Crystallization of Hydrogenated Amorphous Silicon Thin Films Using Combined Continuous Wave Laser and Thermal Annealing

  • Research
  • Published:
Silicon Aims and scope Submit manuscript

Abstract

The thermal process of amorphous silicon thin film crystallization when combined with an aluminum (Al) film using a continuous wave (CW) laser is accompanied by additional interactions induced by the aluminum layer. This technique is frequently employed to optimize the crystallization process and enhance the quality of crystalline silicon by combining the thermodynamic effects of laser annealing with metal-induced crystallization (MIC). Hydrogenated amorphous silicon (a-Si:H) films were deposited using the plasma-enhanced chemical vapor deposition (PECVD) process on Corning glass substrates. An aluminum overcoat was deposited on the films. The specimens were irradiated with a continuous wave (CW) argon-ion (Ar +) laser beam of varying power density and duration. The samples were then annealed at 250 °C for 15 min to convert the amorphous silicon into polysilicon film. The grain size of the polycrystalline silicon films varies by varying the laser power density and the exposure time. The polysilicon grains acquired diameters ranging from 0.4 to 1.25 µm when the laser power density was set between 74.7 W/cm2 and 94.3 W/cm2. The grains with a size ranging between 1 and 2.5 µm showed plate-like and dendritic-like configurations when laser power densities changed between 31.4 and 74.7 W/cm2. The X-ray diffraction analysis (XRD) analysis revealed polycrystalline silicon with expected relative strengths.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

Data Availability

The data that support the findings of this study are available from the corresponding author, [AS], upon reasonable request.

References

  1. Park M et al (2020) Comprehensive analysis of blue diode laser-annealing of amorphous silicon films. Thin Solid Films 696:137779

    Article  Google Scholar 

  2. Çınar K, Yesil C, Bek A (2019) Revealing laser crystallization mechanism of silicon thin films via pulsed IR lasers. J Phys Chem C 124(1):976–985

    Article  Google Scholar 

  3. Do Y et al (2020) Remarkable improvement in foldability of poly-Si thin-film transistor on polyimide substrate using blue laser crystallization of amorphous Si and comparison with conventional poly-Si thin-film transistor used for foldable displays. Adv Eng Mater 22(5):1901430

    Article  CAS  Google Scholar 

  4. Zhang B et al (2007) Polysilicon thin film-transistors with uniform and reliable performance using solution-based metal-induced crystallization. IEEE Trans Electron Devices 54(5):1244–1248

    Article  CAS  Google Scholar 

  5. Lee S et al (2015) Localized tail states and electron mobility in amorphous ZnON thin film transistors. Sci Rep 5(1):1–9

    Google Scholar 

  6. Lai M-H, Wu YCS, Chang C-P (2011) Electrical performance and thermal stability of MIC poly-Si TFTs improved using drive-in nickel induced crystallization. Mater Chem Phys 126(1–2):69–72

    Article  CAS  Google Scholar 

  7. Cattin J et al (2021) Influence of light soaking on silicon heterojunction solar cells with various architectures. IEEE J Photovolt 11(3):575–583

    Article  Google Scholar 

  8. Li S et al (2019) In situ-doped silicon thin films for passivating contacts by hot-wire chemical vapor deposition with a high deposition rate of 42 nm/min. ACS Appl Mater Interfaces 11(33):30493–30499

    Article  CAS  PubMed  Google Scholar 

  9. He R et al (2016) High pressure chemical vapor deposition of hydrogenated amorphous silicon films and solar cells. Adv Mater 28(28):5939–5942

    Article  CAS  PubMed  Google Scholar 

  10. Moreno M et al (2021) Comparative study on the quality of microcrystalline and epitaxial silicon films produced by pecvd using identical sif4 based process conditions. Materials 14(22):6947

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  11. Sridhar N et al (1996) Effect of deposition temperature on the structural and electrical properties of laser-crystallized hydrogenated amorphous silicon films. J Appl Phys 79(3):1569–1577

    Article  CAS  Google Scholar 

  12. Chen J et al (2017) Control of grain size and crystallinity of poly-Si films on quartz by Al-induced crystallization. CrystEngComm 19(17):2305–2311

    Article  CAS  Google Scholar 

  13. Mohiddon M et al (2011) Growth, optical, and electrical properties of silicon films produced by the metal-induced crystallization process. J Nanopart Res 13(11):5999–6004

    Article  CAS  Google Scholar 

  14. Wu M et al (1999) High electron mobility polycrystalline silicon thin-film transistors on steel foil substrates. Appl Phys Lett 75(15):2244–2246

    Article  CAS  Google Scholar 

  15. Jang J et al (1998) Electric-field-enhanced crystallization of amorphous silicon. Nature 395(6701):481–483

    Article  CAS  Google Scholar 

  16. Chan K-Y et al (2008) High-mobility microcrystalline silicon thin-film transistors prepared near the transition to amorphous growth. J Appl Phys 104(5):054506

