Abstract
Dimethylaminoethyl methacrylate maleate (DMAEMA–MA) polymerizable ionic liquid was synthesized from 2-(dimethylamino)ethyl methacrylate and maleic acid and characterized by 1HNMR and FTIR. IC-P hydrogel was prepared by hydrothermal synthesis method using 2-acrylamide-2-methylpropane sulphonic acid and acrylamide as monomers, DMAEMA–MA as crosslinker and potassium peroxodisulphate as initiator. BIS-P hydrogel was prepared by using N,N′-methylene bisacrylamide (BIS) as non-ionic crosslinker, and the performances of BIS-P and IC-P hydrogels were compared. The results showed that IC-P hydrogel had a pore structure similar to BIS-P. When the dosage of DMAEMA–MA was 1.6% (based on the total mass of monomers), the swelling rate of the prepared IC1.6 hydrogel in water can reach 235.97%, the conductivity was 58.8 μS cm−1, and the derusting effect of Q235 low carbon steel with rust grade C could reach grade A. Moreover, DMAEMA–MA could improve the thermal stability of IC-P hydrogel.
Similar content being viewed by others
References
Zhang X, Yang S W, Zhang W H and He X L 2014 Corros. Sci. 82 165
Michelin A, Drouet E, Foy E, Dynes J J, Neff D and Dillmann P 2013 J. Anal. At. Spectrom. 28 59
Sørensen P A, Kiil S K, Johansen K D and Weinell C E 2009 J. Coat. Technol. Res. 6 135
Ishikawa T, Ueno T, Yasukawa A, Kandori K, Nakayama T and Tsubota T 2003 Corros. Sci. 45 1037
Odhiambo D and Soyama H 2003 Int. J. Fatigue 25 1217
Negm N A, Ghuiba F M and Tawfik S M 2011 Corros. Sci. 53 3566
Zhang S T, Tao Z H, Li W H and Hou B R 2009 Appl. Surf. Sci. 255 6257
Collazo A, Nóvoa X R, Pérez C and Puga B 2010 Electrochim. Acta 55 6156
Barchiche C, Sabot R, Jeannin M and Refait P 2010 Eletrochim. Acta 55 1940
Qin T T, Li J, Luo H Q, Li M and Li N B 2011 Corros. Sci. 53 1072
Domingues J A L, Bonelli N, Giorgi R, Fratini E, Gorel F and Baglioni P 2013 Langmuir 29 2746
Carretti E, Grassi S, Cossalter M, Natali I, Baglioni P and Dei L 2009 Langmuir 25 8656
Natali I, Carretti E, Angelova L, Baglioni P, Weiss R G and Dei L 2011 Langmuir 27 13400
Wolbers R 1994 Recent developments in the use of gel formulations for the cleaning of paintings. in Restoration’92: conservation, training, materials and techniques: latest developments (London: IIC)
Silveira L D 1997 Stud. Conserv. 42 11
Sosa M O, Contreras A G, Durán C F A G, García R G and Palestino G 2019 J. Appl. Polym. Sci. 48403 1
Cowan M G, Gin D L and Noble R D 2016 Acc. Chem. Res. 49 724
Kçddermann T, Klembt S, Klasen D, Paschek D, Kragl U and Ludwig R 2012 ChemPhysChem 13 1748
Gu H, Yan F and Texter J 2016 J. Commun. 34 1218
Ludwig R and Kragl U 2007 Angew. Chem. Int. Ed. 46 6582
Wei X J, Li H B, Zhang Q H, Yu P, Chen Q H and Jin K 2020 J. Pre. 69 1607
Rodrigues A S M C, Fernandes A M, Dévemy J, Gomes M C and Santos L M N B F 2019 J. Mol. Liq. 282 385
Chen G Y, Kang S J, Ma Q S, Chen W Q and Tang Y C 2014 Magn. Reson. Chem. 52 673
Monteiro B, Maria L, Cruz A, Carretas J M, Marçalo J and Leal J P 2020 Thermochim. Acta 684 178482
Williams M L, Holahan S P, McCorkill M E, Dickmann J S and Kiran E 2018 Thermochim. Acta 669 126
Neumann J, Grundmann O, Thöming J, Schulte M and Stolte S 2010 Green Chem. 12 260
Liu H F, Zhang Z M and Li H Y 2003 J. Shanxi Univ. 4 356
Sun L J, Li Y M and Gu G W 2005 Sichuan Environ. 1 61
Gurdag G and Kurtulus B 2010 Ind. Eng. Chem. Res. 49 12675
Sejdic J T and Easteal A J 2000 Polymer 41 7451
State Bureau of Technical Supervision 1989 Rust grades and preparation grades of steel surfaces before application of paints related products: GB 8923-88[S]
Yang J C, Jablonsky M J and Mays J W 2002 Polymer 43 5125
Wei W, Li J J, Qi X L, Zhong Y, Su T and Zhang J F 2017 Carbohydr. Polym. 177 275
Ren Y Y, Guo J N, Liu Z Y and Yan F 2019 Sci Adv. 5 648
Weng T T, Guo J W, Li X M, Cui Y D, Howel C A and Sandeman S R 2014 Des. Monomers Polym. 17 140
Weng T T, Guo J W, Li X M, Cui Y D, Mikhalovska L I and Savina I N 2014 Int. J. Polym. Polym. Biomater. 63 73
Ma G H, Xu Y J, Fan B and Liang B R 2007 Euro. Polym. J. 43 2221
Singh B, Sharma N and Chauhan N 2007 Carbohydr. Polym. 69 631
Gurdag G and Cavus S 2006 Polym. Adv. Technol. 17 878
Huang Y, Liu J, Wang J Q, Hu M M, Liang G J and Zhi C Y 2018 Angew. Chem. Int. Ed. 57 9810
Yoshizawa M, Ogihara and Ohno H 2002 Polym. Adv. Technol. 13 589
Acknowledgements
This work was supported by Jilin Province Science and Technology Development plan project (20180201019SF), the Research Fund of Science and Technology Department of Jilin Province (20100551) and special project of Industrial Technology Research and Development in Jilin Province (2013779).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Sun, J., Wang, J., Wang, H. et al. Properties of ionic liquid cross-linked hydrogels and their application of derusting. Bull Mater Sci 44, 183 (2021). https://doi.org/10.1007/s12034-021-02471-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s12034-021-02471-w