Effect of foaming temperature on the mechanical properties of produced closed-cell A356Aluminum foams with melting method

  • Published:
Metals and Materials International Aims and scope Submit manuscript

Abstract

In this study an attempt was carried out to determine the effect of production temperature on the mechanical properties and energy absorption behavior of closed-cell A356 alloy foams under uniaxial compression test. For this purpose, three different A356 alloy closed-cell foams were synthesized at three different casting temperatures, 650 °C, 675 °C and 700 °C by adding the same amounts of granulated calcium as thickening and TiH2 as blowing agent. The samples were characterized by SEM to study the pore morphology at different foaming temperatures. Compression tests of the A356 foams were carried out to assess their mechanical properties and energy absorption behavior. The results indicated that increasing the foaming temperature from 650 °C to 675 °C and 700 °C reduces the relative density of closed cell A356 alloys by 18.3% and 38% respectively and consequently affects the compressive strength and energy absorption of cellular structures by changing them from equiaxed polyhedral closed cells to distorted cells. Also at 700 °C foaming temperature, growth of micro-pores and coalescence with other surrounding pores leads to several big voids.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Similar content being viewed by others

References

  1. HP. Degischer and B. Kriszt, Handbook of Cellular Metals Production, Processing, Applications.1st Ed. WILEY-VCH Verlag GmbH, Germany (2002).

    Book  Google Scholar 

  2. W. Deqing, M. Xiangjun, X. Weiwei, and S. Ziyuan, Mater. Sci.Eng. A. 420, 235 (2006).

    Article  Google Scholar 

  3. R. E. Raj and B. S. S. Daniel, Int. J. Adv. Manuf. Tech. 38, 605 (2008).

    Article  Google Scholar 

  4. L. A. Bin, Y.X. Hong, G. Lin, L. B.-ling, T. Z.-Bin, and R. Wei, Trans Nonferr. Met. Soc. China. 22, S33 (2012).

    Article  Google Scholar 

  5. X. Q. Cao, Z. H. Wang, H. W. Ma, L. M. Zhao, and G. T. Yang, Trans. Nonferr. Met. Soc. China. 16, 351 (2006).

    Article  Google Scholar 

  6. F. Han, J. Wei, H. Cheng, and J. Gao, J. Mater. Process. Technol. 138, 505 (2003).

    Article  Google Scholar 

  7. J. Banhart, Prog. Mater. Sci. 45, 559 (2001).

    Article  Google Scholar 

  8. C. C Yang and H. Nakae, J. Alloy. Compd. 313, 188 (2000).

    Article  Google Scholar 

  9. G. Zu and G. Yao, J. Mater. Eng. Perform. 21, 985 (2011).

    Google Scholar 

  10. M. Malekjafarian and S. K. Sadrnezhaad, Mater. Des. 42, 8 (2012).

    Article  Google Scholar 

  11. C. Korner, Integral Foam Molding of Light Metals. 1st Ed. Springer, Germany (2008).

    Google Scholar 

  12. W. Deqing and S. Ziyuan, Mater. Sci. Eng. A. 361, 45 (2003).

    Article  Google Scholar 

  13. E. E. Michaelides, Particles, Bubbles and Drops Their Motion, Heatand Mass Transfer, World Scientific Publishing Co. Pte. Ltd. (2006).

    Book  Google Scholar 

  14. E. Ricci, D. Giuranno, and N. Sobczak, J. Mater. Eng. Perform. 22, 3381 (2013).

    Article  Google Scholar 

  15. M. F. Ashby, A. Evans, N. A. Fleck, L. J. Gibson, J. W. Hutchinson, H. N. G. Wadley, and F. Delale, Metal Foams: A Design Guide. Butterworth-Heinemann, USA (2000).

    Google Scholar 

  16. R. Sriram, U. K. Vaidya, and J. E. Kim, J. Mater. Sci. 41, 4023 (2006).

    Article  Google Scholar 

  17. H. Bafti and A. Habibolahzadeh, Mater. Des. 52, 404 (2013).

    Article  Google Scholar 

  18. E. Andrews, W. Sanders, and L. J. Gibson, Mater. Sci. Eng. A 270, 113 (1999).

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to N. Movahedi.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Movahedi, N., Mirbagheri, S.M.H. & Hoseini, S.R. Effect of foaming temperature on the mechanical properties of produced closed-cell A356Aluminum foams with melting method. Met. Mater. Int. 20, 757–763 (2014). https://doi.org/10.1007/s12540-014-4021-2

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12540-014-4021-2

Keywords

Navigation