Abstract
The effect of the High Temperature Gas Nitriding (HTGN) and tempering treatment of 17Cr-1Ni-0.5C-0.8Mo (CNMo) steel was experimentally investigated. The HTGN was carried out at 1050 °C for 1 h in a gaseous atmosphere containing 98.07 kPa of nitrogen. Chromium nitrides in the austenite and martensite phase appeared at the nitrogen-permeated surface layer after the HTGN treatment. The hardness of the outmost surface of the HTGN treated specimen measured 708 Hv. When it was tempered at 500 °C for 1 h, the hardness of the outmost surface was 763 Hv as a result of the precipitation of mostly micro Cr2N, which was densely packed with a small amount of Cr23C6 and the secondary hardening effect. In addition, an improvement in the corrosion resistance was observed in the tempered specimen.
Similar content being viewed by others
References
M. L. G. Byrnes, M. Grujicic, and W.S. Owen, Acta metall 35, 1853 (1987).
E. Werner, Mater. Sci. Eng. A 101, 93 (1988).
Valentin G. Gavriljuk, Scripta mater. 52, 951 (2005).
M. O. Speidel and R. M. Pedrazzoli, Mater. Perform. 31, 59 (1992).
P. W. Kroger, U.S. Patent 3, 791, 876.
D. K. Yoo, D. W. Joo, Insoo Kim, C. Y. Kang, and J. H. Sung, J. of the Korean Society for Heat Treatment 15, 57 (2002).
R. R. Winston and H. H. Uhlig, Uhlig’s Corrosion Handbook, 2 nd ed., John Wiley (2000).
W. J. Kaluba, T. Kaluba, and R. Taillard, The Austenizing Behaviour of High-Nitrogen Martensitic Stainless Steels, Scripta mater. 41, 1289 (1999).
H. Leda, J. Mater. Process. Tech. 53, 263–272 (1995).
R. Devaux, D. Vouagner, A. M. De Becdelievre, and C. Duret-Thual, Corros. Sci. 36, 171 (1994).
C. R. Clayton and Y. C. Lu, J. Electrochem. Soc. 133 (1986).
C. O. Olsson, Corros. Sci. 37, 467 (1995).
R. Qvarfort, Corros. Sci. 40, 215 (1998).
T. R. Beck, Corrosion 30, 408 (1974).
J. C. Scully, Corro. Sci. 15, 207 (1975).
J. H. Sung, J. H. Kong, D. K. Yoo, H. Y. On, D. J. Lee, and H. W. Lee, Mater. Sci. Eng. A 489, 38 (2008).
D. K. Yoo and J. H. Sung, J. of the Korean Society for Heat Treatment 19, 3 (2006).
V. G. Garvriljuk and H. Berns, High Nitrogen steels, 1 st ed., p. 215, spring (1999).
D. K. Yoo and J. H. Sung, J. of the Korean Society for Heat Treatment 13, 83 (2006).
D. K. Yoo, H. J. Lee, C. Y. Kang, K. H. Kim, Y. H. Kim, and J. H. Sung, Solid State Phenomena 118, 149 (2006).
E. Folkhard, Welding Metallurgy of Stainless Steels, 1 st ed., p. 103, Springer, New York (1986).
F. B. Pickering, Physical Metallurgy and the Design of steels, Applied Science Publishers (1978).
O. Bletton, Stainless Steels Proceedings of the 1989 Spring School Organization, p. 477–546, France (1993).
H. Berns, Steel Research 63, 8 (1992).
H. Hanninen, Mater. Sci. Forum, 318 (1999).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kong, J.H., Lee, D.J., On, H.Y. et al. The characteristics of high temperature Gas Nitriding heat treatment and tempering in 0.8Mo added 17Cr-1Ni-0.5C. Met. Mater. Int. 15, 179–185 (2009). https://doi.org/10.1007/s12540-009-0179-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-009-0179-4