Abstract
To investigate the effects of holding time after deposition of polyethylenimine (PEI) solution and molecular weight of PEI on the surface morphology of multi-layer films prepared by layer-by-layer (LbL) method, polyamic acid (PAA)/PEI/graphene oxide (GO) films were prepared using different holding times and different molecular weights of PEI. To convert PAA into polyimide (PI), the films were thermally imidized after film deposition. In this process, GO was also converted into partially reduced GO (rGO). The effects of holding time and molecular weight of PEI on the surface morphology and the sheet resistance of PI/PEI/rGO films were investigated. Also, to investigate the effect of rGO on the barrier properties of PI based multilayer films, (PI/PEI/rGO/PEI)6 films were prepared by LbL method. Longer holding time (10 min) and smaller molecular weight (25,000) of PEI lead to relatively flat surfaces, but shorter holding time (5 min) and larger molecular weight (75,000) result in wrinkled and overlapped surfaces. The sheet resistance of PI/PEI25K/rGO films prepared with holding time 10 and 5 min is 502.1 kΩ/sq and out of range (> 2000 kΩ/sq), respectively. The sheet resistance of PI/PEI75K/rGO films prepared with holding time 10 min is out of range (> 2000 kΩ/sq). Gas transmission rate (GTR) and permeability coefficient of (PI/PEI25K/rGO/PEI25K)6 are lower than those of (PI/PEI75K/rGO/PEI75K)6, respectively.
References
M. C. Choi, Y. Kim, and C. S. Ha, Prog. Polym. Sci., 33, 581 (2008).
Y. G. Tropsha and N. G. Harvey, J. Phys. Chem. B, 101, 2259 (1997).
C. Cho, F. Xiang, K. L. Wallace, and J. C. Grunlan, Macromolecules, 48, 5723 (2015).
R. K. Iler, J. Colloid Interface Sci., 21, 569 (1966).
S. W. Keller, H.-N. Kim, and T. E. Mallouk, J. Am. Chem. Soc., 116, 8817 (1994).
Y. Long, T. Wang, L. Liu, G. Liu, and G. Zhang, Langmuir, 29, 3645 (2013).
N. A. Kotov, I. Dekany, and J. H. Fendler, J. Phys. Chem., 99, 13065 (1995).
Y. Lvov, G. Decher, and G. Sukhorukov, Macromolecules, 26, 5396 (1993).
A. Y. W. Sham, and S. M. Notley, J. Colloid Interface Sci., 32, 456 (2015).
M.-H. Tsai, I.-H. Tseng, Y.-C. Huang, H.-P. Yu, and P.-Y. Chang, Adv. Eng. Mater., 18, 582 (2016).
G. Wang, Y. Kim, M. Choe, T.-W. Kim, and T. Lee, Adv. Mater., 23, 755 (2011).
R. Rajasekar, N. H. Kim, D. Jung, T. Kuila, J. K. Lim, M. J. Park, and J. H. Lee, Compos. Sci. Technol., 89, 167 (2013).
W. S. Hummers and R. E. Offeman, J. Am. Chem. Soc., 80, 1339 (1958).
V. V. Tsukruk, V. N. Bliznyuk, D. Visser, A. L. Campbell, T. J. Bunning, and W. W. Adams, Macromolecules, 30, 6615 (1997).
M. Schneider, P. Frantz, and S. Granick, Langmuir, 12, 994 (1996).
E. L. Cussler, S. E. Hughes, W. J. Ward, and R. Aris, J. Membr. Sci., 38, 161 (1988).
H. Ito, W. Oka, H. Goto, and H. Umeda, Jpn. J. Appl. Phys., 45, 4325 (2006).
Author information
Authors and Affiliations
Corresponding authors
Additional information
Acknowledgments: The work was supported by the National Research Foundation of Korea (NRF) Grant funded by the Ministry of Science, ICT, and Future Planning, Korea {Acceleration Research Program (NRF-2014 R1A2A111 054584); Brain Korea 21 Plus Program (21A2013800002)} and Dongseo University.
Electronic supplementary material
Rights and permissions
About this article
Cite this article
Li, Y., Choi, MC., Jeong, KM. et al. Layer-by-layer assembly of graphene on polyimide films via thermal imidization and synchronous reduction of graphene oxide. Macromol. Res. 25, 496–499 (2017). https://doi.org/10.1007/s13233-017-5093-x
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13233-017-5093-x