Abstract
ZrN coatings were grown on silicon (100) substrate by reactive pulsed direct current sputtering in a mixture of argon and nitrogen gases. The structural parameters and crystallite size as a function of substrate temperatures in the range 300–873 K were studied using x-ray diffraction. A comparative wear Study of ZrN coatings was performed with steel and ceramic balls to evaluate the frictional properties of coatings. It was found that coefficient of friction of ZrN coatings tested with steel ball is lower than the coatings tested with ceramic balls. It is also found that the coefficient of friction is lower for the coatings deposited at higher temperature (873 K) than the coatings deposited at lower temperature (300 K). The morphology and phase distribution of the wear tracks were examined using scanning electron microscope and were correlated with tribological properties
Similar content being viewed by others
References
Holmberg K A, Mathews and Dowson D, Coatings Tribology: Properties, Techniques and Applications in Surface Engineering. Amsterdam: Elsevier; (1994).
Ducros C, Benevent V and Sanchette F, Surface and Coatings Technology 163–164 (2003) 681.
Kalss W, Reiter A, Derflinger V, Gey C and Endrino J L, Int J Refract Met Hard Mater 24(5) (2006) 399.
Pichon L, Girardeau T, Straboni A, Lignou F and Guerin P, J. Applied Surface Science 150 (1999) 115.
Jehn H A, Surface and Coatings Technology 131 (2000) 433.
Hübler R, Surface and Coatings Technology 158 (2002) 680.
Brown R, Alias M N and Fontana R, Surf Coat Technology 62 (1993) 467.
Chou W J, Yu G P and Huang J H, Thin Solid Films 403(I 1–2, 22) (2002) 162.
Pilloud D, Dehlinger A S, Pierson J F, Roman A and Pichon L, PSE 2002 paper TuPSC16.
Ramana J V, Kumar S, David C, Ray A K and Raju V S, Mater. Lett. 43 (2000) 73.
Constantin R and Miremad B, Surf. Coat. Technol. 120–121 (1999) 728.
Boxman R, Zhitomirsky V, Grimberg I, Rapoport L, Goldsmith S and Weiss B, Surf. Coat. Technol. 125 (2000) 257.
Han J G, Ion J S, Kim H J and Song K, Surf. Coat. Technol. 85-–87 (1996) 82.
Ye. L. Ostrovskaya, Strelnitskij V E, Kuleba V I and Gamulya G D, Surf. Coat. Technol. 34 (2001) 255.
Wilson S and Alpas A T, Surf. Coat. Technol. 86–87 (1996) 75.
Mc Connell M L, Dowling D P, Donnelly N, Donnelly K and Flood R V, Surf. Coat. Technol. 116–119 (1999) 1133.
Xiao Z G, Mantei T D, Surface and Coatings Technology, 177–178 (2004) 389.
Yong M. Kim, Yun M. Chung, Min J. Jung, Musil J and Jeon G. Han, Surface and Coatings Technology, 200 (2005) 835.
Arup Dasgupta, Kuppusami P, Falix Lawrence, Raghunathan V S, Antony Premkumar P and Nagaraja K S, Materials Science and Engineering A, 374(1–2) (2004) 362.
Polcar T, Parreira N M G and Novák R, Surface & Coatings Technology 201 (2007) 5228.
Philip C. Dokko and Joseph A. Pask, Materials Science and Engineering, 25 (1976) 77.
Mo J L and Zhu M H, Wear 267 (2009) 874.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Singh, A., Geetha, M., Kumar, N. et al. A comparative wear study of sputtered ZrN coatings on Si substrate. Trans Indian Inst Met 64, 37 (2011). https://doi.org/10.1007/s12666-011-0007-7
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1007/s12666-011-0007-7