Synthesis and Characterization of Nano CoFe2O4 Prepared by Sol-Gel Auto-Combustion with Ultrasonic Irradiation and Evaluation of Photocatalytic Removal and Degradation Kinetic of Reactive Red 195

  • Janan Parhizkar
  • Mohammad Hossein Habibi
  • Seyed Yousef Mosavian
Original Paper
  • 19 Downloads

Abstract

A combination of sol-gel auto-combustion and ultrasonic irradiation methodswere developed for fabrication of CoFe2O4nanoparticles using aqueous solution of Co(NO3)2.6H2O and Fe(NO3)3.9H2O with glycine as chelating agent under nitrogen atmosphere. CoFe2O4 nano-particles werecoated on glass by Doctor Blade method. The precursor powders were analyzed by thermogravimetry (TG) and differential thermogravimetry (DTG). The structural, optical and the chemical features of the nano-particles have been studied by powder X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and UV–Vis diffuse reflectance spectroscopy (DRS).The results of TG-DTG indicated that the CoFe2O4nano-particles have a very good thermal stability. Powder XRD analysis confirmed formation of CoFe2O4 spinel phase. The morphological and optical properties of the cobalt ferrite were found to be depended on ultrasonic irradiation. Nanoparticles prepared with ultrasonic irradiation have diameter of about 46 nmwith spherical morphology and narrow size distribution and nanoparticles prepared without ultrasonic irradiation is about 57 nm. The photocatalytic activity of the immobilizedcobalt ferrite nanocomposite was studied on Reactive Red 195 (RR195) as an azo textile dye used textile industries and the results showed about 74% degradation in less than 2 h. The photocatalytic activity of CoFe2O4nanoparticles is attributed to band gap energy and small particle size. The coated cobalt ferrite nanocomposite with a reproducible photocatalytic activity was well separable from water media by removing the glass coated with thin film and acted as a promising catalyst for the remediation of textile wastewater. Degradation of Reactive Red 195 by cobalt ferrite nanocomposite coated on glass follows second order rate kinetic.

Keywords

CoFe2O4 Sol–Gel Kinetic Ultrasonic irradiation Optical properties Reactive Red 195 

Preview

Unable to display preview. Download preview PDF.

Unable to display preview. Download preview PDF.

Notes

Acknowledgements

The authors wish to thank the University of Isfahan for financially supporting this work.

