Al–12Si–3Cu–1 Mg–1.78Ni alloy is widely used for piston parts in automobile industry. The present paper investigates the effect of aging time for 1–16 h at 180 °C after solution treatment of the alloy at 500 °C for 5 h, on alloys prepared by gravity casting and squeeze casting. The wear rate of the alloy shows a minimum at an intermediate aging time. The hardness and ultimate tensile strength showed a peak at intermediate aging time. Mechanical properties and wear resistance are found to be better in squeeze cast alloy. The result are explained based on the microstructure developed during casting process and on heat treatment for various durations.
Similar content being viewed by others
References
Li W, Ji-rong L, Guo-dong L, and Quiong-hua L, J Huzhong Univ Sci Technol 36 (2008) 92.
Raincon E, Lopez H, and Cineros H, Mater Sci Eng 519 (2009) 128.
Lee K, Kwon Y N, and Lee S, J Alloy Compd 461 (2008) 532.
Wang G, Bian X, Wang W, and Zhang J, Mater Lett 57 (2003) 4083.
Yasmin T, Khalid A, and Haque M M, J Mater Process Technol 153 (2004) 833.
Haque M M, and Sharif A, J Mater Process Technol 118 (2001) 69.
Murray M T, and Murray M, Fundam Alum Metall (2011) 57 217.
Zeren M, J Mater Process Technol 169 (2005) 292.
Dwivedi D K, Mater Sci Technol 19 (2003) 1091.
Franklin J R, and Das A A, Br Foundrym 77 (1984) 150.
Conflict of interest
None
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Krishnankutty, P., Kanjirathinkal, A., Joseph, M.A. et al. Effect of Aging Time on Mechanical Properties and Wear Characteristics of Near Eutectic Al–Si–Cu–Mg–Ni Piston Alloy. Trans Indian Inst Met 68 (Suppl 1), 25–30 (2015). https://doi.org/10.1007/s12666-015-0584-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-015-0584-y