Abstract
A hydrothermal synthesis route is used to synthesize nanomagnetic particles of Co0.3Zn0.7Fe2O4 ferrite ferrofluids with particle diameter ranging from 5.5–9 nm. XRD analysis shows the formation of a single phase spinel structure. EDX results confirm the stoichiometric composition of the cations. Small angle neutron scattering technique is used to determine the size and size distribution of Co0.3Zn0.7Fe2O4 ferrofluid. The sizes thus obtained are in the range of 5.4 to 8.4 nm. These results are in agreement with magnetic measurements.
Similar content being viewed by others
References
P Lindner and T Zemb, Neutron, X-ray and light scattering: Introduction to an investigation tool for colloids and polymeric systems (North Holland, 1991)
V K Aswal and P S Goyal, Curr. Sci. 79, 947 (2000)
R V Upadhyay, Amita Gupta, C Sudakar, K V Rao, Kinari Parekh, Rucha Desai and R V Mehta, J. Appl. Phys. 99, 08M906 (2006)
Trupti Upadhyay, R V Upadhyay, R V Mehta, V K Aswal and P S Goyal, Phys. Rev. B55, 5585 (1997)
V K Aswal, J V Joshi, P S Goyal, Rajesh Patel, R V Upadhyay and R V Mehta, Pramana — J. Phys. 63, 285 (2004)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Acharya, P., Desai, R., Aswal, V.K. et al. Structure of Co-Zn ferrite ferrofluid: A small angle neutron scattering analysis. Pramana - J Phys 71, 1069–1074 (2008). https://doi.org/10.1007/s12043-008-0225-7
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12043-008-0225-7