Mold filling simulation and experimental investigation of metallic feedstock used in low-pressure powder injection molding

  • Original Research
  • Published:
International Journal of Material Forming Aims and scope Submit manuscript

Abstract

The mold filling stage of the low-pressure powder injection molding process was simulated numerically and validated by experimental injections. For this, a feedstock formulated from a 17-4PH stainless steel powder (60 vol.%) and a wax-based binder system (40 vol.%) was used. The feedstock was characterized to obtain its thermal properties and rheological profiles at different temperatures. These were then implemented into the Autodesk Moldflow Synergy 2019 package, the numerical tool used for the simulation. The numerical results, including those pertaining to the injected length, the melt front velocity, and the pressure, were validated using a laboratory experiment set-up made of an injection press and two instrumented molds. The injected lengths predicted by the simulation were similar to the experimental short-shot results, with a relative difference below 0.5%. Since the injections were performed at constant volumetric flow, the injected length was not influenced by the feedstock temperature, but only by the shape of the mold cavity. Numerical and experimental results for the pressure were also compared. The agreement between the was good except at the end of the injection process. It is conjectured that the disagreement observed might be due to a difference in boundary conditions. The physical mold not being “air-tight” as the numerical one, an excess pressure could have been present in the latter. As a final note, this interesting simulation capability to predict the injection pressure experienced by a low-pressure (metallic or ceramic) powder injection molding feedstock was, to the best of the authors’ knowledge, for the first time, validated experimentally in this study using a low-pressure sensor placed in the mold during real-scale LPIM injections.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

Similar content being viewed by others

References

  1. Heaney D (2012) Handbook of metal injection molding. Woodhead Publishing

  2. German RM, Bose A (1997) Injection molding of metals and ceramics. Metal Powder Industries Federation, Princeton

    Google Scholar 

  3. Rei M, Milke E, Gomes R, Schaeffer L, Souza J (2002) Low-pressure injection molding processing of a 316-L stainless steel feedstock. Mater Lett 52(4–5):360–365

    Article  Google Scholar 

  4. Costa C, Michels A, Kipper M (2018) Welding lines formation in holes obtained by low pressure injection molding of ceramic parts. Cerâmica 64(369):97–103

    Article  Google Scholar 

  5. Medvedovski E, Peltsman M (2013) Low pressure injection molding of advanced ceramic components with complex shapes for mass production. Advanced Processing and Manufacturing Technologies for Structural and Multifunctional Materials VI- 36th International Conference on Advanced Ceramics and Composites, ICACC 2012, January 22–27, 2012, American Ceramic Society, Daytona Beach, FL, United states:35–51

  6. Mangels JA (1994) Low-pressure injection molding. Am Ceram Soc Bull 73:37–41

    Google Scholar 

  7. Zorzi JE, Perottoni CA, Da Jornada JAH (2003) Wax-based binder for low-pressure injection molding and the robust production of ceramic parts. Ind Ceram 23:47–49

    Google Scholar 

  8. Hidalgo J, Abajo C, Jimenez-Morales A, Torralba JM (2013) Effect of a binder system on the low-pressure powder injection moulding of water-soluble zircon feedstocks. J Eur Ceram Soc 33(15-16):3185–3194

    Article  Google Scholar 

  9. Hausnerova B, Kasparkova V, Hnatkova E (2016) Rheological and thermal performance of newly developed binder Systems for Ceramic Injection Molding, VIII international conference on "times of polymers and composites": from aerospace to nanotechnology. American Institute of Physics, USA: 020120–020124

  10. Goncalves AC (2001) Metallic powder injection molding using low pressure. J Mater Process Technol 118(1-3):193–198

    Article  Google Scholar 

  11. Julien B, Després M (2006) Metal injection Moulding: a near net shape fabrication method for the manufacture of turbine engine component, cost effective manufacture via net shape processing, research and technology organisation (NATO). Amsterdam, Netherlands: 8.1–8.16

