Abstract
Based on the anthracene-pyrene dual core, a new blue fluorescent material in the form of a polymer was developed. After introducing styrene at the end of the dual-core, a polymer blue emitting material was obtained through radical polymerization. In the case of the newly synthesized Poly 1-(4-vinylphenyl)-6-(10-(4-vinyl-phenyl)anthracen-9-yl)pyrene (S-AP-S), it not only emitted in the blue region of 443 nm in solution state, but also showed a high photoluminescence quantum yield (PLQY) of 79%. When Poly S-AP-S was applied as an emitter to solution process organic light-emitting diodes (OLEDs), current efficiency of 4.48 cd/A and external quantum efficiency (EQE) of 3.62% were realized. It also exhibited the deep-blue color coordinates of (0.157, 0.094) which satisfy with the mobile specification.
Similar content being viewed by others
References
C. W. Tang and S. A. VanSlyke, Appl. Phys. Lett., 51, 913 (1987).
M. Wu, S. Yeh, C. Chen, H. Murayama, T. Tsuboi, W. Li, I. Chao, S. Liu, and J. Wang, Adv. Funct. Mater., 17, 1887 (2007).
Y. Sun, N. C. Giebink, H. Kanno, B. Ma, M. E. Thompson, and S. R. Forrest, Nature, 440, 908 (2006).
Z. Zhao, C. Deng, S. Chen, J. W. Lam, W. Qin, P. Lu, Z. Wang, H. S. Kwok, Y. Ma, and H. Qiu, Chem. Commun., 47, 8847 (2011).
Y. Wada, S. Kubo, and H. Kaji, Adv. Mater., 30, 1705641 (2018).
C. Li, Z. Ren, X. Sun, H. Li, and S. Yan, Macromolecules, 52, 2296 (2019).
Y. Hu, W. Cai, L. Yang, D. Chen, X. Yang, X. Jiang, S. Su, F. Huang, and Y. Cao, J. Mater. Chem. C, 6, 2690 (2018).
L. Duan, L. Hou, T. Lee, J. Qiao, D. Zhang, G. Dong, L. Wang, and Y. Qiu, J. Mater. Chem. C, 20, 6392 (2010).
Q. Wei, Z. Ge, and B. Voit, Macromol. Rapid Commun., 40, 1800570 (2019).
T. Chiba, Y. Pu, and J. Kido, J. Mater. Chem. C, 3, 11567 (2015).
J. Guo, Z. Zhao, and B. Z. Tang, Adv. Opt. Mater., 6, 1800264 (2018).
R. Furue, T. Nishimoto, I. S. Park, J. Lee, and T. Yasuda, Angew. Chem. Int. Ed., 55, 7171 (2016).
S. Kang, H. Jung, H. Lee, S. Park, J. Kim, and J. Park, J. Mater. Chem. C, 7, 14709 (2019).
S. Kang, J. Huh, J. Kim, and J. Park, J. Mater. Chem. C, 8, 11168 (2020).
H. Jung, H. Lee, S. Kang, B. An, K. S. Yook, Y. Park, B. Kim, and J. Park, Appl. Chem., 27, 455 (2016).
S. Kang, H. Lee, H. Jung, M. Jo, M. Jung, and J. Park, Dyes Pigm., 156, 299 (2018).
S. Baek, S. Kang, C. Son, S. J. Shin, J. H. Kim, J. Park, and S. Kim, Adv. Opt. Mater., 8, 1901897 (2020).
S. Kang, R. Jillella, J. Jeong, Y. Park, Y. Pu, and J. Park, ACS Appl. Mater. Interfaces, 12, 51756 (2020).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Acknowledgment: This work was supported by a grant from Kyung Hee University in 2018 (KHU-20180243).
Supporting information: Information includes general information, optical properties, and film morphology. The materials are available via the Internet at http://www.springer.com/13233.
Supporting Information
Rights and permissions
About this article
Cite this article
Kang, S., Kwon, H., Jeong, J. et al. Synthesis and Electroluminescence Properties of New Blue Emitting Polymer Based on Dual-Core Type for Solution Process OLEDs. Macromol. Res. 30, 454–459 (2022). https://doi.org/10.1007/s13233-022-0053-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13233-022-0053-5