Abstract
Rubber blending has been widely used to improve various properties in finished rubber products. The purpose of this paper is to investigate the effect of filler size, type, concentration, and surface treatment on the mechanical, swelling, dielectric, and morphology properties of ethylene propylene diene rubber (EPDM)/styrene-butadiene rubber (SBR) rubber blend nanocomposites filled with alumina (Al2O3) nanoparticles. Bis-(3-(triethoxysilyl)-propyl)-tetrasulfide (TESPT) was used as a silane coupling agent. Rubber blend nanocomposites containing Al2O3 nanoparticles were compared to carbon black (CB). The results indicate that the nanocomposites prepared, in particular with the TESPT, had better properties than the composites without the TESPT. Mechanical properties of the CB-filled EPDM/SBR rubber blend were noticeably improved, indicating CB's inherent reinforcing potential. We found that rubber nanocomposites' crosslink density and filler–rubber interaction increase, and the swelling coefficient decreases with increasing filler content. The dielectric properties of the nanocomposites showed a significant enhancement with fillers. SEM images showed that the CB sample had a higher distribution than Al2O3 due to good interaction and dispersion. This study's experimental data will help design and manufacture outdoor insulators.
Article PDF
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Availability of Data and Material
The author claims that the data and information in this article are all derived from this research, and the cited data and information have all been indicated in the article.
Data Availability
All data generated or analyzed during this investigation are included in this published article.
References
Ren PG, Si XH, Sun ZF et al (2016) Synergistic effect of BN and MWCNT hybrid fillers on thermal conductivity and thermal stability of ultra-high-molecular-weight polyethylene composites with a segregated structure. J Polym Res 23:1–11. https://doi.org/10.1007/s10965-015-0908-y
Mahmoud AM, Nasrat LS, Ibrahim AAA (2017) Dielectric Properties of Polymer Blends Using Least Square Method. Eur J Eng Res Sci 2:1. https://doi.org/10.24018/ejers.2017.2.1.207
Bazli L, Eskandarinezhad S, Kakur N et al (2021) Electrical properties of polymer blend composites based on Silicone rubber/EPDM/clay for high voltage insulators. J Compos Compd 2:18–24. https://doi.org/10.52547/jcc.3.1.3
Abdelsalam AA, Mohamed WS, Abd El-Naeem G, El-Sabbagh SH (2022) Effect of the silane coupling agent on the physicomechanical properties of EPDM/SBR/Al2O3 rubber blend nanocomposites. J Thermoplast Compos Mater 0:1–22. https://doi.org/10.1177/08927057211067702
Jasna VC, Ramesan MT (2017) Preparation, characterization, dielectric properties and diffusion studies of styrene butadiene rubber (SBR)/manganous tungstate (MnWO4) nanocomposites. AIP Conf Proc 1849
Abdelsalam AA, El-Sabbagh SH, Mohamed WS, Khozami MA (2022) Studies on swelling behavior, mechanical and thermal properties of ternary rubber blend composites in the presence of compatibilizers. Pigment Resin Technol. https://doi.org/10.1108/PRT-02-2022-0020
Komalan C, Poothanari MA, Maria H J, Thomas S (2019) Effect of blend ratio and compatibilisation on the electrical and dielectric properties of nylon copolymer (6, 66)/EPDM rubber blends. Polym Eng Sci 59:2195–2201. https://doi.org/10.1002/pen.25222
Abdelsalam AA, El-Sabbagh SH, Mohamed WS et al (2022) Effect of compatibilisers on the cure characteristics and mechanical properties of ternary rubber blend composites. Pigment Resin Technol. https://doi.org/10.1108/PRT-10-2021-0123
Zegaoui A, Derradji M, Ma R et al (2018) Silane-modified carbon fibers reinforced cyanate ester/benzoxazine resin composites: Morphological, mechanical and thermal degradation properties. Vacuum 150:12–23. https://doi.org/10.1016/j.vacuum.2018.01.025
