Carbon Dioxide Capture Using Amine Functionalized Hydrothermal Carbons from Technical Lignin
- 91 Downloads
Amine scrubbing is the most optimized and widely researched post combustion carbon dioxide capture technology till date. However, amine scrubbing remains costly because of high energy inputs during the regeneration stage. Although less researched, “solid sorbents” such as zeolite, active carbon, carbon coke, metal–organic frameworks and mesoporous silica are currently under development for CO2 capture as potential alternatives to amine scrubbers. In this study, sorbents were synthesized from carbonaceous materials (CMs) obtained from hydrothermally treated (350 °C) lignin, a waste material from forest biorefineries. CMs were activated with potassium hydroxide (KOH) at 800 °C to improve their textural properties and finally functionalized with polyethyleneimine (PEI) to also improve its CO2 capture properties. This study evaluated synergistic effect of these two treatments on adsorption capacity of CO2. Activation increased surface area of CMs from 2.8 to 1341 m2 g−1. CO2 capacities of 2 mmol g−1 (L350 PEI 5%) and 1.53 mmol g−1 (L350) could be reached at 30 °C, due to improved textural and chemical properties of the samples. Optimal PEI loading was determined to be 5%, after which CO2 sorption decreased with further additions of PEI. This was ascribed to blockage of the micro-pores in the activated samples at high PEI impregnation. Also, activated samples showed faster adsorption kinetics compared to PEI functionalized activated samples. The feasibility of using waste lignin with improved surface area and surface functionalities as alternative materials for CO2 adsorption was demonstrated.
KeywordsCarbon dioxide Polyethyleneimine (PEI) Activation Carbonaceous materials Lignin
The authors gratefully acknowledge the financial support of the USDA Northeast Sun Grant funded proposal (2014–2015) “Engineered High-Value Carbonaceous Products from Bio-refinery By-Products” and the USDA McIntire-Stennis Project # 1002913. The authors will also like to thank the School of Natural Resources, Davis College of Agriculture, Natural Resources and Design, West Virginia University, Morgantown, WV. USA and WVU Division of Diversity, Equity, & Inclusion, Chancellor’s Scholars Program for their partial financial support of Mr. Emmanuel Atta-Obeng Ph.D. studies.
- 15.Qi, G., Wang, Y., Estevez, L., Duan, X., Anako, N., Park, A.-H.A., Li, W., Jones, C.W., Giannelis, E.P.: High efficiency nanocomposite sorbents for CO2 capture based on amine-functionalized mesoporous capsules. Energy Environ. Sci. 4, 444–452 (2011). https://doi.org/10.1039/C0EE00213E CrossRefGoogle Scholar
- 19.Atta-Obeng, E., Dawson-Andoh, B., Seehra, M.S., Geddam, U., Poston, J., Leisen, J.: Physico-chemical characterization of carbons produced from technical lignin by sub-critical hydrothermal carbonization. Biomass Bioenergy 107, 172–181 (2017). https://doi.org/10.1016/j.biombioe.2017.09.023 CrossRefGoogle Scholar
- 20.Wang, X., Schwartz, V., Clark, J.C., Ma, X., Overbury, S.H., Xu, X., Song, C.: Infrared study of CO2 sorption over “molecular basket” sorbent consisting of polyethylenimine-modified mesoporous molecular sieve. J. Phys. Chem. C 113, 7260–7268 (2009). https://doi.org/10.1021/jp809946y CrossRefGoogle Scholar
- 28.Fierro, V., Torné-Fernández, V., Celzard, A.: Kraft lignin as a precursor for microporous activated carbons prepared by impregnation with ortho-phosphoric acid: synthesis and textural characterisation. Microporous and Mesoporous Materials. 92, 243–250 (2006). https://doi.org/10.1016/j.micromeso.2006.01.013 CrossRefGoogle Scholar
- 30.Falco, C., Marco-Lozar, J.P., Salinas-Torres, D., Morallón, E., Cazorla-Amorós, D., Titirici, M.M., Lozano-Castelló, D.: Tailoring the porosity of chemically activated hydrothermal carbons: influence of the precursor and hydrothermal carbonization temperature. Carbon 62, 346–355 (2013). https://doi.org/10.1016/j.carbon.2013.06.017 CrossRefGoogle Scholar
- 36.Yu, C.-H., Huang, C.-H., Tan, C.-S.: A review of CO2 capture by absorption and adsorption. Aerosol Air Qual. Res. 12, 745–769 (2012)Google Scholar