Abstract
This study examined the effects of adding iron to rice hulls samples (RHs) on the thermal degradation to prepare nano silica and iron oxide-silica mixtures. Iron is precipitated in different amounts within the RH fibers (as hydroxide) by dipping them in a solution of different concentrations of acidic ferrous sulfate and then immersing it in a dilute ammonia solution. The dry RHs were fired at temperatures between 400 °C and 700 °C in a static or limited air atmosphere. Both weight loss and residual weight are determined to follow its thermal degradation. The products of the RH degradation of silica or iron oxide-silica mixtures were characterized by X-ray diffraction and Fourier transform infrared spectroscopy. The surface area, average particle size, and pore diameter of both products were determined. The chemical treatment of RHs before firing accelerates their thermal degradation and leads to obtaining firing products of high purity. Firing RHs in a limited air atmosphere increases thermal degradation and, at the same time, accelerates the catalyst effect of iron on its degradation. Under these conditions, silica and iron oxide bonded silica with an average particle size of 1.31 and 0.07 μm were obtained by firing treated RHs at 600 °C and 500 °C, respectively. Firing in a limited air atmosphere encourages CO2 to react with burned C to form CO, and iron as an accelerator for this reaction completes its degradation. In contrast, iron oxide remained in the ferrous state. Therefore, the bonding between iron and silica was complete.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Data Availability
Not applicable.
References
Chandrasekhar SATHY, Satyanarayana KG, Pramada PN, Raghavan P, Gupta TN (2003) Review processing, properties and applications of reactive silica from rice husk—an overview. J Mater Sci 38(15):3159–3168
Houston DF (1972) Rice hulls. Rice chemistry and Technology, pp 301–352
Lanning FC (1963) Plant constituents, silicon in rice. J Agric Food Chem 11(5):435–437
Sharma NK, Williams WS, Zangvil A (1984) Formation and structure of silicon carbide whiskers from rice hulls. J Am Ceram Soc 67(11):715–720
Ibrahim DM, El-Hemaly SA, Abdel-Kerim FM (1980) Study of rice-husk ash silica by infrared spectroscopy. Thermochim Acta 37(3):307–314
Thuadaij N, Nuntiya A (2008) Synthesis and characterization of nanosilica from rice husk ash prepared by precipitation method. J Nat Sci Special Issue on Nanotechnology 7(1):59–65
Yuvakkumar R, Elango V, Rajendran V, Kannan N (2014) High-purity nano silica powder from rice husk using a simple chemical method. J Exp Nanosci 9(3):272–281
Liou TH, Yang CC (2011) Synthesis and surface characteristics of nanosilica produced from alkali-extracted rice husk ash. Mater Sci Eng B 176(7):521–529
Liou TH (2004) Preparation and characterization of nano-structured silica from rice husk. Mater Sci Eng A 364(1–2):313–323
Carmona VB, Oliveira RM, Silva WTL, Mattoso LHC, Marconcini JM (2013) Nanosilica from rice husk: extraction and characterization. Ind Crop Prod 43:291–296
Ramachandran, VS, (1996) Concrete admixtures handbook: properties, science and technology. William Andrew
Chaudhary DS, Jollands MC, Cser F (2002) Understanding rice hull ash as fillers in polymers: a review. Silicon Chem 1(4):281–289
Adam F, Appaturi JN, Iqbal A (2012) The utilization of rice husk silica as a catalyst: review and recent progress. Catal Today 190(1):2–14
Mansour NA, Hanna SB (1979) Silicon carbide and nitride from rice hulls: II, effect of iron on the formation of silicon carbide. Trans J Br Ceram Soc 78(6):132–136
Natarajan E, Nordin A, Rao AN (1998) Overview of combustion and gasification of rice husk in fluidized bed reactors. Biomass Bioenergy 14(5–6):533–546
Soltani N, Bahrami A, Pech-Canul MI, González LA (2015) Review on the physicochemical treatments of rice husk for production of advanced materials. Chem Eng J 264:899–935
Hennig GR (1962) Catalytic oxidation of graphite. J Inorg Nucl Chem 24(9):1129–1137
Hanna SB, Farag LM (1985) Kinetic studies on thermal degradation of treated and untreated rice hulls. Thermochim Acta 87:239–247
Hanna SB, Farag LM, Mansour NA (1984) Pyrolysis and combustion of treated and untreated rice hulls. Thermochim Acta 81:77–86
