Abstract
Surface of \(\hbox {TiO}_{2}\) is known to chemically bind the polysulfides in Li–S cell. In the present study, the effect of surface defects or oxygen vacancies in \(\hbox {TiO}_{2}\) present as a composite with sulfur cathode on the performance of Li–S cell was investigated by using \(\hbox {NaBH}_{4}\) reduced (black colour) \(\hbox {TiO}_{2}\) and pristine (white) \(\hbox {TiO}_{2}\) in cathode. Results show that former is superior in performance.
Similar content being viewed by others
References
Evers S and Nazar L F 2013 Acc. Chem. Res. 46 1135
Evers S, Yim T and Nazar L F 2012 J. Phys. Chem. C 116 19653
Ji X, Lee K T and Nazar L F 2009 Nat. Mater. 8 500
Liang C, Dudney N J and Howe J Y 2009 Chem. Mater. 21 4724
Zhang C, Wu H B, Yuan C, Guo Z and Lou X W 2012 Angew. Chem. Int. Ed. 51 9592
Yang C-P, Yin Y-X, Ye H, Jiang K-C, Zhang J and Guo Y-G 2014 ACS Appl. Mater. Interfaces 6 8789
Song J, Xu T, Gordin M L, Zhu P, Lv D, Jiang Y-B et al 2014 Adv. Funct. Mater. 24 1243
Guo M-Q, Huang J-Q, Kong X-Y, Peng H-J, Shui H, Qian F-Y et al 2016 New Carbon Mater. 31 352
Ding B, Shen L, Xu G, Nie P and Zhang X 2013 Electrochim. Acta 107 78
Wang S, Yang Z, Zhang H, Tan H, Yu J and Wu J 2013 Electrochim. Acta 106 307
Wei Seh Z, Li W, Cha J J, Zheng G, Yang Y, McDowell M T et al 2013 Nat. Commun. 4 1331
Tang H, Yao S, Jing M, Wu X, Hou J, Qian X et al 2015 J. Alloys Compd. 650 351
Zhao C, Shen C, Xin F, Sun Z and Han W 2014 Mater. Lett. 137 52
Tao X, Wang J, Liu C, Wang H, Yao H, Zheng G et al 2016 Nat. Commun. 7 11203
Xie K, Han Y, Wei W, Yu H, Zhang C, Wang J-G et al 2015 RSC Adv. 5 77348
Grätzel M 2001 Nature 414 338
Wang W, Lu C, Ni Y, Su M and Xu Z 2012 Appl. Catal. B 127 28
Chen X, Liu L, Yu P Y and Mao S S 2011 Science 331 746
Tan H, Zhao Z, Niu M, Mao C, Cao D, Cheng D et al 2014 Nanoscale 6 10216
Myung S-T, Kikuchi M, Yoon C S, Yashiro H, Kim S-J, Sun Y-K et al 2013 Energy Environ. Sci. 6 2609
Shen J, Wang H, Zhou Y, Ye N, Li G and Wang L 2012 RSC Adv. 2 9173
Chen J, Ding Z, Wang C, Hou H, Zhang Y, Wang C et al 2016 ACS Appl. Mater. Interfaces 8 9142
Jiang X, Zhang Y, Jiang J, Rong Y, Wang Y, Wu Y et al 2012 J. Phys. Chem. C 116 22619
Acknowledgements
University Grants Commission, India and Evonik, India, are acknowledged for Dr D S Kothari’s postdoctoral research fellowship (SPM) and \(\hbox {TiO}_{2}\) (P25), respectively.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mohanty, S.P., Nookala, M. Effect of surface modification of \(\hbox {TiO}_{2}\) on the electrochemical performance of lithium–sulfur cell. Bull Mater Sci 41, 136 (2018). https://doi.org/10.1007/s12034-018-1656-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s12034-018-1656-5