Production and Characterization of Concrete Paving Blocks Containing Ferronickel Slag as a Substitute for Aggregates

  • Original Paper
  • Published:
Waste and Biomass Valorization Aims and scope Submit manuscript

Abstract

The present work aims to investigate the potential valorization of ferronickel slag (FNS) as a substitute for aggregates in the production of H-shaped concrete paving blocks (CPB). FNS is a byproduct of the pyrometallurgical treatment of laterites for the recovery of Ni as ferronickel; its size distribution ranges within the specified limits for use as aggregates replacement, as shown by granulometric tests. Three compositions were prepared: a reference, containing only ordinary raw materials (CPBRef) and two others containing 10 wt% (CPB10) and 20 wt% (CPB20) aggregates replacement by FNS. Approximately 1000 blocks were produced in pilot scale for each composition. All mixtures were tested after 28 days of curing, in accordance with European Standard BS EN 1338 to determine water absorption, abrasion resistance, compressive and tensile/splitting strength. Spectral reflectance was measured on a UV–Visible-NIR spectrophotometer between 250 and 2500 nm, while thermal conductivity was determined by using a thermal conductivity analyzer. CPB morphological characteristics and microstructure were examined by scanning electron microscopy. Although it was found that limestone (LS) aggregates replacement by FNS relatively impaired the quality of the resulting CPB to a certain extent, the paving blocks using 10 wt% FNS met the minimum requirements specified by BS EN 1338 standard.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Pritchard, C., Dawson, S.: Precast Concrete Paving: A Design Handbook. Interpave, Leicester (1999)

    Google Scholar 

  2. Rada, G.R., Smith, D.R., Miller, J.S., Witchak, M.W.: Structural design of concrete block pavements. J. Transport. Eng. 116(5), 615–635 (1990)

    Article  Google Scholar 

  3. Interpave: Concrete Paving Block—Guide to the Properties Design, Construction, Reinstatement and Maintenance of Concrete Block Pavements, 2nd edn. Precast Concrete Paving and Kerb Association, Leicester (2005)

    Google Scholar 

  4. Ghafoori, N., Mathis, R.: Scaling resistance of concrete paving block surface exposed to deicing chemicals’. ACI Mater. J. 94(1), 32–38 (1997)

    Google Scholar 

  5. Soutsos, M.N., Tang, K., Millard, S.G.: Use of recycled demolition aggregate in precast products, phase II: concrete paving blocks. Constr. Build. Mater. 25(7), 3131–3143 (2011)

    Article  Google Scholar 

  6. Poon, C.S., Chan, D.: Paving blocks made with recycled concrete aggregate and crushed clay brick. Constr. Build. Mater. 20(8), 569–577 (2006)

    Article  Google Scholar 

  7. Hu, J., Wang, K., Gaunt, J.A.: Behavior and mix design development of concrete made with recycled aggregate from deconstructed lead-contaminated masonry materials. Constr. Build. Mater. 40, 1184–1192 (2013)

    Article  Google Scholar 

  8. Tavares, C.R.G., de Melo Franco, J.: Production of concrete paving blocks (CPB) utilizing electroplating residues—evaluation of mechanical and micro-structural properties. Can. J. Chem. Eng. 90(5), 1092–1101 (2012)

    Article  Google Scholar 

  9. Gencel, O., Ozel, C., Koksal, F., Erdogmus, E., Martínez-Barrera, G., Brostow, W.: Properties of concrete paving blocks made with waste marble. J. Clean. Prod. 21(1), 62–70 (2012)

    Article  Google Scholar 

  10. Uygunoglu, T., Topcu, I.B., Gencel, O., Brostow, W.: The effect of fly ash content and types of aggregates on the properties of pre-fabricated concrete interlocking blocks (PCIBs). Constr. Build. Mater. 30, 180–187 (2012)

    Article  Google Scholar 

  11. Wattanasiriwech, D., Saiton, A., Wattanasiriwech, S.: Paving blocks from ceramic tile production waste. J. Clean. Prod. 17, 1663–1668 (2009)

    Article  Google Scholar 

  12. Shinzato, M.C., Hypolito, R.: Solid waste from aluminum recycling process: characterization and reuse of its economically valuable constituents. Waste Manag 25, 37–46 (2005)

    Article  Google Scholar 

  13. Baeza-Brotons, F., Garcés, P., Payá, J., Saval, J.M.: Portland cement systems with addition of sewage sludge ash. Application in concretes for the manufacture of blocks. J. Clean. Prod. 82(1), 112–124 (2014)

    Article  Google Scholar 

  14. Dourdounis, E., Stivanakis, V., Angelopoulos, G.N., Chaniotakis, E., Frogoudakis, E., Papanastasiou, D., Papamantellos, D.C.: High-alumina cement production from FeNi-ERF slag, limestone and diasporic bauxite. Cem. Concr. Res. 34(6), 941–947 (2004)

