Polym J 23, 277–287 (2014). https://doi.org/10.1007/s13726-014-0223-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s13726-014-0223-1

Keywords

Search

Navigation