  12. Nor NHM, Muhamad N, Jamaludin KR, Ahmad S, Ibrahim MHI (2011) Characterisation of titanium alloy feedstock for metal injection Moulding using palm stearin binder system. Adv Mater Res 264-265(1):586–591

    Google Scholar 

  13. Aslam M, Ahmad F, Yusoff P S M B M, Altaf K, Omar M A, Abdul Khalil H P S (2016) Raza M.R., Investigation of Rheological Behavior of Low Pressure Injection Molded Stainless Steel Feedstocks. Adv Mater Sci Eng 2016

  14. Fareh F, Demers V, Demarquette NR, Turenne S, Scalzo O (2017) Influence of segregation on rheological properties of wax-based feedstocks. Powder Technol 320:273–284

    Article  Google Scholar 

  15. Zhang Y, Basso A, Christensen SE, Pedersen DB, Staal L, Valler P, Hansen HN (2020) Characterization of near-zero pressure powder injection moulding with sacrificial mould by using fingerprint geometries. CIRP Ann 69(1):185–188

    Article  Google Scholar 

  16. Thornagel M (2010) Simulating flow can help avoid mould mistakes. Met Powder Rep 65(3):26–29

    Article  Google Scholar 

  17. Ilinca F, Hétu JF, Derdouri A, Stevenson J (2002) Metal injection molding: 3D modeling of nonisothermal filling. Polym Eng Sci 42(4):760–770

    Article  Google Scholar 

  18. Ilinca F, Hetu J-F, Derdouri A, Stevenson J (2002) Three-dimensional filling and post-filling simulation of metal injection molding. J Inject Molding Technol 6(4):229

    Google Scholar 

  19. Ahn S, Chung S, Atre S, Park S, German R (2008) Integrated filling, packing and cooling CAE analysis of powder injection moulding parts. Powder Metall 51(4):318–326

    Article  Google Scholar 

  20. Tseng H-C, Chang Y-J, Tien C-H, Hsu C-H (2014) Prediction of powder concentration for filling simulation of metal injection molding. In: SPE Annual Tech meeting

  21. Zheng Z-X, Wei X, Zhou Z-Y, Zhu Q-L (2008) Numerical simulation of tungsten alloy in powder injection molding process. Trans Nonferrous Met Soc 18(5):1209–1215

    Article  Google Scholar 

  22. Bilovol V, Kowalski L, Duszczyk J, Katgerman L (2003) Comparison of numerical codes for simulation of powder injection moulding. Powder Metall 46(1):55–60

    Article  Google Scholar 

  23. Bilovol V, Kowalski L, Duszczyk J, Katgerman L (2006) The effect of constitutive description of PIM feedstock viscosity in numerical analysis of the powder injection moulding process. J Mater Process Technol 178(1–3):194–199

    Article  Google Scholar 

  24. Sardarian M, Mirzaee O, Habibolahzadeh A (2017) Influence of injection temperature and pressure on the properties of alumina parts fabricated by low pressure injection molding (LPIM). Ceram Int 43(6):4785–4793

    Article  Google Scholar 

  25. Sardarian M, Mirzaee O, Habibolahzadeh A (2017) Mold filling simulation of low pressure injection molding (LPIM) of alumina: effect of temperature and pressure. Ceram Int 43(1):28–34

    Article  Google Scholar 

  26. Sardarian M, Mirzaee O, Habibolahzadeh A (2017) Numerical simulation and experimental investigation on jetting phenomenon in low pressure injection molding (LPIM) of alumina. J Mater Process Technol 243:374–380

    Article  Google Scholar 

  27. Ben Trad MA, Demers V, Côté R, Sardarian M, Dufresne L (2020) Numerical simulation and experimental investigation of mold filling and segregation in low-pressure powder injection molding of metallic feedstock. Adv Powder Technol 31(3):1349–1358