    Article  Google Scholar 

  17. Maity G et al (2019) Aluminum induced crystallization of amorphous Si: Thermal annealing and ion irradiation process. J Non-Cryst Solids 523:119628

    Article  CAS  Google Scholar 

  18. Hamasha E et al (2016) Aluminum induced crystallization of amorphous silicon thin films with assistance of electric field for solar photovoltaic applications. Sol Energy 127:223–231

    Article  CAS  Google Scholar 

  19. Pécz B et al (2021) Structural Characteristics of the Si Whiskers Grown by Ni-Metal-Induced-Lateral-Crystallization. Nanomaterials 11(8):1878

    Article  PubMed  PubMed Central  Google Scholar 

  20. Hara A et al (2004) High performance low temperature polycrystalline silicon thin film transistors on non-alkaline glass produced using diode pumped solid state continuous wave laser lateral crystallization. Jpn J Appl Phys 43(4R):1269

    Article  CAS  Google Scholar 

  21. Andrä G et al (2013) Multicrystalline silicon thin film solar cells based on a two-step liquid phase laser crystallization process. 2013 IEEE 39th Photovoltaic Specialists Conference (PVSC), Tampa, FL, USA, pp 1330–1333. https://doi.org/10.1109/PVSC.2013.6744388

  22. Said-Bacar Z et al (2012) CW laser induced crystallization of thin amorphous silicon films deposited by EBE and PECVD. Appl Surf Sci 258(23):9359–9365

    Article  CAS  Google Scholar 

  23. Jin S et al (2016) Lateral grain growth of amorphous silicon films with wide thickness range by blue laser annealing and application to high performance poly-Si TFTs. IEEE Electron Device Lett 37(3):291–294

    Article  CAS  Google Scholar 

  24. Jia G et al (2014) Nanotechnology enhanced solar cells prepared on laser-crystallized polycrystalline thin films (< 10 µm). Sol Energy Mater Sol Cells 126:62–67

    Article  CAS  Google Scholar 

  25. Lee Y-J et al (2013) Structural characterization of wavelength-dependent Raman scattering and laser-induced crystallization of silicon thin films. Thin Solid Films 542:388–392

    Article  CAS  Google Scholar 

  26. Al-Nuaimy E, Marshall J (1996) Excimer laser crystallization and doping of source and drain regions in high quality amorphous silicon thin film transistors. Appl Phys Lett 69(25):3857–3859

    Article  CAS  Google Scholar 

  27. Farid N et al (2021) Femtosecond laser-induced crystallization of amorphous silicon thin films under a thin molybdenum layer. ACS Appl Mater Interfaces 13(31):37797–37808

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  28. Chowdhury S et al (2020) Crystallization of Amorphous Silicon via Excimer Laser Annealing and Evaluation of Its Passivation Properties. Energies 13(13):3335

    Article  CAS  Google Scholar 

  29. Volkovoynova L et al (2022) Heat transfer estimation during laser-assisted metal-induced crystallization of amorphous silicon films. Proceedings of 8th International Congress on Energy Fluxes and Radiation Effects (EFRE–2022) Tomsk, Russia. https://doi.org/10.56761/EFRE2022.C3-P-005701

  30. Shariah A, Bataineh MI (2023) Electrical and Structural Properties of Crystallized Amorphous Silicon Thin Films. Silicon 15(6):2727–2735

    Article  CAS  Google Scholar 

  31. Nast O, Hartmann AJ (2000) Influence of interface and Al structure on layer exchange during aluminum-induced crystallization of amorphous silicon. J Appl Phys 88(2):716–724

    Article  CAS  Google Scholar 

Download references

Acknowledgements

The author would like to thank Prof. Hameed Naseem of Arkansas University's electrical engineering department for sample preparation and Prof. Surendra Singh of the Physics department for enabling me to utilize his laser facility.

Author information

Authors and Affiliations

  1. Department of Applied Physics, Jordan University of Science and Technology, Irbid, 22110, Jordan

    Adnan Shariah

Authors
  1. Adnan Shariah
    View author publications

    You can also search for this author in PubMed Google Scholar

Contributions

AS carried out the experimental work, AS put shape for the research, AS analyzed and interpreted the results, AS prepared the figures, AS wrote the final version and reviewed the manuscript.

Corresponding author

Correspondence to Adnan Shariah.

Ethics declarations

Ethics Approval

Not applicable.

Consent to Participate

Not applicable.

Consent for Publication

Not applicable.

Competing interests

The authors declare no competing interests.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

The author did not receive support from any organization for the submitted work.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Shariah, A. Crystallization of Hydrogenated Amorphous Silicon Thin Films Using Combined Continuous Wave Laser and Thermal Annealing. Silicon (2024). https://doi.org/10.1007/s12633-024-03003-x

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1007/s12633-024-03003-x

Keywords

Search

Navigation