Abstract
This study assesses the changes on the surface of crystalline stones due to salt crystallisation. Efflorescence was forced to grow on the surface of granite and marbles through 60 cycles of salt crystallisation with sodium sulphate. Changes on surface roughness, gloss and colour were measured every 15 cycles and the specimens were examined with naked eye and SEM. Sodium sulphate produces damage which depends on mineral composition. Results show that granites experience a mechanical decay with an increase in roughness. Peaks of mica can be observed on the surface and cracks widen and grow deeper. Colour and gloss do not show any significant change, although gloss decreases with an increase in surface roughness. In marbles, the decay is mainly chemical. Surface roughness increases due to dissolution of the calcite. White marbles exhibit yellowing. Gloss decreases during the first cycles—as grain boundaries become more visible—but tends to regain almost its initial value as the number of cycles increases. In this case, gloss does not show any relation with surface roughness.
Similar content being viewed by others
References
Alonso FJ, Vázquez P, Esbert RM, Ordaz J (2007) Influence of measuring conditions on roughness parameters of ornamental stones. In: Workshop: preservation of natural stone and rock weathering. Taylor & Francis, pp 13–16
Alonso FJ, Vázquez P, Esbert RM, Ordaz J (2008) Ornamental granite durability: evaluation of damage caused by salt crystallization test. Mater Construcc 58(289–290):191–201
Appelo CAJ, Postma D (1993) Geochemistry, groundwater and pollution. Balkema, Amsterdam, p 536
Arnold A (1976) Behaviour of some soluble salts in stone deterioration. In: 2nd International symposium on the deterioration of building stones, Athens, pp 27–36
Arnold A, Zehnder K (1985) Crystallization and habits of salt efflorescence on walls II: conditions of crystallization. In: Vth International congress of deterioration and conservation of stone, Laussane, pp 269–278
Battaglia S, Franzini M, Mango F (1993) High sensitivity apparatus for measuring linear thermal expansion: preliminary results on the response of marbles. Il Nuovo Cimiento 16:453–461
Benavente D, Martínez-Verdú F, Bernabeu A, Viqueira V, Fort R, García del Cura MA, Illueca C, Ordóñez S (2003) Influence of surface roughness on colour changes in building stones. Color Res Appl 28(5):343–351
Bionda D (2006) Modelling indoor climate and salt behaviour in historic buildings: a case study. Dissertation, ETH Zürich
Cardell-Fernández C, Benavente D, Rodríguez-Gordillo J (2008) Weathering of limestone building material by mixed sulfate solutions. Characterization of stone microstructure, reaction products and decay forms. Mater Charact 59:1371–1385
Charola AE, Lewin SZ (1979) Example of Stone decay due to salt efflorescence. In: 3rd International congress on the deterioration and preservation of stones, Venezia, pp 153–164
CIE (1932) Commission internationale de l’Eclairage proceedings, 1931. Cambridge University Press, Cambridge
Coussy O (2006) Deformation and stress from in-pore drying-induced crystallization of salt. J Mech Phys Solid 54(8):1517–1547
Erdogan M (2000) Measurement of polished stone surface brightness by image analysis methods. Eng Geol 57:65–72
Fischer C, Kaufhold S, Wedekind W, Dohrmann R, Karius V, Siegesmund S (2011) Weathering of Fruchtschiefer building stones: mineral dissolution or rock disaggregation? Environ Earth Sci 63:1665–1676. doi:10.1007/s12665-011-0986-z
Flatt RJ (2002) Salt damage in porous materials: how high supersaturations are generated. J Cryst Growth 242:435–454
Fletcher TE (2002) A simple model to describe relationships between gloss behaviour, matting agent concentration and the rheology of matted paints and coatings. Prog Org Coat 44:25–36
Gökay MK, Gundogdu IB (2008) Color identification of some Turkish marbles. Constr Build Mater 22(7):1342–1349
Görgülü K, Ceylanoglu A (2008) Evaluation of continuous grinding tests on some marble and limestone units with silicon carbide and diamond type abrasives. J Mater Process Technol 204:264–268
Grossi CM, Brimblecombe P (2004) Aesthetic of simulated soiling patterns on architecture. Environ Sci Tech 54(273):45–55
Grossi CM, Esbert RM (1994) Las sales solubles en el deterioro de rocas monumentales: revisión bibliográfica. Mater Construcc 44(235):15–30
Grossi CM, Esbert RM, Suarez del Río LM, Montoto M, Laurenzi-Tabasso M (1997) Acoustic emission monitoring to study sodium sulphate crystallization in monumental porous carbonate stone. Stud Conserv 42(2):115–125
Grossi CM, Esbert RM, Díaz-Pache F, Alonso FJ (2003) Soiling of building stones in urban environments. Build Environ 38:147–159