    Article  Google Scholar 

  15. Diamantopoulos, A.S., Angelopoulos, G.N., Papamantellos, D.C.: Investigation of the sedimentation of FeNi fine grains entrained in ERF slag. Steel Res. 67, 179–187 (1996)

    Google Scholar 

  16. Balomenos, E., Panias, D.: Iron recovery and production of high added value products from the metallurgical by-products of primary aluminum and ferro-nickel industries. In Proceedings of the 3rd international slag valorisation symposium, pp. 161–172. Leuven (2013)

  17. Bartzas, G., Komnitsas, K.: Life cycle assessment of ferronickel production in Greece. Res. Conserv. Recycl. 105, 113–122 (2015)

    Article  Google Scholar 

  18. European Waste Catalogue and Hazardous Waste List: Environmental Protection Agency, Ireland, Valid from 1 Jan 2002

  19. Kirillidi, Y., Frogoudakis, E.: Electricarc furnace slag utilization. In: Proceedings of the 9th international conference on environmental science and technology, pp. 768–772. Rhodes (2005)

  20. Komnitsas, K., Zaharaki, D., Perdikatsis, V.: Effect of synthesis parameters on the compressive strength of low-calcium ferronickel slag inorganic polymers. J. Hazard. Mater. 161, 760–768 (2009)

    Article  Google Scholar 

  21. Komnitsas, K., Zaharaki, D., Bartzas, G.: Effect of sulphate and nitrate anions on heavy metal immobilisation in ferronickel slag geopolymers. Appl. Clay Sci. 73, 103–109 (2013)

    Article  Google Scholar 

  22. Katsiotis, N.S., Tsakiridis, P.E., Velissariou, D., Katsiotis, M.S., Alhassan, S.M., Katsioti, M.: Utilization of ferronickel slag as additive in Portland cement: a hydration and leaching study. Waste Biomass Valoriz., doi: 10.1007/s12649-015-9346-7 (2015, in press)

  23. American Society for Testing and Materials-ASTM. ASTM C 936. Standard specification for solid concrete-interlocking paving units, ASTM International (2001)

  24. British Standards Institution: EN 1338: Concrete Paving Blocks Requirements and Test Methods. British Standards Institution, London (2003)

    Google Scholar 

  25. British Standards Institution: EN 934-2: Admixtures for Concrete, Mortar and Grout. Concrete Aadmixtures, Definitions, Requirements, Conformity, Marking and Labelling. British Standards Institution, London (2009)

    Google Scholar 

  26. Mehta, P.K., Monteiro, P.J.M.: Concrete Microstructure, Properties, and Materials, 3rd edn. McGraw-Hill, New York (2006)

    Google Scholar 

  27. Bohac, M., Palou, M., Novotny, R., Masilko, J., Vsiansky, D., Stanek, T.: Investigation on early hydration of ternary Portland cement-blast-furnace slag-metakaolin blends. Constr. Build. Mater. 64, 333–341 (2014)

    Article  Google Scholar 

  28. Hellenic National Standard 244/80: Cement regulation for concrete construction works, Article 8 (1980)

  29. Levinson, R., Akbari, H.: Effects of composition and exposure on the solar reflectance of portland cement concrete. Cem. Concr. Res. 32(11), 1679–1698 (2002)

    Article  Google Scholar 

  30. American Society of Heating, Refrigerating and Air-Conditioning Engineers Inc, ASHRAE 189.1, Standard for the Design of High Performance Green Buildings Except Low-Rise Buildings, AHRAE, IES, and USGBC, Atlanta (2011)

  31. Demirboga, R.: Thermal conductivity and compressive strength of concrete incorporation with mineral admixtures. Build. Environ. 42(7), 2467–2471 (2007)

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Laboratory of Analytical and Inorganic Chemistry, School of Chemical Engineering, National Technical University of Athens, 9 Heroon Polytechniou St, 15773, Athens, Greece

    N. Dimitrioglou, N. S. Katsiotis & M. Beazi

  2. Laboratory of Physical Metallurgy, School of Mining and Metallurgical Engineering, National Technical University of Athens, 9 Heroon Polytechniou St, 15780, Athens, Greece

    P. E. Tsakiridis

  3. Chemical Engineering Department, The Petroleum Institute, PO Box 2533, Abu Dhabi, UAE

    M. S. Katsiotis

  4. Abolin Co., Galaxia 18 Afaia Skaramaga, Haidari, 12462, Athens, Greece

    P. Perdikis

Authors
  1. N. Dimitrioglou
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. P. E. Tsakiridis
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. N. S. Katsiotis
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. M. S. Katsiotis
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. P. Perdikis
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. M. Beazi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to P. E. Tsakiridis.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Dimitrioglou, N., Tsakiridis, P.E., Katsiotis, N.S. et al. Production and Characterization of Concrete Paving Blocks Containing Ferronickel Slag as a Substitute for Aggregates. Waste Biomass Valor 7, 941–951 (2016). https://doi.org/10.1007/s12649-015-9465-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12649-015-9465-1

Keywords

Search

Navigation