    Article  Google Scholar 

  28. Zhang MM, Lin B Simulation of ceramic injection molding for zirconia optical ferrule. Key Eng Mater 336–338:997–1000

  29. Jiang B-Y, Wang L, Xie L, Huang B-Y (2005) Viscosity model parameters fitting of feedstock in MIM simulation and analysis. Chin J Nonferrous Met 15(3):429–434

    Google Scholar 

  30. Binet C, Heaney D, Spina R, Tricarico L (2005) Experimental and numerical analysis of metal injection molded products. J Mater Process Technol 164:1160–1166

    Article  Google Scholar 

  31. Koszkul J, Nabialek J (2004) Viscosity models in simulation of the filling stage of the injection molding process. J Mater Process Technol 157(158):183–187

    Article  Google Scholar 

  32. Wang W, Li X, Han X (2012) Numerical simulation and experimental verification of the filling stage in injection molding. Polym Eng Sci 52(1):42–51

    Article  Google Scholar 

  33. Leverkoehne M, Coronel-Hernandez J, Dirscherl R, Gorlov I, Janssen R, Claussen N (2001) Novel binder system based on paraffin-wax for low-pressure injection molding of metal-ceramic powder mixtures. Adv Eng Mater 3(12):995

    Article  Google Scholar 

  34. Majewska-Glabus I, Zhuang L, Vetter R, Duszczyk J (1995) Thermal debinding of Fe 3 Al-X metal powder compacts. J Mater Sci 30(24):6209–6217

    Article  Google Scholar 

  35. Y-m L, Liu X-Q, Luo F-h, Yue J-L (2007) Effects of surfactant on properties of MIM feedstock. Trans Nonferrous Met Soc 17(1):1–8

    Article  Google Scholar 

  36. ASTM-B923–16 (2016) Standard test method for metal powder skeletal density by helium or nitrogen Pycnometry. ASTM International, West Conshohocken, PA

  37. ASTM-D3418–15 (2015) Standard test method for transition temperatures and enthalpies of fusion and crystallization of polymers by differential scanning Calorimetry. ASTM International, West Conshohocken, PA

  38. ASTM-E1269–11 (2018) Standard test method for determining specific heat capacity by differential scanning Calorimetry. ASTM International. West Conshohocken, PA

  39. Borup KA, de Boor J, Wang H, Drymiotis F, Gascoin F, Shi X, Chen L, Fedorov MI, Müller E, Iversen BB, Snyder GJ (2015) Measuring thermoelectric transport properties of materials. Energy Environ Sci 8(2):423–435

    Article  Google Scholar 

  40. Xie P, Guo F, Jiao Z, Ding Y, Yang W (2014) Effect of gate size on the melt filling behavior and residual stress of injection molded parts. Mater Des 53:366–372

    Article  Google Scholar 

  41. Bosioc A, Susan-Resiga R, Muntean S (2008) Design and manufacturing of a convergent-divergent test section for swirling flow apparatus. In: proceedings of the 4th German–Romanian workshop on Turbomachinery hydrodynamics (GRoWTH)

Download references

Acknowledgments

Special thanks to Mr. Sarthak Kapoor for his cooperation and help with the experiments in this research.

Author information

Authors and Affiliations

  1. École de technologie supérieure, 1100 Notre-Dame West, Montreal, QC, H3C 1K3, Canada

    Mohamed Azzouni, Vincent Demers & Louis Dufresne

Authors
  1. Mohamed Azzouni
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Vincent Demers
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Louis Dufresne
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Vincent Demers.

Ethics declarations

This work was carried out with the financial support of the Mitacs Globalink Graduate Fellowship and the Natural Science and Engineering Research Council (NSERC, Grant RGPIN-2018-04407).

Conflict of interest

The authors declare that they have no conflict of interest.

Additional information

Publisher’s note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Azzouni, M., Demers, V. & Dufresne, L. Mold filling simulation and experimental investigation of metallic feedstock used in low-pressure powder injection molding. Int J Mater Form 14, 961–972 (2021). https://doi.org/10.1007/s12289-021-01612-0

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12289-021-01612-0

Keywords

Search

Navigation