References

  1. 1.
    Ianosn R, Bosca M, Lazau R (2014) Fine tuning of CoFe 2 O 4 properties prepared by solution combustion synthesis. Ceram Inter 40:10223–10229CrossRefGoogle Scholar
  2. 2.
    Habibi MH, Parhizkar HJ (2014) FTIR and UV–vis diffuse reflectance spectroscopy studies of the wet chemical (WC) route synthesized nano-structure CoFe 2 O 4 from CoCl 2 and FeCl 3. Spectrochim Acta A 127:102–106CrossRefGoogle Scholar
  3. 3.
    Xingbin Y, Jiangtao C, Qunji X, Philippe M (2010) Synthesis and magnetic properties of CoFe 2 O 4 nanoparticles confined within mesoporous silica. Micropor Mesopor Mat 135:137–142CrossRefGoogle Scholar
  4. 4.
    Habibi MH, Rahmati MH (2015) The effect of operational parameters on the photocatalytic degradation of Congo red organic dye using ZnO–CdS core–shell nano-structure coated on glass by Doctor Blade method. Spectrochim Acta A 137:160–164CrossRefGoogle Scholar
  5. 5.
    Jing W, Tong D, Yulong L, Caiqin Y, Wenhong Z (2008) Synthesis and characterization of CoFe 2 O 4 magnetic particles prepared by co-precipitation method: effect of mixture procedures of initial solution. J Alloys Compd 450:532–539CrossRefGoogle Scholar
  6. 6.
    Habibi MH, Rahmati MH (2014) Fabrication and characterization of ZnO@ CdS core–shell nanostructure using acetate precursors: XRD, FESEM, DRS, FTIR studies and effects of cadmium ion concentration on band gap. Spectrochim Acta A 133:13–18CrossRefGoogle Scholar
  7. 7.
    Xing-Hua L, Cai-Ling X, Xiang-Hua H, Liang Q, Tao W, Fa-Shen L (2010) Synthesis and magnetic properties of nearly monodisperse CoFe 2 O 4 nanoparticles through a simple hydrothermal condition. Nanoscale Res Lett 5:1039–1044CrossRefGoogle Scholar
  8. 8.
    Habibi MH, Rezvani Z (2014) Nanostructure copper oxocobaltate fabricated by co-precipitation route using copper and cobalt nitrate as precursors: Characterization by combined diffuse reflectance and FT infrared spectra. Spectrochim Acta A 130:309–312CrossRefGoogle Scholar
  9. 9.
    Habibi MH, Karimi B (2014) Nanostructure Cu–Zn mixed-oxide supported photocatalyst fabricated by impregnation method for the photocatalytic degradation of CI Reactive Orange 16 (V3R) in water. Spectrochim Acta A 124:629–631CrossRefGoogle Scholar
  10. 10.
    Salunkhe AB, Khot VM, Thorat ND, Phadatare MR, Satish CI, Dhawale DS, Pawar SH (2013) Polyvinyl alcohol functionalized cobalt ferrite nanoparticles for biomedical applications. Appl Surf Sci 264:598–604CrossRefGoogle Scholar
  11. 11.
    Habibi MH, Karimi B (2015) Co-precipitation synthesis of nano-composites consists of zinc and tin oxides coatings on glass with enhanced photocatalytic activity on degradation of Reactive Blue 160 KE2B. Spectrochim Acta A 137:785–789CrossRefGoogle Scholar
  12. 12.
    Chao L, Rondinone AJ, Zhang ZJ (2000) Synthesis of magnetic spinel ferrite CoFe2O4 nanoparticles from ferric salt and characterization of the size-dependent superparamagnetic properties. Pure Appl Chem 72:37–45CrossRefGoogle Scholar
  13. 13.
    Ilkhechi NN, Alijani M (2016) Optical and structural properties of TiO2 nanopowders with Co/Ce doping at various temperature. Opt Quant Electron 48:148–156CrossRefGoogle Scholar
  14. 14.
    Ilkhechi NN, Koozegar-Kaleji B (2015) Optical and structural properties of tenorite nanopowders doped by Si and Zr. Opt Quant Electron 47:633–642CrossRefGoogle Scholar
  15. 15.
    Ilkhechi NN, Koozegar-Kaleji B (2015) Optical and structural properties of tenorite nanopowders doped by Si and Zr. Opt Quant Electron 47:633–642CrossRefGoogle Scholar
  16. 16.
    Ilkhechi NN, Ahmadi A (2015) Optical and structural properties of nanocrystalline anatase powders doped by Zr, Si and Cu at high temperature. Opt Quant Electron 47:2423–2434CrossRefGoogle Scholar
  17. 17.
    Ilkhechi NN, Kaleji BK (2016) Effect of Cu2+, Si4 + and Zr4+ dopant on structural, optical and photocatalytic properties of titania nanopowders. Opt Quant Electron 48:347–355CrossRefGoogle Scholar
  18. 18.
