The paper describes the pack siliconizing optimization procedure for AISI D2 tool steel. Pack siliconizing was performed by employing different treating temperatures (falling in the range 650–950 °C) and times (falling in the range 2–4 h). The siliconizing atmosphere was obtained through silicon (at 12 wt.%) with the addition of different percentages of NH4Cl (falling in the range 0.5–1 wt.%), Al2O3 was used as halide activator. The coatings’ phases evolution was analyzed through X-ray diffraction; the coatings’ thickness was measured through scanning electron microscopy observations of the cross section of the samples; the mechanical properties were evaluated through micro hardness measurements. The results showed that the coatings’ thickness and hardness increase as the treating time and temperature as well as the halide activator percentage increase. The coating procedure optimization was performed by employing the response surface methodology based on Box-Behnken method. The results of the optimization procedure led to the of the optimal combination of processing parameters: 1 wt.% of halide activator, 3.575 holding time, 950 °C in temperature.
Article PDF
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Avoid common mistakes on your manuscript.
Data Availability
Data available on request from the authors.
Change history
19 July 2022
Missing Open Access funding information has been added in the Funding Note.
References
Wills WH (1935) Practical observations on high-carbon high-chromium tool steels. Trans ASM 23:469
Gobbi SJ, Gobbi VJ, Reinke G, Muterlle PV, Rosa DM (2019) Ultra-low-temperature process effects on microscale abrasion of tool steel AISI D2 mater. Sci Technol 35(11):1355–1364
Khan AM, Jamil M, Ul Haq A, Hussain S, Meng L, He N (2019) Sustainable machining Modeling and optimization of temperature and surface roughness in the milling of AISI D2 steel. Ind Lubr Tribol 71(2):267–277
Bombač D, Terčelj M, Kugler G, Peruš I (2014) Amelioration of surface cracking during hot rolling of AISI D2 tool steel. Mater Sci Technol 34(14):1723–1736
Sun Y, Dong J, Zhao P, Dou B (2017) Formation and phase transformation of aluminide coating prepared by low- temperature aluminizing process. Surf Coat Technol 330:234–240
Kim H-L (2014) Effect of surface pretreatment and pack cementation on bioactivity of titanium dental implant. Surf Coat Technol 259:178–184
Juzoń P, Ziemnicka M, Chevalier S, Przybylski K, Larpin JP (2007) Improving Fe3Al alloy resistance against high temperature oxidation by pack cementation process. Appl Surf Sci 253(11):4928–4934
Xiang J, Xie F, Wu X, Yu Y (2019) Microstructure and tribological properties of Si-Y/Al two-step deposition coating prepared on Ti2AlNb based alloy by halide activated pack cementation technique. Tribol Int 136:45–57
Tsipas SA, Gordo E (2016) Molybdeno-aluminizing of powder metallurgy and wrought Ti and Ti-6Al-4V alloys by pack cementation process. Mater Charact 118:494–504
Bozza F (2014) Diffusion mechanisms and microstructure development in pack aluminizing of Ni-based alloys. Surf Coat Technol 239:147–159
Xiang ZD, Datta PK (2004) Pack aluminisation of low alloy steels at temperatures below 700 °C. Surf Coat Technol 184(1):108–115
Hosseinzadeh M, Ghasempour Mouziraji M (2016) An analysis of tube drawing process used to produce squared sections from round tubes through FE simulation and response surface methodology. Int J Adv Manuf Technol 87(5–8):2179–2194
Salehi M, Hosseinzadeh M, Elyasi M (2016) A study on optimal design of process parameters in tube drawing process of rectangular parts by combining box–behnken design of experiment, response surface methodology and artificial bee colony algorithm. Trans Indian Inst Metals 69:1223–1235
Mirshaban J, Hosseinzadeh M, Elyasi M (2018) Optimization of tube drawing process through FE analysis, intelligent computation, and experimental verification. Proc Inst Mech Eng-E: J Proc Mech Eng 232:94–107
Ghorbani H, Kim JH, Hosseinzadeh M et al (2020) Manufacturing of bent tubes with non-uniform curvature and cross-section using a novel hydroforming die: experimental, finite element analysis, and optimization. Int J Adv Manuf Technol 107:1683–1695
Cavaliere P, Perrone A, Silvello A (2016) Multi-objective optimization of steel nitriding. Eng Sci Technol 19:292–312
Najafizadeh M, Ghasempour-Mouziraji M (2021) Multi-objective optimization of process parameters in pack siliconizing on AISI D2 steel. Silicon 13:2233–2242
Cavaliere P, Zavarise G, Perillo M (2009) Modelling of the carburizing and Nitriding process. Comput Mater Sci 46(1):26–35
Chang J, Li Y, Shi H, Sun L, Cui Y (2022) Correlation between processing parameters and behavior of chromium diffusion coatings on nickel-based Superalloys: a review. In: Chinese Society of Aeronautics and Astronautics (eds) Proceedings of the 5th China Aeronautical Science and Technology Conference. Lecture Notes in Electrical Engineering, vol 821. Springer, Singapore
Pinto BA, d'Oliveira ASCM (2021) Nb silicide coatings processed by double pack cementation: formation mechanisms and stability. Surf Coat Technol 409:126913
Elhelaly MA, El-Zomor MA, Attia MS et al (2021) Characterization and kinetics of chromium carbide coatings on AISI O2 tool steel performed by pack cementation. J Mater Eng Perform. https://doi.org/10.1007/s11665-021-06211-3
Franco E, Edil da Costa C, Giubilei Milan JC, Tsipas SA, Gordo E (2020) Multi-component boron and niobium coating on M2 high speed steel processed by powder metallurgy. Surf Coat Technol 384:125306
Huang L, Wu X, Xie F, Wang S (2017) Microstructure and growth kinetics of silicide coatings for TiAl alloy. J Wuhan Univ Technol Mater Sci Ed 32(2):245–249
Najafizadeh M, Ghasempour-Mouziraji M, Zhang D (2021) Silicon diffusion in silicide coatings deposition by the pack cementation method on AISI D2 tool steel. Silicon. https://doi.org/10.1007/s12633-021-01057-9
Najafizadeh M, Ghasempour-Mouziraji M, Sadeghi B, Cavaliere P (2021) Characterization of Tribological and mechanical properties of the Si3N4 coating fabricated by duplex surface treatment of pack siliconizing and plasma Nitriding on AISI D2 tool steel. Metall Mater Trans A 52(11):4753–4766
Funding
Open access funding provided by Università del Salento within the CRUI-CARE Agreement. The authors declare that no funds, grants, or other support were received during the preparation of this manuscript.
Author information
Authors and Affiliations
Contributions
All authors contributed to the study conception and design and writing. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors have no relevant financial or non-financial interests to disclose.
Ethics Approval
Not applicable.
Consent to Participate
Not applicable.
Consent for Publication
Not applicable.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Najafizadeh, M., Hosseinzadeh, M., Ghasempour-Mouziraji, M. et al. Pack Siliconizing Optimization of AISI D2 Tool Steel. Silicon 14, 10669–10679 (2022). https://doi.org/10.1007/s12633-022-01760-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12633-022-01760-1