Evaluation of Mechanical Properties and Structure of Al-1100 Composite Reinforced with ZrO2 Nanoparticles via Accumulative Roll-Bonding

Abstract

In this study, aluminum metal matrix composites reinforced with ZrO2 nano-particles in volume fraction of 0.5, 0.75 and 1 % were manufactured through accumulative roll bonding (ARB) process. The results of composite microstructure indicated excellent ZrO2 particle distribution in the Al matrix after 10 cycles of ARB process. The X-ray diffraction results also showed that nanostructured Al/ZrO2 nano-particles composite with the average crystallite size of 48.6 nm was successfully achieved after 10 cycles of ARB process. The tensile tests were conducted on the ARBed strips. The tensile strength increased 2.15 times more than the initial value. The elongation dropped abruptly at the first cycle, and then increased slightly. The SEM images observations from the fracture surface showed that after 10 cycles of ARB process the fracture was almost shear fracture mode with fine and stretched pores.

This is a preview of subscription content, access via your institution.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6

References

  1. 1.

    Tsuji N, Saito Y, Lee S, Minamino Y, Adv Eng Mater 5 (2003) 338.

    Article  Google Scholar 

  2. 2.

    Lee S H, Saito Y, Tsuji N, Utsunomiya H, Sakai T. Scr Mater 46 (2002) 281.

    Article  Google Scholar 

  3. 3.

    Valiev R Z, Islamgaliev R K, Alexandrov I V, Prog Mater Sci 45 (2000) 103.

    Article  Google Scholar 

  4. 4.

    G. Sakai, Z. Horita, T.G. Langdon, Mater. Sci. Eng. A 393 (2005) 344.

    Article  Google Scholar 

  5. 5.

    Yin J, Lu J, Ma H, Zhang P, J Mater Sci 39 (2004) 2851.

    Article  Google Scholar 

  6. 6.

    Wang Q, Chen Y, Liu M, Lin J, Roven H J, Mater Sci Eng A 527 (2010) 2265.

    Article  Google Scholar 

  7. 7.

    Jafarian H, Borhani E, Shibata A, Terada D, Tsuji N, J Mater Sci 46 (2011) 4216.

    Article  Google Scholar 

  8. 8.

    Baazamat S, Tajally M, Borhani E, J Alloys Compd, 653 (2015) 39-46.

    Article  Google Scholar 

  9. 9.

    Hajizadeh K, Tajally M, Emadoddin E, Borhani E, J Alloys Compd, 588 (2014) 690.

    Article  Google Scholar 

  10. 10.

    Jafarian H, Borhani E, Shibata A, Tsuji N, J Alloys Compd, 577 (2013) 668.

    Article  Google Scholar 

  11. 11.

    Jafarian H, Borhani E, Shibata A, Terada D, Tsuji N, Mater Sci Forum, 667 (2010) 361.

    Article  Google Scholar 

  12. 12.

    Borhani E, Jafarian H, Adachi H, Terada D, Tsuji N, Mater Sci Forum, 667 (2010) 211.

    Article  Google Scholar 

  13. 13.

    Borhani E, Jafarian H, Shibata A, Tsuji N, Mater Trans 53 (2012) 1863.

    Article  Google Scholar 

  14. 14.

    Borhani E, Jafarian H, Terada D, Adachi H, Tsuji N, Mater Trans 53 (2012) 72.

    Article  Google Scholar 

  15. 15.

    Shu K M, Tu G C, Mater Manuf Process 16 (2001) 483.

    Article  Google Scholar 

  16. 16.

    Liu Y M, Li H C, Liou S S, Shie M T, Master Sci Eng A 373 (2007) 363.

    Google Scholar 

  17. 17.

    Hosseini S A, Manesh H D, Mater Des 30 (2009) 2911.

    Article  Google Scholar 

  18. 18.

    Jamaati R, Amirkhanlou S, Toroghinejad M R, Niroumand B, Mater Sci Eng A 528 (2011) 2143.

    Article  Google Scholar 

  19. 19.

    Jamaati R, Toroghinejad M R, Mater Sci Eng A 527 (2010) 4858.

    Article  Google Scholar 

  20. 20.

