Abstract
Lanthanum-substituted SrBi4Ti4O15 (SBTi) ceramic, that is SrBi4−x La x Ti4O15 (SBLTi), samples were calcined by solid-state reaction and densified using the microwave sintering and conventional sintering techniques. Their structural, morphological and mechanical properties were investigated. The microwave sintered samples showed high densities like 95% of the theoretical density with short duration exposures. Compared with SBTi ceramics and other lanthanide-substituted compositions, the incorporation of La 3+ results in clear improvement in properties for SBLT (x ∼0.75) with respect to the values of hardness and Young’s modulus of the microwave sintered samples (8.8–12.5 and 160–180 GPa) are higher than that for conventional sintered (8–10 and 135–155 GPa) samples.
Similar content being viewed by others
References
Hao J, Xu Z, Chu R and Zhang Y 2010, J. Adv. Mater. Res. 105–106 248
Suhua F, Wen C and Fengqing Z 2007, J. Rare Earths 25 317
Fang Y, Agrawal D K, Roy D M and Roy R 1994, J. Mater. Res. 9 180
Oliver W C and Pharr G M 1992, J. Mater. Res. 7 1564
Patro P K 2006, Trans. Ind. Inst. Met. 59 229
Lan C, Jiang Y and Yang S 2011, J. Mater. Sci. 46 734
Lawita P, Watcharapasorn A and Jiansirisomboon S 2012, J. Microsc. Soc. Thailand 5 71
Fang C Y, Randal C A and Lanagan M T 2009, J. Electroceram. 22 152
Ricote J, Pardo L and Jimenz B 1994, J. Mater. Sci. 29 3248
Pamu D, James Raju K C and Lakshiminarayana Rao G 2008, J. Indian Ceram. Soc. 67 1
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
RAMBABU, A., JAMES RAJU, K.C. Effect of increasing lanthanum substitution and the sintering procedures on the properties of SrBi4Ti4O15 ceramics. Bull Mater Sci 38, 1375–1380 (2015). https://doi.org/10.1007/s12034-015-1023-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-015-1023-8