Abstract
A study was carried out to investigate the probable cause or events that might have led to the failure of two parallel natural gas pipes, API 5L X42 carbon steel (NPS 8) and the SDR 17, 125 mm medium density polyethylene pipes. These two pipes were laid side by side in the same trench with a water pipe. The investigation was performed by analyzing the existing design and construction data, visual inspection of failed pipes, and pipe material analysis. Investigation from the relevant pipes data suggests that the leaked water pipe was the first to fail. The leaked water pipe created high pressure water jetting that mixed with the backfilling soil to form water–sand–soil slurry with high erosive properties. The impact of this erosive slurry upon the NPS 8 pipe had caused serious losses of pipe coating materials. This phenomenon explains the rapid thinning of the steel pipe body which later led to its failure. Evidence from the metallurgical study using photomicrograph showed that the morphology of the steel material was consistent and did not show any evidence of micro fractures.
Similar content being viewed by others
References
National Transportation Safety Board: Pipeline Incident Report: Natural Gas Pipeline Rupture and Fire, Near Carlsbad, New Mexico, 19 August 2000. National Technical Information Service, Virginia (2000)
National Transportation Safety Board: Pipeline Incident Report: Natural Gas Pipeline Rupture and Fire in South Riding, Virginia, 7 July 1998. National Technical Information Service, Virginia (1998)
National Transportation Safety Board: Pipeline Accident Report: Natural Gas Pipeline Rupture and Subsequent Explosion St Cloud, Minnesota, 11 December 1998. National Technical Information Service, Virginia (1998)
National Transportation Safety Board: Pipeline Accident Report: Natural Gas Pipeline Rupture and Fire during Dredging of Tiger Pass, Louisiana, 23 October 1996. National Technical Information Service, Virginia (1996)
National Transportation Safety Board: Pipeline Accident Report: Texas Eastern Transmission Corporation Natural Gas Pipeline Explosion and Fire, Edison, New Jersey, 23 March 1994. National Technical Information Service, Virginia (1994)
National Transportation Safety Board: Pipeline Accident Report: UGI Utilities, Inc., Natural Gas Distribution Pipeline Explosion and Fire, Allentown, Pennsylvania, 9 June 1994. National Technical Information Service, Virginia (1994)
Hasan , F. , Iqbal J., Ahmed F.: Stress corrosion failure of high-pressure gas pipeline. Eng. Fail. Anal. 14, 801–809 (2007)
Hemandez-Rodridriguez M.A.L., Martinez-Delgado D., Gonzalez R., Perez Enzeta A., Mercado-Solis R.D., Rodriguez J.: Corrosive wear failure analysis in a natural gas pipeline. Wear 263, 567–571 (2007)
Shalaby H.M., Riad W.T., Alhazza A.A., Behbehani M.H.: Failure analysis of fuel supply pipeline. Eng. Fail. Anal. 13, 789–796 (2006)
Azevedo C.R.F.: Failure analysis of a crude oil pipeline. Eng. Fail. Anal. 13, 789–796 (2006)
AI-Bukhaiti M.A., Ahmed S.M., Badran F.M.F., Emara K.M.: Effect of impingement angle on slurry erosion behaviour and mechanism of 1017 steel and high-chromium white cast iron. Wear 262, 1187–1198 (2007)
Hamzah R., Stephenson D.J., Strutt J.E.: Erosion of materials used in petroleum production. Wear 186, 493–496 (2004)
Aimin F., Jinming L., Ziyun T.T.: Failure analysis of the impeller of slurry pump subjected to corrosive wear. Wear 181–182, 876–882 (1995)
Haugen K., Kvernvold O., Ronold A., Sandberg R.: Sand erosive of wear-resistance materials: erosion in choke. Wear 186–187, 179–188 (1995)
Majid Z.A., Mohsin R., Yaacob Z., Hassan Z.: Failure analysis of natural gas pipes. Eng. Fail. Anal. 17, 818–837 (2010)
Hasan F., Iqbal J., Ahmed F.: Consequential rupture of gas pipeline. Eng. Fail. Anal. 13, 127–135 (2006)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Majid, Z.A., Mohsin, R. Failure Investigation of Natural Gas Pipeline. Arab J Sci Eng 37, 1083–1088 (2012). https://doi.org/10.1007/s13369-012-0236-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13369-012-0236-z