Abstract
A trimer with thermally crosslinkable vinyl groups, (4-butyl-phenyl)-bis-[4-((4-vinyl-phenyl)-(4-butyl-phenyl)-phenyl-amine)-phenyl]-amine (3-TPA), was synthesized successfully. Differential scanning calorimetry (DSC) thermogram of 3-TPA showed two endothermic processes at 122 and 218 °C at the first heating scan. The endothermic peak at 122 °C corresponds to the melting behavior of 3-TPA and the other at 218 °C seems to be from thermal crosslinking. Thermally cured 3-TPA film at 180 °C for 1 h showed very good solvent resistance and was electrochemically stable. The highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) energy levels of cured 3-TPA film was −5.09 and −2.10 eV, respectively. The turn on electric field of PLEDs with cured 3-TPA was 1.37–1.80 MV/cm, which was smaller than that of the device without 3-TPA (2.51 MV/cm). The luminance efficiency and brightness of polymer light-emitting diodes (PLEDs) based on 3-TPA were much higher than that of the PLED without 3-TPA. This is due to that cured 3-TPA has hole injection and transporting property. Among the PLEDs, the device with a 20 nm-thick cured 3-TPA showed the best performance with a maximum efficiency of 1.29 cd/A and a maximum brightnes of 2,500 cd/m2.
Similar content being viewed by others
References
A. J. Heeger, Angew. Chem. Int. Ed., 40, 2591 (2001).
R. H. Friend, R. W. Gymer, A. B. Holmes, J. H. Burroughes, R. N. Marks, C. Taliani, D. D. C. Bradley, D. A. Dos Santos, J. L. Bredas, M. Logdlund, and W. R. Salaneck, Nature (London), 397, 121 (1999).
J. Hou, H.-Y. Chen, S. Zhang, G. Li, and Y. Yang, J. Am. Chem. Soc., 130, 16144 (2008).
J. H. Kwon, H.-D. Yeo, H.-J. Cha, M. J. Lee, H.-T. Park, J.-H. Park, C.-E. Park, and Y.-H. Kim, Macromol. Res., 19, 197 (2011).
M. Y. Jo, S. J. Park, T. Park, Y. S. Won, and J. H. Kim, Org. Electron., 13, 2185 (2012).
W. Shin, M. Y. Jo, D. S. You, Y. S. Jeong, D. Y. Yoon, J.-W. Kang, J. H. Jo, G. D. Lee, S.-S. Hong, and J. H. Kim, Synth. Met., 162, 768 (2012).
Z. Bao, A. Dodabalapur, and A. J. Lovinger, Appl. Phys. Lett., 69, 4108 (1996).
H. Sirringhaus, N. Tessler, and R. H. Friend, Science, 280, 1741 (1998).
A. Babel and S. A. Jenekhe, Adv. Mater., 14, 371 (2002).
D. C. Kim, T. W. Lee, J. E. Lee, K. H. Kim, M. J. Cho, D. H. Choi, Y D. Han, M. Y. Cho, and J.-S Joo, Macromol. Res., 17, 491 (2009).
A. Babel and S. A. Jenekhe, J. Phys. Chem. B, 107, 1749 (2003).
A. Babel and S. A. Jenekhe, Macromolecules, 36, 7759 (2003).
S. A. Sapp, G. A. Sotzing, and J. R. Reynolds, Chem. Mater., 10, 2101 (1998).
J. Kim, Y. Kim, and E. Kim, Macromol. Res., 17, 791 (2009).
L. Sen, X. Jiang, H. Ma, M. S. Liu, and A. K.-Y. Jen, Macromolecules, 33, 3514 (2000).
X. Jiang, L. Sen, H. Ma, M. S. Liu, and A. K.-Y. Jen, Appl. Phys. Lett., 76, 2985 (2000).
J. H. Kim, S. Liu, A. K.-Y. Jen, B. Carlson, L. R. Dalton, C.-F. Shu, and R. Dodda, Appl. Phys. Lett., 83, 776 (2003).
J. H. Kim, P. Herguth, M.-S. Kang, Y.-H. Tseng, and C.-F. Shu, Appl. Phys. Lett., 85, 1116 (2004).
M. S. Liu, Y.-H. Niu, J.-W. Ka, H.-L. Yip, F. Huang, J. Luo, T.-D. Kim, and A. K.-Y. Jen, Macromolecules, 41, 9570 (2008).
Y. -J. Cheng, M. S. Liu, Y. Zhang, Y.-N. Niu, F. Huang, J.-W. Ka, H.-L. Yip, Y. Tian, and A. K.-Y. Jen, Chem. Mater. 20, 413 (2008).
M. S. Jung, W. Shin, S. J. Park, H. You, J. B. Park, H. Suh, Y. Lim, D. Y. Yoon, and J. H. Kim, Synth. Met., 159, 1928 (2009).
Y. Lim, Y.-S. Park, Y. Kang, D. Y. Jang, J. H. Kim, J.-J. Kim, A. Sellinger, and D. Y. Yoon, J. Am. Chem. Soc., 133, 1375 (2011).
M. Y. Jo, S. S. Park, and J. H. Kim, Synth. Met., 162, 70 (2012).
M. Y. Jo, Y. Lim, B.-H. Ahn, G. D. Lee, and J. H. Kim, Bull. Korean Chem. Soc., 33, 492 (2012).
P. Herguth, X. Jiang, M. S. Liu, and A. K.-Y. Jen, Macromolecules, 35, 6094 (2002).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Hong, H., Jo, M.Y., Ha, Y.E. et al. Synthesis and characterization of thermally cross-linkable trimer based on triphenylamine. Macromol. Res. 21, 321–326 (2013). https://doi.org/10.1007/s13233-013-1116-4
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13233-013-1116-4