Thermoelectric performance of p-type zone-melted Se-doped Bi0.5Sb1.5Te3 alloys
- 46 Downloads
For zone-melted (ZM) bismuth telluride-based alloys, which are widely commercially available for solid-state cooling and low-temperature power generation around room temperature, introducing point defects is the chief approach to improve their thermoelectric performance. Herein, we report the multiple effects of Se doping on thermoelectric performance of p-type Bi0.5Sb1.5Te3-xSe x + 3 wt% Te ZM ingots, which increases carrier concentration, reduces lattice thermal conductivity and deteriorates the carrier mobility. As a result, the peak figure of merit (ZT) is shifted to a higher temperature and a high ZT ~ 1.2 at 350 K is obtained, due to the reduced thermal conductivity and suppressed intrinsic conduction. Further, decreasing Sb content is followed to optimize the room temperature performance and a ZT ~ 1.1 at 300 K is obtained. These results are significant for designing and optimizing the thermoelectric performance of commercial Bi0.5Sb1.5Te3+ 3 wt% Te ZM alloys.
KeywordsThermoelectric materials Bismuth telluride Zone melting Se doping Bi0.5Sb1.5Te3
This work was supported by the National Natural Science Foundation of China (Nos. 61534001 and 11574267) and the National Science Fund for Distinguished Young Scholars (No.51725102).
- Lošt’ák P, Drašar Č, Bachan D, Beneš L, Krejčová A. Defects in Bi2Te3−xSex single crystals. Radiat Eff Defect. S. 2010;165(3):211.Google Scholar