Hua M, Zhang S, Pan B, Zhang W, Lv L, Zhang Q (2012) Heavy metal removal from water/wastewater by nanosized metal oxides: a review. J Hazard Mater 211:317–331
Uygur V, Rimmer DL (2000) Reactions of zinc with iron-oxide coated calcite surfaces at alkaline pH. Eur J Soil Sci 51(3):511–516
Zeng L (2003) A method for preparing silica-containing iron (III) oxide adsorbents for arsenic removal. Water Res 37(18):4351–4358
Xu Y, Axe L (2005) Synthesis and characterization of iron oxide-coated silica and its effect on metal adsorption. J Colloid Interface Sci 282(1):11–19
Ullah R, Deb BK, Mollah MYA (2014) Synthesis and characterization of silica coated iron-oxide composites of different ratios. Int J Compos Mater 4(2):135–145
Rusch B, Hanna K, Humbert B (2010) Coating of quartz silica with iron oxides: characterization and surface reactivity of iron coating phases. Colloids Surf A Physicochem Eng Asp 353(2–3):172–180
Andrade AL, Souza DM, Pereira MC, Fabris JD, Domingues RZ (2009) Synthesis and characterization of magnetic nanoparticles coated with silica through a sol-gel approach. Cerâmica 55:420–424
Tadic M, Kralj S, Kopanja L (2019) Synthesis, particle shape characterization, magnetic properties and surface modification of superparamagnetic iron oxide nanochains. Mater Charact 148:123–133
Krishnarao RV, Godkhindi MM (1992) Distribution of silica in rice husks and its effect on the formation of silicon carbide. Ceram Int 18(4):243–249
Rao GR, Sastry ARK, Rohatgi PK (1989) Nature and reactivity of silica available in rice husk and its ashes. Bull Mater Sci 12(5):469–479
Boucher, FB, (1977) Pyrolysis of industrial wastes for oil and activated carbon recovery (Vol. 1). Environmental Protection Agency, Office of Research and Development, industrial environmental research laboratory
Bruni S, Cariati F, Casu M, Lai A, Musinu A, Piccaluga G, Solinas S (1999) IR and NMR study of nanoparticle-support interactions in a Fe2O3-SiO2 nanocomposite prepared by a sol-gel method. Nanostruct Mater 11(5):573–586
Pretsch E, Bühlmann P, Affolter C, Pretsch E, Bhuhlmann P, Affolter C (2000) Structure determination of organic compounds. Springer-Verlag, Berlin, pp 121–122
Sodipo, BK, Azlan, AA (2015) Superparamagnetic iron oxide nanoparticles incorporated into silica nanoparticles by inelastic collision via ultrasonic field: role of colloidal stability. In AIP conference proceedings (Vol. 1657, No. 1, p. 100002). AIP Publishing LLC
Ahangaran F, Hassanzadeh A, Nouri S (2013) Surface modification of Fe 3 O 4@ SiO 2 microsphere by silane coupling agent. Int Nano Lett 3(1):1–5
Long FJ, Sykes KW (1952) The effect of specific catalysts on the reactions of the steam-carbon system. Proceed Royal Soc London Ser Math Phys Sci 215(1120):100–110
Liang Z, Yi L, Huang Z, Lu B, Dan C, Zhong R (2018) Effect of silica on reduction behaviors of hematite-carbon composite compact at 1223–1373 K. ISIJ International 59(2):227–234
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB). The authors declare that no funds, grants, or other support were received during the preparation of this manuscript.
Author information
Authors and Affiliations
Contributions
Samir Bushra Hanna contributed to the design and implementation of the research, to the analysis of the results and to the writing of the manuscript.
Tamer Sami Mansour contributed to the design and implementation of the research, to the analysis of the results and to the writing of the manuscript.
Noha Ahmed Ajiba contributed to the design and implementation of the research, to the analysis of the results and to the writing of the manuscript.
Corresponding author
Ethics declarations
Ethics Approval
Not applicable.
Consent to Participate
All authors agreed to take part in this study.
Consent for Publication
All authors agreed to publish this study.
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hanna, S.B., Mansour, T.S. & Ajiba, N.A. Processing and Characterization of Nano Silica and Iron Oxide Coated Silica Composites Extracted from Rice Hulls. Silicon 15, 6099–6111 (2023). https://doi.org/10.1007/s12633-023-02491-7
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12633-023-02491-7