Grossi CM, Alonso FJ, Esbert RM, Rojo A (2007) Effect of laser cleaning on granite color. Color Res Appl 32(2):152–159
Huang HLY, Shen JY, Zhu HM, Xu XP (2002) Microstructure detection of a glossy granite surface machined by the grinding process. J Mater Process Technol 129:403–407
Juuti M, Prykäri T, Alarousu E, Koivula H, Myllys M, Lähteelä A, Toivakka M, Timonen J, Myllylä R, Peiponen KE (2007) Detection of local specular gloss and surface roughness from black prints. Coll Surf A Physicochem Engineering Aspects 299:101–108
Klanjsek Gunde M, Kunaver M, Cekada M (2007) Surface analysis of matt powder coatings. Dyes Pigment 74:202–207
López-Arce P, Varas-Muriel MJ, Fernández-Revuelta B, Álvarez de Buergo M, Fort R, Pérez-Soba C (2010) Artificial weathering of Spanish granites subjected to salt crystallization tests: surface roughness quantification. Catena 83(2–3):170–185. doi:10.1016/j.catena.2010.08.009
Martínez-Martínez J, Benavente D, García del Cura MA (2007) Pérdida del pulido de diferentes mármoles comerciales en ambientes salinos. Macla 7:92
Pinheiro Sousa FJ, Júnior NV, Weingaertner WL, Alarcón E (2007) Glossiness distribution over the surface of stoneware floor tiles due to the polishing process. J Mater Sci 42:10124–10132
Pinto Ribeiro R, Braga Paraguassú A (2008) Relationship between technological properties and slab surface roughness of siliceous dimension stones. Int J Rock Mech Min Sci 45(8):1526–1531
Price CA (2000) An expert chemical model for determining the environmental conditions needed to prevent salt damage in porous materials. Archetype Publications, London
Rodriguez-Navarro C, Doehne E (1999) Salt weathering: influence of evaporation rate, supersaturation and crystallization pattern. Earth Surf Proc Land 24:191–209
Rodriguez-Navarro C, Doehne E, Sebastián E (2000) How does sodium sulfate crystalize? Implications for the decay and testing of building materials. Cement Concr Res 30:1527–1534
Saidov TA, Espinosa-Marzal RM, Pel L, Scherer GW (2012) Nucleation of sodium sulfate heptahydrate on mineral substrates studied by nuclear magnetic resonance. J Cryst Growth 338:166–169
Selwitz C, Doehne E (2002) The evaluation of crystallization modifiers for controlling salt damage to limestone. J Cult Herit 3:205–216
Steiger M, Asmussen J (2008) Crystallization of sodium sulfate phases in porous materials: the phase diagram Na2SO4–H2O and the generation of stress. Geochim Cosmochim Acta 72:4291–4306
Streckeisen A (1976) To each plutonic rocks its proper name. Herat Sci 12:73–85
Török A, Licha T, Simon K, Siegesmund S (2011) Urban and rural limestone weathering; the contribution of dust to black crust formation. Environ Earth Sci 63(4):675–693
Tsui N, Flatt RJ, Scherer GW (2003) Crystallization damage by sodium sulphate. J Cult Herit 4:109–115
UNE-EN 12370 (1999) Natural stone test methods. Determination of resistance to salt crystallization
UNE-EN ISO 105-JO3 (1997) Textiles. Tests for colour fastness. Calculation of color differences
Vázquez P (2010) Granitos ornamentales: caracterización, durabilidad y sugerencias de uso. Tesis Doctoral, Universidad de Oviedo
Vázquez P, Luque A, Alonso FJ, Ordaz J, Sebastián E (2007) Diferencias de rugosidad en granitos y mármoles pulidos. In: XXVII Reunión Sociedad Española de Mineralogía (SEM), Jaén. Macla 7, p 99
Vázquez P, Esbert RM, Alonso FJ, Ordaz J (2008) Evaluation of damage induced by salt crystallization in granitic building stones. In: 11th International congress on deterioration and conservation of stone, vol I, pp 325–331
Warke PA, Smith BJ, Lehane E (2011) Micro-environmental change as a trigger for granite decay in offshore Irish lighthouses: implications for the long-term preservation of operational historic buildings. Environ Earth Sci 63:1415–1431. doi:10.1007/s12665-010-0662-8
Winkler EM, Singer PC (1972) Crystallization pressure of salts in stone and concrete. Geol Soc Am Bull 83:3509–3514
Zehner K, Arnold A (1988) New experiments on salt crystallization. In: 6th International congress on deterioration and conservation of stone. Torún
Acknowledgments
This research was funded by the “Fondo Social Europeo” from Spanish Ministry of Science and Innovation under project MAT2004-06804-C02-01, and by FICYT under the project IB09-080. The Asociación de Graniteiros de Galicia is thanked for providing the material used. We would like to thank Dr. David Benavente for his help in understanding the chemical processes.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Vázquez, P., Luque, A., Alonso, F.J. et al. Surface changes on crystalline stones due to salt crystallisation. Environ Earth Sci 69, 1237–1248 (2013). https://doi.org/10.1007/s12665-012-2003-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12665-012-2003-6