    Yazdani A, Salahinejad E, Mater Des 32 (2011) 3137.

    Article  Google Scholar 

  21. 21.

    Soltani M A, Jamaati R, Toroghinejad M R, Mater Sci Eng A 550 (2012) 367.

    Article  Google Scholar 

  22. 22.

    Amirkhanlou S, Ketabchia M, Parvin N, Khorsand S, Bahrami R, Mater Des 51 (2013) 367.

    Article  Google Scholar 

  23. 23.

    Salimi S, Izadi H, Gerlich A P, J Mater Sci 46 (2011) 409.

    Article  Google Scholar 

  24. 24.

    Khorramie S A, Baghchesara M A, Lotfi R, Moradi Dehagi S, Int J Nano Dim 4 (2012) 261.

  25. 25.

    Li G, Li W, Zhang M, Tao K, Catal Today 93 (2004) 595.

    Article  Google Scholar 

  26. 26.

    Kitazono K, Kikuchi Y, Sato E, Kuribayashi K, Mater Lett 61 (2007) 1771.

    Article  Google Scholar 

  27. 27.

    Jamaati R, Toroghinejad M R, Mater Sci Eng A 527 (2010) 4146.

    Article  Google Scholar 

  28. 28.

    Akbari-Beni H, Alizadeh M, Ghaffari M, Amini R, Compos Part B 58 (2014) 438.

    Article  Google Scholar 

  29. 29.

    Kitahara H, Yada T, Tsushidab M, Andoa S, Pro Eng 10 (2011) 2737.

    Article  Google Scholar 

  30. 30.

    Monzen R, Takagawa Y, Watanabe C, Terada D, Tsuji N, Proc Eng 10 (2011) 2417.

    Article  Google Scholar 

  31. 31.

    Williamson G K, Hall W H, Acta Metall 1 (1953) 22.

    Article  Google Scholar 

  32. 32.

    Nasiri Dehsorkhi R, Qods F, Tajally M, Mater Sci Eng A 549 (2012) 206.

    Article  Google Scholar 

  33. 33.

    Borhani E, Microstructure and Mechanical Property of Heavily Deformed Al-Sc Alloy Having Different Starting Microstructures, PhD thesis (2012).

  34. 34.

    Borhani E, Jafarian H R, J Ultrafine Grained Nanostruct Mater 47, (2014) 1.

    Google Scholar 

  35. 35.

    [35] Alizadeh M, Paydar M H, J Alloys Compds 492 (2010) 231.

    Article  Google Scholar 

  36. 36.

    Jamaati R, Toroghinejad M R, Edris H, Mater Des 54 (2014) 168.

    Article  Google Scholar 

  37. 37.

    Jamaati R, Toroghinejad M R, Edris H, Salmani M R, Mater Des 56 (2014) 359.

    Article  Google Scholar 

  38. 38.

    Liu C Y, Wang Q, Jia Y Z, Zhang B, Jing R, Ma M Z, Jing Q, Liu R P, Mater Sci Eng A 547 (2012) 120.

    Article  Google Scholar 

  39. 39.

    Alizadeh M, Samiei M, Mater Des 56 (2014) 680-4.

    Article  Google Scholar 

  40. 40.

    Eizadjou M, Danesh Manesh H, Janghorban K, J Alloys Compd 474 (2009) 406.

    Article  Google Scholar 

  41. 41.

    Liu C Y, Wang Q, Jia Y Z, Zhang B, Jing R, Ma M Z, Jing Q, Liu R P, Mater Des 43 (2013) 367.

    Article  Google Scholar 

Download references

Author information

Affiliations

Authors

Corresponding author

Correspondence to Ehsan Borhani.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Salimi, A., Borhani, E. & Emadoddin, E. Evaluation of Mechanical Properties and Structure of Al-1100 Composite Reinforced with ZrO2 Nanoparticles via Accumulative Roll-Bonding. Trans Indian Inst Met 70, 989–995 (2017). https://doi.org/10.1007/s12666-016-0892-x

Download citation

Keywords

  • Accumulatively roll-bonded
  • Composites
  • Microstructure
  • ZrO2
  • Nanoparticles