    Ilkhechi NN, Ghobadi N (2016) Comparison of structural, optical, photocatalytic behavior and hydrophilic properties of pure and Sn/La co-doped TiO2 thin Films. J Mater Sci Mater Electron 27:12050–12059CrossRefGoogle Scholar
  19. 19.
    Ilkhechi NN, Kaleji BK (2017) Temperature stability and photocatalytic activity of nanocrystalline cristobalite powders with Cu dopant. Silicon 9:943–948CrossRefGoogle Scholar
  20. 20.
    Habibi MH, Karimi B, Zendehdel M, Habibi M (2014) Preparation of nanostructure mixed copper-zinc oxide via co-precipitation rout for dye-sensitized solar cells: the influence of blocking layer and Co (II)/Co (III) complex redox shuttle. Spectrochim Acta A 20:1462–1467Google Scholar
  21. 21.
    Unyong J, Xiaowei T, Yong W, Hong Y, Younan X (2007) Superparamagnetic colloids: controlled synthesis and niche applications. Adv Mater 19:33–60CrossRefGoogle Scholar
  22. 22.
    Habibi MH, Karimi B, Zendehdel M, Habibi M (2013) Fabrication, characterization of two nano-composite CuO–ZnO working electrodes for dye-sensitized solar cell. Spectrochim Acta A 116:374–380CrossRefGoogle Scholar
  23. 23.
    Fereydouni M, Sabbaghi1 S, Saboori R, Zeinali S (2012) Effect of polyanionic cellulose polymer nanoparticles on rheological properties of drilling mud. Int J Nanosci Nanotechnol 8:171– 174Google Scholar
  24. 24.
    Jafari V, Allahverdi A (2014) Synthesis and characterization of colloidal nanosilica via an ultrasound assisted route based on alkali leaching of silica fume. Int J Nanosci Nanotechnol 10:145–152Google Scholar
  25. 25.
    Foroutan T (2015) The effects of zinc oxide nanoparticles on differentiation of human mesenchymal stem cells to osteoblast. Nanomed J 1:308–314Google Scholar
  26. 26.
    Tohidi SH, Novinrooz AJ, Derhambakhsh M, Grigoryan GL (2012) Dependence of spectroscopic properties of copper oxide based silica supported nanostructure on temperature. Int J Nanosci Nanotechnol 8:143–148Google Scholar
  27. 27.
    Ilkhechi NN, Azar Z (2016) Enhanced structural, optical and super-hydrophilic properties of TiO2 thin film co-doped by V and Sn. J Mater Sci Mater Electron 27:10541–10549CrossRefGoogle Scholar
  28. 28.
    Ilkhechi NN, Ghorbani M (2017) The optical, photo catalytic behavior and hydrophilic properties of silver and tin co doped TiO2 thin films using sol–gel method. J Mater Sci Mater Electron 28:3571–3580CrossRefGoogle Scholar
  29. 29.
    Habibi MH, Askari E (2013) Novel nanostructure zinc zirconate, zinc oxide or zirconium oxide pastes coated on fluorine doped tin oxide thin film as photoelectrochemical working electrodes for dye-sensitized solar cell. Spectrochim Acta A 104:197–202CrossRefGoogle Scholar
  30. 30.
    Habibi MH, Sheibani R (2013) Nanostructure silver-doped zinc oxide films coating on glass prepared by sol–gel and photochemical deposition process: application for removal of mercaptan. J Ind Eng Chem 19:161–165CrossRefGoogle Scholar
  31. 31.
    Calero-DdelC VL, Rinaldi C (2007) Synthesis and magnetic characterization of cobalt-substituted ferrite (CoxFe 3- xO 4) nanoparticles. J Magn Magn Mater 314:60–67CrossRefGoogle Scholar
  32. 32.
    Suslick S (1988) Ultrasound: its chemical, physical, and biological effects. VCH Publishers K., New YorkGoogle Scholar
  33. 33.
    Silva ACA, Gratens X, Chitta VA, Franco SD, da Silva RS, Condeles JF, Dantas NO (2014) Effects of ultrasonic agitation on the structural and magnetic properties of CoFe2O4 nanocrystals. Eur J Inorg Chem, 5603–5608Google Scholar
  34. 34.
    Tedesco AC, Oliveira DM, Lacava ZGM, Azevedo RB, Lima ECD, Morais PC (2004) Investigation of the binding constant and stoichiometry of biocompatible cobalt ferrite-based magnetic fluids to serum albumin. J Magn Magn Mat 272:2404–2405CrossRefGoogle Scholar
  35. 35.
    Song O, Zhang ZJ (2004) Shape control and associated magnetic properties of spinel cobalt ferrite nanocrystals. J Am Chem Soc 126:6164–6168CrossRefPubMedGoogle Scholar
  36. 36.
    Ayyappan S, Mahadevan S, Chandramohan P, Srinivasan MP, Philip J, Raj B (2010) Influence of Co2 + ion concentration on the size, magnetic properties, and purity of CoFe2O4 spinel ferrite nanoparticles. J Phys Chem C 114:6334–6341CrossRefGoogle Scholar
