Abstract
Si3N4 powders were synthesized by a carbothermal reduction method using a SiO2 + C combustion synthesis precursor derived from a mixed solution consisting of silicic acid (Si source), polyacrylamide (additive), nitric acid (oxidizer), urea (fuel), and glucose (C source). Scanning electron microscopy (SEM) micrographs showed that the obtained precursor exhibited a uniform mixture of SiO2 + C composed of porous blocky particles up to ∼20 μm. The precursor was subsequently calcined under nitrogen at 1200–1550°C for 2 h. X-ray diffraction (XRD) analysis revealed that the initial reduction reaction started at about 1300°C, and the complete transition of SiO2 into Si3N4 was found at 1550°C. The Si3N4 powders, synthesized at 1550°C, exhibit a mixture phase of α- and β-Si3N4 and consist of mainly agglomerates of fine particles of 100–300 nm, needle-like crystals and whiskers with a diameter of about 100 nm and a length up to several micrometers, and a minor amount of irregular-shaped growths.
Similar content being viewed by others
References
F.L. Riley, Silicon nitride and related materials, J. Am. Ceram. Soc., 83(2000), No. 2, p. 245.
C. Methivier, J. Massardier, and J.C. Bertolini, Pd/Si3N4 catalysts: preparation, characterization and catalytic activity for the methane oxidation, Appl. Catal. A, 182(1999), No. 2, p. 337.
T. Yamada, Preparation and evaluation of sinterable silicon nitride powder by imide decomposition method, Am. Ceram. Soc. Bull., 72(1993), No. 5, p. 99.
R. Reidel and W. Dressler, Chemical formation of ceramics, Ceram. Int., 22(1996), No. 3, p. 233.
W.R. Cannon, S.C. Danforth, J.H. Flint, J.S. Haggerty, and R.A. Marra, Sinterable ceramic powders from laser-driven reactions: I. Process description and modeling, J. Am. Ceram. Soc., 65(1982), No. 7, p. 324.
Ž.G. Kostić, P.L. Stefanović, and P.B. Pavlović, Ther modynamic consideration of Si-N and Si-H-N systems for silicon nitride powder production in thermal plasma, Ceram. Int., 22(1996), No. 3, p. 179.
I.G. Cano and M.A. Rodríguez, Synthesis of β-silicon nitride by SHS: fiber growth, Scripta Mater., 50(2004), No. 3, p. 383.
A.D. Pablos, J. Bermudo, and M.I. Osendi, Microstructure and mechanical properties of silicon nitride materials fabricated from SHS powders, J. Am. Ceram. Soc., 84(2001), No. 5, p. 1033.
C.L. Guo, Z. Xing, X.J. Ma, L.Q. Xu, and Y.T. Qian, Solvothermal synthesis of Si3N4 nanomaterials at a low temperature, J. Am. Ceram. Soc., 91(2008), No. 5, p. 1725.
X.C. Wu, W.H. Song, B. Zhao, W.D. Huang, M.H. Pu, Y.P. Sun, and J.J. Du, Synthesis of coaxial nanowires of silicon nitride sheathed with silicon and silicon oxide, Solid State Commun., 115(2000), No. 12, p. 683.
J.F. Yang, S.Y. Shan, R. Janssen, G. Schneider, T. Ohji, and S. Kanzaki, Synthesis of fibrous β-Si3N4 structured porous ceramics using carbothermal nitridation of silica, Acta Mater., 53(2005), No. 10, p. 2981.
S.C. Zhang and W.R. Cannon, Preparation of silicon nitride from silica, J. Am. Ceram. Soc., 67(1984), No. 10, p. 691.
R. Koc and S. Kaza, Synthesis of α-Si3N4 from carbon coated silica by carbothermal reduction and nitridation, J. Eur. Ceram. Soc., 18(1998), No. 10, p. 1471.
S.L. Chung and C.W. Chang, Carbothermal reduction and nitridation synthesis of silicon nitride by using solution combustion synthesized precursors, J. Mater. Sci., 44(2009), No. 14, p. 3784.
M.V. Vlasova, T.S. Bartnitskaya, L.L. Sukhikh, L.A. Krushinskaya, T.V. Tomila, and S.Y. Artyuch, Mechanism of Si3N4 nucleation during carbothermal reduction of silica, J. Mater. Sci., 30(1995), No. 20, p. 5263.
A.O. Kurt and T.J. Davies, Synthesis of Si3N4 using sepiolite and various sources of carbon, J. Mater. Sci., 36(2001), No. 24, p. 5895.
J.J. Kingsley and K.C. Patil, A novel combustion process for the synthesis of fine particle α-alumina and related materials, Mater. Lett., 6(1988), No. 11-12, p. 427.
J.C. Kuang, C.R. Zhang, X.G. Zhou, and S.Q. Wang, Influence of processing parameters on synthesis of nano-sized AlN powders, J. Cryst. Growth, 263(2004), No. 1–2, p. 12.
M.L. Qin, X.L. Du, Z.X. Li, I.S. Humail, and X.H. Qu, Synthesis of aluminum nitride powders by carbothermal reduction of a combustion synthesis precursor, Mater. Res. Bull., 43(2008), No. 11, p. 2954.
S. Moalla, R. Kalfat, A.P. Legrand, and H. Zarrouk, Polysiloxane-diamine modified gel as precursor to crystalline/ amorphous Si3N4, J. Sol Gel Sci. Technol., 26(2003), No. 1–3, p. 125.
K. Sujirote and P. Leangsuwan, Silicon carbide formation from pretreated rice husks, J. Mater. Sci., 38(2003), No. 23, p. 4739.
M. Sitarz, M. Handke, and W. Mozgawa, Identification of silicooxygen rings in SiO2 based on IR spectra, Spectr. Acta Part A, 56(2000), No. 9, p. 1819.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Chu, Am., Qin, Ml., Jia, Br. et al. Carbothermal synthesis of Si3N4 powders using a combustion synthesis precursor. Int J Miner Metall Mater 20, 76–81 (2013). https://doi.org/10.1007/s12613-013-0696-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12613-013-0696-5