Abstract
The effect of warm working, hot working and heat treatment conditions on microstructure of Al-7.0%Si-0.45%Mg alloys were investigated in strain induced melt activation (SIMA) process. Predeformation of 30%, 40% and 50% was done by hot working. The hot working has been carried out at 380°C. The samples of various deformations were kept at 580°C, 590°C, 600°C with varied soaking time for 10, 20, 30 min respectively. It was found that increased predeformation reduced the soaking time to obtain globular α Al grains. The shape factor and metallography were done on SIMA processed Al-7.0%Si-0.45%Mg alloys. Those were compared with as cast Al-7.0%Si-0.45%Mg alloy and it was observed that strain induced predeformation and subsequently melt activation has caused the globular microstructure of the alloy.
Similar content being viewed by others
References
Sirong Yu, Dongcheng Li and Kim N, Microstructure Evolution of SIMA Processed Al2024, Mater. Sci. Emgg. A, 420 (2006). 165.
Kirkwood D H, Semi-Solid Metal Processing, Int. Mater Rev., 39 (1994) 173.
Srikanth Madhulika and Sharma Ashok, In pursuit of Advanced Technologies-Semi solid metal precessing, Foundry Journal, (2009) 75.
Zoqui Jose Eugenio and Robert Helena Maria; contribution to the Study of mechanisms involved in the formation of Rheocast structure; Journal of Materials processing Technology, 109 (2001) 251.
Zhang Q Q, Cao Z Y, Zhang Y F, Su G H and Liu Y B, Effect of Compression ration on the microstructure evolution of semisolid AZ91D alloy; Journal of Materials Processing Technology, 184 (2007) 195.
Ashouri S, Ahmadabadi Nili, Moradi M and Iranpour M, Semisolid microstructure evolution during reheating of Al A356 alloy deformed severely by ECAP, Journal of Alloys and Compounds (2007).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Srikanth, M., Sharma, A. The effect of predeformation and heat treatment on microstructure of Al-7.0% Si-0.45% Mg alloy cast through SIMA route. Trans Indian Inst Met 63, 11–14 (2010). https://doi.org/10.1007/s12666-010-0002-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12666-010-0002-4