Abstract
Beta-SiC powder samples containing 1 wt.% α-SiC as a seed and 10 vol.% AlN-Sc2O3 as a sintering additive were hot-pressed at 1900 °C for 1 h and subsequently annealed at 2000 °C for 1 h, 3 h and 6 h. When the annealing time was increased, the microstructure changed from equiaxed to elongated grains, which resulted in a self-reinforced microstructure consisting of elongated grains (hexagonal platelet grains in 3-dimensions). The development of a self-reinforced microstructure resulted in significant improvement in toughness. However, the improved toughness was offset by a reduction in strength. The typical fracture toughness and strength of the ceramics annealed for 6 h were 7.3 MPa·m1/2 and ∼500 MPa, respectively.
Similar content being viewed by others
References
K. Biswas, G. Rixecker, and F. Aldinger, Mater. Sci. Eng. A. 374, 56 (2004).
Y.-W. Kim, Y. S. Chun, T. Nishimura, M. Mitomo, and Y. H. Lee, Acta mater. 55, 727 (2007).
Y.-W. Kim, Y. S. Chun, J. Y. Park, W. S. Ryu, and D. S. Park, Met. Mater. Int. 13, 197 (2007).
M. Nader, F. Aldinger, and M.-J. Hoffmann, J. Mater. Sci. 34, 1197 (1999).
Y.-W. Kim, M. Mitomo, H. Emoto, and J. G. Lee, J. Am. Ceram. Soc. 81, 3136 (1998).
M. D. Sacks, G. W. Scheiffele, and G. A. Staab, J. Am. Ceram. Soc. 79, 1611 (1996).
Y.-W. Kim, M. Mitomo, and H. Hirotsuru, J. Am. Ceram. Soc. 80, 99 (1997).
K. Strecker, S. Ribeiro, R. Oberacker, and M.-J. Hoffmann, Int. J. Ref. Mat. Hard Mater. 22, 169 (2004).
V. A. Izhevskyi, A. H. A. Bressiani, and J. C. Bressiani, J. Am. Ceram. Soc. 88, 1115 (2005).
D. I. Cheong, J. Kim, and S. J. L. Kang, J. Europ. Ceram. Soc. 22, 1321 (2002).
A. Can, M. Herrmann, D. S. McLachlan, I. Sigalas, and J. Adler, J. Europ. Ceram. Soc. 26, 1707 (2006).
Z. Chen, J. Am. Ceram. Soc. 79, 530 (1996).
Y.-W. Kim, M. Mitomo, and T. Nishimura, J. Am. Ceram. Soc. 84, 2060 (2001).
K. Biswas, G. Rixecker, and F. Aldinger, J. Europ. Ceram. Soc. 23, 1099 (2003).
Y.-W. Kim, S. H. Lee, T. Nishimura, and M. Mitomo, Acta mater. 53, 4701 (2005).
D. Foster and D. P. Thompson, J. Europ. Ceram. Soc. 19, 2823 (1999).
S. Tabata, Y. Hirata, S. Sameshima, N. Matsunaga, and K. Ijichi, J. Ceram. Soc. Jpn. 114, 247 (2006).
S. K. Lee, K. Ando, and Y.-W. Kim, J. Am. Ceram. Soc. 88, 3478 (2005).
G. R. Anstis, P. Chantikul, B. R. Lawn, and D. B. Marshall, J. Am. Ceram. Soc. 64, 533 (1981).
E. J. Winn and W. J. Clegg, J. Am. Ceram. Soc. 82, 3466 (1999).
N. A. Toropov and V. A. Vasil’eva, Russ. J. Inorg. Chem. 7, 1001 (1962).
J. Y. Kim, Y.-W. Kim, J. G. Lee, and K. S. Cho, J. Mater. Sci. 34, 2325 (1999).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ko, SI., Lee, SJ., Roh, MH. et al. Effect of annealing on mechanical properties of silicon carbide sintered with aluminum nitride and scandium oxide. Met. Mater. Int. 15, 149–153 (2009). https://doi.org/10.1007/s12540-009-0149-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12540-009-0149-x