Effect of Basicity on the Reduction Behavior of Iron Ore Pellets

  • Manoja Kumar Mohanty
  • Srishti Mishra
  • Bhagiratha Mishra
  • Smarajit Sarkar
Research Article - Chemical Engineering
  • 6 Downloads

Abstract

Physicochemical properties of the iron ore pellets depend on the iron oxide concentrate, gangue content and the amount of fluxes added. The objective of this present work is to study the reducibility as well as the softening–melting behavior of the iron ore bearing fines (mainly containing hematite) pellet with lime to silica ratio (C/S) varying from 0.9 to 2.4 in the temperature range of 1100–\(1400 \,^{{\circ }}\hbox {C}\). Reduction test results show that the highest degree of reduction and degree of metallization of about 95.1 and 94.3%, respectively, are achieved for pellets having C/S ratio 1.6 reduced at \(1400\,^{{\circ }}\hbox {C}\) for 60 min. Further increase in C/S ratio resulted in lowering the reduction rates due to the formation of calcium ferrite phases as confirmed from X-ray diffractogram and photomicrographs. However, softening–melting characteristics study of slag (C/S above 1.6) revealed that the slag of C/S ratio 2.0 can be considered as primary slag.

Keywords

Iron ore pellet Reduction Basicity Softening–melting characteristics 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

References

  1. 1.
    Mandal, A.K.; Sarkar, A.; Sinha, O.P.: Conversion of solid waste fines of comminution process into feeding material of the Blast Furnace grade iron ore pellets. SGAT Bull. 13, 95–113 (2012)Google Scholar
  2. 2.
    Sarkar, A.; Mandal, A.K.; Sinha, O.P.: Pelletisation behavior of fluxed iron ore pellets of varying basicities made with waste fines. Int. J. Sci. Eng. 5, 9–14 (2013)CrossRefGoogle Scholar
  3. 3.
    Dwarapudi, S.; Ghosh, T.K.; Tathavadkar, V.; Denys, M.B.; Bhattacharjee, D.; Venugopal, R.: Effect of MgO in the form of magnesite on the quality and microstructure of hematite pellets. Int. J. Miner. Process. 112–113, 55–62 (2012)CrossRefGoogle Scholar
  4. 4.
    Nogueira, P.F.; Fruehan, R.J.: Blast furnace burden softening and melting phenomena – melting onset in acid and basic fluxed pellets. I&SM 30, 29–35 (2003)Google Scholar
  5. 5.
    Dwarapudi, S.; Ghosh, T.K.; Shankar, A.; Tathavadkar, V.; Bhattacharjee, D.; Venugopal, R.: Effect of pyroxenite flux on the quality and microstructure of hematite pellets. Int.l J. Miner. Process. 96, 45–53 (2010)CrossRefGoogle Scholar
  6. 6.
    Onoda, M., Tsuchiya, O., Sugiyama, T., Fujita, I.; Quality improvements of lime fluxed pellets. In: Proceedings of ISS-AIME 40th Iron Making Conference, Toronto, Canada, pp. 286-298 (1980)Google Scholar
  7. 7.
    Panigrahy, S.C.; Jena, B.C.; Rigaud, M.: Characterization of bonding and crystalline phases in fluxed pellets using peat moss and bentonite as binders. Metall. Trans. B. 21, 463–474 (1990)CrossRefGoogle Scholar
  8. 8.
    Umadevi, T.; Kumar, P.; Lobo, N.F.; Prabhu, M.; Mahapatra, P.C.; Ranjan, M.: Influence of Pellet Basicity (CaO/SiO2) on Iron Ore Pellet Properties and Microstructure. ISIJ Int. 51, 14–20 (2011)CrossRefGoogle Scholar
  9. 9.
    Iljana, M.; Kemppainen, A.; Paananen, T.; Mattila, O.; Pisilä, E.; Kondrakov, M.; Fabritius, T.: Effect of adding limestone on the metallurgical properties of iron ore pellets. Int. J. Miner. Process. 141, 34–43 (2015)CrossRefGoogle Scholar
  10. 10.
    Dwarapudi, S.; Ghosh, T.K.; Shankar, A.; Tathavadkar, V.; Bhattacharjee, D.; Venugopal, R.: Effect of pellet basicity and MgO content on the quality and microstructure of hematite pellets. Int. J. Miner. Process. 99, 43–53 (2011)CrossRefGoogle Scholar
  11. 11.
    Friel, J.J.; Erickson, E.S.: Chemistry, microstructure, and reduction characteristics of dolomite-fluxed magnetite pellets. Metall. Trans. B. 11, 233–243 (1980)CrossRefGoogle Scholar
  12. 12.
    Yadav, U.S.; Pandey, B.D.; Das, B.K.; Jena, D.N.: Influence of magnesia on sintering characteristics of iron ore. Ironnmak. Steelmak. 29, 91–95 (2002)CrossRefGoogle Scholar
  13. 13.
    Mandal, A.K.; Sinha, O.P.: Characterization of fluxed iron ore pellets as compared to feed material for blast furnace. J. Progress. Res. Chem. 2, 74–82 (2015)Google Scholar
  14. 14.
    Phillips, B.; Muan, A.: Phase equilibria in the system CaO-iron oxide-SiO2. Air. J. Am. Ceram. Soc. 42, 413–423 (1959)CrossRefGoogle Scholar
  15. 15.
    Biswas, A.K.: Principle of Blast Furnace Iron Making. Calcutta (1984)Google Scholar
  16. 16.
    Bogdandy, L. von., Engell, H.J.: The Reduction of Iron Ores. New York (1971)Google Scholar
  17. 17.
    Murakami, T.; Kodaira, T.; Kasai, E.: Effect of the reduction of calcium ferrite on disintegration behavior of sinter under high hydrogen atmosphere. ISIJ Int. 55, 1197–1205 (2015)CrossRefGoogle Scholar
  18. 18.
    Levin, E.M.; Robbins, C.R.; McMurdie, H.F.: Phase Diagrams for Ceramists. Fig. 2647, p. 185. The American Ceramic Society, Columbus (1969)Google Scholar
  19. 19.
    Mohanty, U.K.: Thermo Physical Properties of Some Metallorthermic Slags. Ph.D. thesis. NIT Rourkela, India (1998)Google Scholar
  20. 20.
    Behera, R.C.; Mohanty, U.K.; Mohanty, A.K.: Viscosity and constitution of slags associated with metallorthermic extraction of some less common metals. High Temp. Mater. Process. 9, 57–76 (1990)CrossRefGoogle Scholar
  21. 21.
    Dash, S.; Mohanty, N.; Mohanty, U.K.; Sarkar, S.: A novel technique for determination of flow characteristics of blast furnace slag. Open J. Met. 02, 42–47 (2012)CrossRefGoogle Scholar

Copyright information

© King Fahd University of Petroleum & Minerals 2018

Authors and Affiliations

  • Manoja Kumar Mohanty
    • 1
  • Srishti Mishra
    • 1
  • Bhagiratha Mishra
    • 2
  • Smarajit Sarkar
    • 1
  1. 1.Department of Metallurgical and Materials EngineeringNational Institute of TechnologyRourkelaIndia
  2. 2.Dalmia Institute of Scientific and Industrial ResearchRajgangpurIndia

Personalised recommendations