  37. 37.
    Peddis D, Mansilla MV, Morup S, Cannas C, Musinu A, Piccaluga G, DOrazio F, Lucari F, Fiorani D (2008) Spin-canting and magnetic anisotropy in ultrasmall CoFe2O4 nanoparticles. J Phys Chem B 112:8507–8513CrossRefPubMedGoogle Scholar
  38. 38.
    Banerjee Y, Katsenovich L, Lagos M, McIintosh X, Zhang C, Li Z (2010) Nanomedicine: magnetic nanoparticles and their biomedical applications. Curr Med Chem 17:3120–3141CrossRefPubMedGoogle Scholar
  39. 39.
    Zhao LJ, Zhang HJ, Xing Y, Song SY, Yu SY, Shi WD, Guo XM, Yang JH, Lei YQ, Cao F (2008) Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method. J Solid State Chem 181:245–252CrossRefGoogle Scholar
  40. 40.
    Meron T, Rosenberg Y, Lereah Y, Markovich G (2005) Synthesis and assembly of high-quality cobalt ferrite nanocrystals prepared by a modified sol–gel technique. J Magn Magn Mater 292:11– 16CrossRefGoogle Scholar
  41. 41.
    Rana S, Philip J, Raj B (2010) Micelle based synthesis of cobalt ferrite nanoparticles and its characterization using Fourier transform infrared transmission spectrometry and thermogravimetry. Mater Chem Phys 124:264–269CrossRefGoogle Scholar
  42. 42.
    Coker VS, Telling ND, van der Laan G, Pattrick RAD, Pearce CI, Arenholz E, Tuna F, Winpenny REP, Lloyd JR (2009) Harnessing the extracellular bacterial production of nanoscale cobalt ferrite with exploitable magnetic properties. Acs Nano 3:1922–1928CrossRefPubMedGoogle Scholar
  43. 43.
    Ayyappan J, Raj BP (2008) Effect of digestion time on size and magnetic properties of spinel CoFe2O4 nanoparticles. J Phys Chem C 113:590–596CrossRefGoogle Scholar
  44. 44.
    Briceno S, Bramer-Escamilla W, Silva P, Delgado GE, Plaza E, Palacios J, Canizales E (2012) Effects of synthesis variables on the magnetic properties of CoFe 2 O 4 nanoparticles. J Magn Magn Mater 324:2926–2931CrossRefGoogle Scholar
  45. 45.
    Soler MAG, Lima ECD, da Silva SW, Melo TFO, Pimenta ACM, Sinnecker JP, Azevedo RB, Garg VK (2014) Effects of ultrasonic agitation on the structural and magnetic properties of CoFe2O4 nanocrystals. Eur J Inorg Chem, pp 5603–5608Google Scholar
  46. 46.
    Ahmed AS, Shafeeq MM, Singla ML, Tabassum S, Naqvi AH, Azam A (2010) Band gap narrowing and fluorescence properties of nickel doped SnO 2 nanoparticles. J Lumin 131:1–6CrossRefGoogle Scholar
  47. 47.
    Shoeb M, Singh BR, Khan JA, Khan W, Singh BN, Singh HB, Naqvi AH (2013) ROS-dependent anticandidal activity of zinc oxide nanoparticles synthesized by using egg albumen as a biotemplate. Adv Nat Sci: Nanosci Nanotechnol 4:035015Google Scholar
  48. 48.
    Nouroozi F, Farzaneh F (2011) Synthesis and characterization of brush-like ZnOnanorods using albumen as biotemplate. J Braz Chem Soc 22(3):484–488CrossRefGoogle Scholar
  49. 49.
    Tauc J (1974) Optical properties of amorphous semiconductors, amorphous and liquid semiconductors. Plenum Press, New York, p 171CrossRefGoogle Scholar
  50. 50.
    Ansari SA, Nisar A, Fatma B, Khan W, Naqvi AH (2012) Investigation on structural, optical and dielectric properties of Co doped ZnO nanoparticles synthesized by gel-combustion route. Mater Sci Eng B 177:428–435CrossRefGoogle Scholar
  51. 51.
    Zhong M, Fei P, Fu X, Lei Z, Su B (2013) Synthesis of PS–CoFe2O4 composite nanomaterial with improved magnetic properties by a one-step solvothermal method. Ind Eng Chem Res 52:8230–8235CrossRefGoogle Scholar
  52. 52.
    Jiang W, Qiu Z, Yao W, Zhu Y, Cui W (2017) TiO 2/Al (H 2 PO4) 3 composite film as separation-free and washing-resistance photocatalyst. Appl Catal B 204:43–48CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media B.V., part of Springer Nature 2018

Authors and Affiliations

  • Janan Parhizkar
    • 1
  • Mohammad Hossein Habibi
    • 1
  • Seyed Yousef Mosavian
    • 2
  1. 1.Nanotechnology Laboratory, Department of ChemistryUniversity of IsfahanIsfahanIran
  2. 2.Department of MaterialIslamic Azad UniversityNajafabadIran

Personalised recommendations