Orthogonal experimental design applied for wear characterization of aluminum/Csf metal composite fabricated by the thixomixing method

  • Original Research
  • Published:
International Journal of Material Forming Aims and scope Submit manuscript

Abstract

High silicon content aluminum alloy (hypereutectic) possess good tribological characteristics with low coefficients of friction, when embedded with short carbon fiber (Csf), making this composite a good material choice where good wear and high strength properties are required in light weight components. There is no previously published information available, to the knowledge of the authors, regarding the influence of wear parameters and their interactions on the tribological behavior of Csf reinforced metal matrix composites. In this study a Taguchi design of experiment (DoE) was conducted to optimize and analyze the effects of the wear parameters on the tribological properties of Al/Csf metal matrix composite. A novel thixomixing method which was used to process the metal within the semisolid state was employed to embed short carbon fibers homogenously into the metal matrix. The influences of the sliding speed, applied load and volume fraction, of Csf on the specific wear rate and coefficient of friction were examined, with each of these input parameters tested at three levels(0, 4.2, 8.1%vol.). The results were indicated that Al/Csf composite had better tribological properties than Al alloy due to which contains carbon as solid lubricant. According to the statistical analysis, the influence of volume fraction of carbon fiber on wear parameters was ranked first; so the load and sliding speed are at the following rankings. The contribution percentage for each parameter was determined by the analysis of variance. The relatively good interfacial adherence of carbon fiber and matrix alloy were demonstrated. The coherent and adherent graphite-rich layer on the worn surface was characterized using scanning electron microscopy (SEM).

This is a preview of subscription content, log in via an institution to check access.

Access this article

Subscribe and save

Springer+ Basic
EUR 32.99 /Month
  • Get 10 units per month
  • Download Article/Chapter or Ebook
  • 1 Unit = 1 Article or 1 Chapter
  • Cancel anytime
Subscribe now

Buy Now

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

References

  1. Ravindran P, Manisekar K, Narayanasamy P, Selvakumar N, Narayanasamy R (2012) Mater & Des 39:42

    Article  Google Scholar 

  2. L. Liu, W. Li, Y. Tang, B. Shen, W Hu, 266, 733 (2009)

  3. Ramesh CS, Adarsha H, Pramod S, Khan Z (2013) Mater Des 50:597

    Article  Google Scholar 

  4. Suresha S, Sridhara BK (2010) Composites Sci and Technol 70:1652

    Article  Google Scholar 

  5. P. Baumli, J. Sychev, I. Budai, J.T. Szabo, G Kaptay, 44, 47 (2013)

  6. W. Yu, J Yao, 101, 3175 (2006)

  7. Even C, Arvieu C, Coutand B, Quenisset JM (2010) J of composite mater

    Google Scholar 

  8. Bhav Singh B, Balasubramanian M (2009) J of Mater Process Technol 209:2104

    Article  Google Scholar 

  9. Shalu T, Abhilash E, Joseph MA (2009) J of Mater Process Technol 209:4809

    Article  Google Scholar 

  10. Chawla N, Chawla KK (2006) JOM 58:67

    Article  Google Scholar 

  11. Deng X, Chawla N (2006) J Mater Sci 41:5731

    Article  Google Scholar 

  12. Das P, Samanta SK, Chattopadhyay H, Dutta P, Barman N (2013) In: Rheological characterization of semi-solid A356 aluminium alloy, vol 192-193. Cape Town

  13. Akbarzadeh E, Shakib SE (2011) Int J Min Met Mater 18:731

    Article  Google Scholar 

  14. Kumar R, Dhiman S (2013) Mater & Des 50:351

    Article  Google Scholar 

  15. Seong HG, Lopez HF, Robertson DP, Rohatgi PK (2008) 487, 201

    Google Scholar 

  16. Huang X (2009) 2, 2369

    Google Scholar 

  17. Burkanudeen A, Krishnan GS, Murali N (2013) J Therm Anal Calorim 112:1261

    Article  Google Scholar 

  18. P. Ravindran, K. Manisekar, R. Narayanasamy, P Narayanasamy, 39, 1169 (2013)

  19. Ramesh CS, Prasad TB (2008) J of Tribology 131:014501

    Article  Google Scholar 

  20. Davis JR (2001) Surface engineering for corrosion and wear resistance. ASM International, Materials Park, OH

    Google Scholar 

  21. A. Ureña, J. Rams, M. Campo, M Sánchez, 266, 1128 (2009)

  22. Chen H, Alpas AT (1996) 192, 186

    Google Scholar 

  23. Wilson S, Alpas AT (1997) 212, 41

    Google Scholar 

  24. T.Z. Wei, S.R.B. Shamsuri, C.S. Yee, M.W.A. Rashid, Q Ahsan, 68, 703 (2013)

  25. Koráb J, Štefánik P, Kavecký Š, Šebo P, Korb G (2002) Compos Part A: Appl Sci Manuf 33:577

    Article  Google Scholar 

  26. Mahato A, Xia S, Perry T, Sachdev A, Biswas SK (2010) Tribol Int 43:381

    Article  Google Scholar 

  27. Saklakoglu N, Irizalp SG, Ercayhan Y, Birol Y (2014) Ind Lubr Tribol 66:46

    Article  Google Scholar 

  28. Mbuyaa TO, Oderaa BO, Ng’ang’a SP (2003) Int J CastMetals Res 15:451

    Google Scholar 

  29. Abouei V, Saghafian H, Shabestari SG, Zarghami M (2010) Mater Des 31:3518

    Article  Google Scholar 

  30. Abouei V, Shabestari SG, Saghafian H (2010) Mater Charact 61:1089

    Article  Google Scholar 

  31. Ye H (2003) J Mater Eng Perform 12:288

    Article  Google Scholar 

Download references

Acknowledgments

The authors are indebted to all colleagues at Light Alloys and Surfaces Treatment Design Center (CDAL) for their kind and helpful collaboration regarding this study.

Author information

Authors and Affiliations

Authors

Corresponding author

Correspondence to Ebrahim Akbarzadeh.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Akbarzadeh, E., Picas, J.A. & Baile, M.T. Orthogonal experimental design applied for wear characterization of aluminum/Csf metal composite fabricated by the thixomixing method. Int J Mater Form 9, 601–612 (2016). https://doi.org/10.1007/s12289-015-1246-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12289-015-1246-7

Keywords

Navigation