Zegaoui A, Ma R, Dayo AQ et al (2018) Morphological, mechanical and thermal properties of cyanate ester/benzoxazine resin composites reinforced by silane treated natural hemp fibers. Chinese J Chem Eng 26:1219–1228. https://doi.org/10.1016/j.cjche.2018.01.008
Derradji M, Ramdani N, Gong L et al (2016) Mechanical, thermal, and UV-shielding behavior of silane surface modified ZnO- reinforced phthalonitrile nanocomposites. Polym Adv Technol 27:882–888. https://doi.org/10.1002/pat.3744
Abdelsalam AA, Araby S, El-Sabbagh SH et al (2021) Effect of carbon black loading on mechanical and rheological properties of natural rubber/styrene-butadiene rubber/nitrile butadiene rubber blends. J Thermoplast Compos Mater 34:490–507. https://doi.org/10.1177/0892705719844556
Abdelsalam AA, Araby S, El-Sabbagh SH et al (2021) A comparative study on mechanical and rheological properties of ternary rubber blends. Polym Polym Compos 29:15–28. https://doi.org/10.1177/0967391119897177
Roy K, Potiyaraj P (2019) Exploring the comparative effect of silane coupling agents with different functional groups on the cure, mechanical and thermal properties of nano-alumina (Al2O3)-based natural rubber (NR) compounds. Polym Bull 76:883–902. https://doi.org/10.1007/s00289-018-2422-y
Li J, Zhao X, Zhang Z et al (2020) Construction of interconnected Al2O3 doped rGO network in natural rubber nanocomposites to achieve significant thermal conductivity and mechanical strength enhancement. Compos Sci Technol 186:1–10. https://doi.org/10.1016/j.compscitech.2019.107930
Abd-El Messieh SL, Rozik NN (2011) Dielectric and morphological studies on polyester/nanosilica fume composites. J Appl Polym Sci 122:714–721. https://doi.org/10.1002/app.33868
Abd-El-Messieh SL, Eid MAM, Hussein AI (2002) Dielectric and mechanical properties of polystyrene/acrylonitrile-butadiene rubber blends. J Appl Polym Sci 86:540–552. https://doi.org/10.1002/app.10828
Johns J, Nakason C (2011) Dielectric properties of natural rubber/chitosan blends: Effects of blend ratio and compatibilization. J Non Cryst Solids 357:1816–1821
Nihmath A, Ramesan MT (2020) Development of novel elastomeric blends derived from chlorinated nitrile rubber and chlorinated ethylene propylene diene rubber. Polym Test 89:106728. https://doi.org/10.1016/j.polymertesting.2020.106728
Thongsang S, Sombatsompop N (2006) Effect of NaOH and Si69 Treatments on the Properties of Fly Ash/Natural Rubber Composites. Polym Compos 16:101–113. https://doi.org/10.1002/pc.20163
ASTM-D380 (2012) Standard Test Methods for Rubber Hose. ASTM Int West Conshohocken, PA i:1–10. https://doi.org/10.1520/D3184-07.2
ASTM D2084-1 (2012) Standard Test Method for Rubber Property — Vulcanization Using Oscillating Disk Cure. ASTM Int West Conshohocken, PA 95:1–11. https://doi.org/10.1520/D2084-07.2
ASTM D412–06 (2006) Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers–Tension. ASTM Int West Conshohocken, PA 1–14. https://doi.org/10.1520/D0412-16
ASTM D3616 − 95 (2014) Standard Test Method for Ruber-Determination of Gel, Swelling Index, and Dilute Solution Viscosity. ASTM Int West Conshohocken, PA 95:1–5. https://doi.org/10.1520/D3616-95R14
Flory PJ, Rehner J (1943) Statistical mechanics of cross-linked polymer networks II. Swelling J Chem Phys 11:521–526. https://doi.org/10.1063/1.1723792
Lorenz O, Parks CR (1961) The crosslinking efficiency of some vulcanizing agents in natural rubber. J Polym Sci 50:299–312. https://doi.org/10.1002/pol.1961.1205015404
Khalf AI, Ward AA (2010) Use of rice husks as potential filler in styrene butadiene rubber/linear low density polyethylene blends in the presence of maleic anhydride. Mater Des 31:2414–2421. https://doi.org/10.1016/j.matdes.2009.11.056
Roy K, Mandal SK, Alam MN, Debnath SC (2016) A comparison between polyethylene glycol (PEG) and polypropylene glycol (PPG) treatment on the properties of nano-titanium dioxide (TiO2) based natural rubber (NR) nanocomposites. Polym Bull 73:3065–3079. https://doi.org/10.1007/s00289-016-1641-3
