Abstract
In the present investigation, dry sliding wear behavior of spray cast Al–6Si alloy in both as-sprayed and different cold rolled reductions have been studied as a function of applied load. The spray cast preform was cold rolled to increase its densification. The preform showed equiaxed grain morphology containing some irregular pores and these were almost eliminated by the cold rolling. The improved wear properties of cold rolled spray cast alloy are discussed on the basis of microstructural features at different rolling reductions and the nature of debris particles collected from wear test.
Similar content being viewed by others
References
Nadimpali R, and Ravi K J, Mater Process Technol 213 (2013) 401.
Hariprasad S, Sastry S M L, Jerina K L, and Lederich R J, Metall Trans 24 (1993) 865.
Rizzi P, Habib A, Castellero A, and Battezzati L, J Alloys Compd 5095 (2011) 5275.
Henrique A G, Andre L R B, Enrico J G, and Claudemiro B, J Alloys Compd 586 (2014) 139.
An J, Dong C, and Zhang Q Y, Tribol Int 36 (2003) 25.
Zhan M Y, Chen Z H, Yan H G, and Xia W J, J Mater Process Technol 182 (2007) 174.
Deshmukh A R, Sundararajan T, Dube R K, and Bhargava S, J Mater Process Technol 84 (1998) 56.
Tripathy M R, Dube R K, and Koria S C, J Mater Process Technol 190 (2007) 342.
Mervin H A, Maiti R, Mitra R, and Chakraborty M, Wear 265 (2008) 1606.
Singh D, and Dangwal S, J Mater Sci 41 (2006) 3853.
Anil M, Srivastava V C, Ghosh M K, and Ojha S V, Wear 268 (2010) 1250.
Rudrakshi G B, Srivastava V C, and Ojha S N, J Mater Sci Eng 457 (2007) 100.
Cai W D, and Lavernia E J, J Mater Sci Eng 226 (1997) 8.
Mervin H A, Sankar C, Mitra R, and M Chakraborty The Minerals, Metals and Materials Society and ASM International 38A (2007) 2110.
Hamid A A, Ghosh P K, Jain S C, and Ray S, Wear 260 (2006) 368.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mittal, R., Singh, D. Dry Sliding Wear Behavior of Cold Rolled Spray Cast Al–6Si Alloy. Trans Indian Inst Met 67, 551–557 (2014). https://doi.org/10.1007/s12666-014-0382-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-014-0382-y