Abstract
Microstructure and macro-texture with different normalizing processes for Hi–B steel were analyzed and compared with the non-normalizing cold-rolled steel by optical microscopy, X-ray diffractometer. The results show that the degree of the elongated grain is small after normalizing, and through the normalizing and cold-rolling process, the tissue of cold-rolled sheet is more uniform, the content of the beneficial {111}〈112〉 texture is relatively higher, and the intensity of α fiber texture is weakened and the intensity of γ fiber texture is gradually enhanced. When the reduction ratio is 88%, the content of {111}〈112〉 texture is the maximum and the intensity of γ fiber texture is the strongest, which is beneficial to the improvement of the {111}〈112〉 texture during the primary recrystallization and the growth of the Goss grains.
Similar content being viewed by others
References
J. Li, Y. Sun, Y. Zhao, Development of low temperature slab reheating technique for grain-oriented silicon steel. Iron Steel 42(10), 72–75 (2007)
J.T. Park, J.A. Szpunar, Evolution of recrystallization texture in nonoriented electrical steels. Acta Mater. 51(11), 3037–3051 (2003)
C.Y. Li, S.B. Zhou, X.R. Zhang, Lattice distortion stored energy of crystallographic orientations in cold-rolled low carbon steel sheets. Phys. Test. Chem. Anal. Part A Phys. Anal. 42(12), 595–598 (2006)
H. Inagaki, T. Suda, The development of rolling texture in low-carbon steels. Texture Stress Microstruct. 1(2), 129–140 (1972)
I. Samajdar, S. Cicale, B. Verlinden, Primary recrystallization in a grain oriented silicon steel: on the origin of goss {110}〈001〉 grains. Scripta Mater. 39(8), 1083–1088 (1998)
Z.C. Li, Q.C. Lv, Z.Z. He, A study of deformed and recrystallized textures and the mechanism of their changes in grain-oriented silicon steel sheets. Iron Steel Res. 3, 015 (1983)
I.V. Gervas’eva, V.A. Zimin, Textural and structural transformations in nonoriented electrical steel. Phys. Met. Metallogr. 108(5), 455–465 (2009)
Y. Zhao, Z.Z. He, Advances in research on mechanism of secondary recrystallization in grain oriented silicon steels. Iron Steel Res. 3(4), 79–90 (1991)
L. Wang, G. Cao, J. Zhang, Effect of combined RE–Ba–Sb addition on microstructure and mechanical properties of 4004 aluminum alloy. Trans. Nonferrous Met. Soc. China 23(8), 2236–2242 (2013)
C.Y. Li, S.B. Zhou, X.R. Zhang, Lattice distortion stored energy of crystallographic orientations in cold-rolled low carbon steel sheets. Phys. Testing. Chem. Anal. Part A: Phys. Anal. 42(12), 595–598 (2006)
R.D. Doherty, D.A. Hughes, F.J. Humphreys et al., Current issues in recrystallization: a review. Mater. Sci. Eng. A 238(2), 219–274 (1997)
H. Li, Y.L. Feng, X.J. Qi et al., Study on microstructure and precipitates at different normalizing in Fe-3.15% Si low temperature oriented silicon steel. Acta Metall. Sin. 49(5), 562–568 (2013)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Su, C., Zhao, G., Zhang, S. et al. Effect of Normalizing Cooling Process and Cold-Rolling Reduction Ratio on the Microstructure and Macro-texture in Hi–B Steel. Metallogr. Microstruct. Anal. 6, 132–138 (2017). https://doi.org/10.1007/s13632-017-0338-9
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13632-017-0338-9