Yu J, Bai H, Wang J et al (2013) Synthesis of alumina nanosheets via supercritical fluid technology with high uranyl adsorptive capacity. New J Chem 37:366–372. https://doi.org/10.1039/c2nj40514h
Bansod ND, Kapgate BP, Maji PK et al (2019) Functionalization of EPDM rubber toward better silica dispersion and reinforcement. Rubber Chem Technol 92:219–236. https://doi.org/10.5254/rct.18.81564
Anand G, Vishvanathperumal S (2022) Properties of SBR/NR Blend: The Effects of Carbon Black/Silica (CB/SiO2) Hybrid Filler and Silane Coupling Agent. SILICON 14:9051–9060. https://doi.org/10.1007/s12633-022-01675-x
Vishvanathperumal S, Anand G (2022) Effect of Nanosilica on the Mechanical Properties, Compression Set, Morphology, Abrasion and Swelling Resistance of Sulphur Cured EPDM/SBR Composites. SILICON 14:3523–3534. https://doi.org/10.1007/s12633-021-01138-9
Othman HS, El-Hashash MA, El-Sabbagh SH et al (2021) A copper-(lignin/silica/fatty acids) complex as an antioxidant/electrical conductivity agent for rubber composites (Part iii). Pigment Resin Technol 51:42–52. https://doi.org/10.1108/PRT-10-2020-0112
Hernández M, Ezquerra TA, Verdejo R, López-Manchado MA (2012) Role of vulcanizing additives on the segmental dynamics of natural rubber. Macromolecules 45:1070–1075. https://doi.org/10.1021/ma202325k
Xu T, Jia Z, Li J et al (2018) Study on the dispersion of carbon black/silica in SBR/BR composites and its properties by adding epoxidized natural rubber as a compatilizer. Polym Compos 39:377–385. https://doi.org/10.1002/pc.23946
Dialeep P, Narayanankutty SK (2020) Styrenated phenol modified nanosilica for improved thermo-oxidative and mechanical properties of natural rubber. Polym Test 82:106302. https://doi.org/10.1016/j.polymertesting.2019.106302
Xiao Y, Zou H, Zhang L et al (2020) Surface modification of silica nanoparticles by a polyoxyethylene sorbitan and silane coupling agent to prepare high-performance rubber composites. Polym Test 81:1–10. https://doi.org/10.1016/j.polymertesting.2019.106195
Rong MZ, Zhang MQ, Ruan WH (2006) Surface modification of nanoscale fillers for improving properties of polymer nanocomposites: A review. Mater Sci Technol 22:787–796. https://doi.org/10.1179/174328406X101247
Acknowledgements
The authors would like to express gratitude to the Polymers and Pigments Department at the National Research Centre in Cairo, Egypt. The authors would also like to thank the Mechanical Engineering Department at Benha Faculty of Engineering at Benha University in Benha, Egypt.
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
Amir A. Abdelsalam: Conceptualization, Investigation, Methodology, Writing – review & editing; Azza A. Ward: Methodology, Writing – original draft; Gamal Abdel-Naeem: Methodology, Writing – original draft; Wael S. Mohamed: Methodology, Writing – original draft; Salwa H. El-Sabbagh: Conceptualization, Investigation, Methodology, Writing – review & editing.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Compliance with Ethical Standards
No, all testing are conducted in this study as per ASTM standards.
Consent to Participate
The authors declare no objection of consent to participate.
Consent for Publication
The authors declare the no objection of con- sent to publication.
Research involving Human Participants and/or Animals
Not applicable.
Informed consent
Not applicable.
Conflict of Interest
The authors declare no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit. http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Abdelsalam, A.A., Ward, A.A., Abdel-Naeem, G. et al. Effect of Alumina Modified by Silane on the Mechanical, Swelling and Dielectric Properties of Al2O3/EPDM/SBR Blend Composites. Silicon 15, 3609–3621 (2023). https://doi.org/10.1007/s12633-023-02290-0
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12633-023-02290-0