Abstract
Thermal analysis of LM29 alloy and Ce added LM29 alloys was carried out. The effect of cerium addition on solidification parameters and microstructural features of hypereutectic Al-Si (LM29) alloy was studied using Newtonian analysis technique. Thermal analysis parameters such as primary and eutectic phase nucleation and solidus temperatures were determined. The addition of Ce to LM29 alloy decreased the nucleation temperature of primary silicon and eutectic silicon. The microstructural examination of Ce added LM29 alloys revealed the presence of a polyhedral shaped Al–Si–Ce compound that might have caused the refinement of primary and eutectic silicon. The dendrite coherency point temperature of LM29 alloy was found to be suppressed on addition of Ce.
Similar content being viewed by others
References
ASM Handbook, vol 2. ASM International, Materials Park, (1990).
Yilimaz F, Atasoy O A, and Elliot R, J Cryst Growth 118 (1992) 377.
Kezhuna H, Fuxiao Y, Dazhib Z, and Lianga Z, Trans Ind Inst Met 62 (2009) 367.
Kowata T, Horie H, Hiratsuka S, and Chida A, IMONO 66 (1994) 803.
Zhi-ying O, Xie-min M, and Mei H, J Shanghai University (English Edition) 11 (2007), 400.
Kores S, Voncina M, Kosec B, Mrvar P, and Medved J, Mater Technol 44 (2010) 137.
Harun M, Talib L A, and Daud A R, Wear, 194 (1996) 54.
Anasyida AS, Daud A R, and Ghazali M J, Mater Des 31 (2010) 365.
Shabestri S G, and Ghodrat S, Mater Sci Eng A 467 (2007) 150.
Djurdjevic M, Jiang H, and Sokolowski J, Mater Charact 46 (2001) 31.
Niklas A, Abaunza U, Fernandez-calvo A I, Lacaze S, and Suarez R, China Foundry 8 (2011) 89.
Robles H F C, and Sokolowski J H, J Alloys Compd 419 (2006) 180.
Marchwica P, Sokolowski J H, and Kierkus W T, J Achieve Manuf Eng 47 (2011) 115.
Emadi D, Whiting L V, Djurdjevic M, Kierkus W T, and Sokolowski J, MJOM (2004) 10 91.
Djurdjevic M B, Huber G, and Odanovic Z, J Thermal Anal Calorim (2012) doi: 10.1007/s10973-012-2389-0.
Chavez-zamarripa R, Ramos-salaa J A, Talamantes-silva J, Valtierra S, and Colas R, Metall Mater Trans A 38A (2007) 1875.
Veldman N L M, Dahle A K, St. Hohn D H, and Arnberg L Metall Mater Trans A 32A (2001) 147.
Malekan M, and Shabestri S G, Metall Mater Trans A 42A (2009) 3196.
Djurdjevic M B, Sokolowski J H, and Odanovic Z, J Thermal Anal Calorim 109 (2012) 875.
Xu C L, and Jiang Q C, Mater Sci Eng A 437 (2006) 451.
Shou-ren W, Ru M, Ying-zi W, Yong W, and Li-ying Y, Trans Nonferrous Met Soc China 22 (2012) 1264.
Lu S, and Hellawell A, J Cryst Growth 73 (1985) 316.
Elliot R, Eutectic Solidification, Processing Butterworths, London (1983).
Faraji M, Todd I, and Jones, H, Metall MaterTrans A 40A (2009) 1710.
Vijeesh V, Ravi M, and Prabhu K N, Mater Perform Charact 2 (1) Paper ID: MPC20120007 (2013).
Raghavan V, J Phase Equilibria Diffus 28 (2007) 456.
Grobner J, Mirkovic D, and Schmid-Fetzer R, Metall Mater Trans A 35A (2004) 3349.
Wu Y, Liu X, Jiang B, and Huang C, Rare Metals 29 (2010) 62.
Acknowledgments
One of the authors (VV) thanks National Institute of Technology Karnataka for the Research Scholarship. Authors acknowledge the help received from Mr. Sathish and Mr. Dinesha, Technicians, Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka (NITK), Surathkal, during the casting process. Authors also thank Ms. Rashmi Banjan, SEM operator, National Institute of Technology Karnataka (NITK), Surathkal, for her assistance during scanning electron microscopy.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Vijeesh, V., Prabhu, K.N. Computer Aided Cooling Curve Analysis and Microstructure of Cerium Added Hypereutectic Al–Si (LM29) Alloy. Trans Indian Inst Met 67, 541–549 (2014). https://doi.org/10.1007/s12666-014-0379-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-014-0379-6