Abstract
Fabrication of TiO2 nanoporous films was carried out by anodic oxidation using two-step voltage mode while the subsequent attaching of the photosensitizer 5,10,15,20-tetra(4-carboxyphenyl) porphyrin (TCPP) on the prepared TiO2 nanoporous films was carried out by the electrochemical method. Photoelectrochemical properties of TiO 2 nanoporous films attached with and without photosensitizer TCPP were analysed by fluorescence spectroscopy and electrochemical test. Effects of process parameters on the photoelectrochemical properties of TiO2 nanoporous films were also investigated. The optimized process parameters for the preparation of TiO2 nanoporous films with the best photoelectrochemical property can be concluded as follows: oxidation potentials is 70–140 V, oxidation temperature is 25∘C, H2SO4 electrolyte concentration is 0.5 mol l−1 and oxidation time is 60 min. The results also show that attaching of the photosensitizer TCPP on the TiO2 nanoporous films can indeed improve the properties of TiO2 nanoporous films, and the optimized attaching temperature and attaching voltage are 25∘C and 60 V, respectively.
Similar content being viewed by others
References
Chen J K, Fu W Y, Yuan G Y, Runa A, Bala H., Wang X D, Sun G, Cao J L and Zhang Z Y 2014 Mater. Lett. 135 229
Zhao Z Y, Zhou Y, Wan W C, Wang F, Zhang Q and Lin Y H 2014 Mater. Lett. 130 150
Palmas S, Pozzo A D, Mascia M, Vacca A, Ardu A, Matarrese R and Nova I 2011 Int. J. Hydrogen Energy 36 8894
Ma T, Inoue K, Noma H, Yao K and Abe E 2002 J. Photochem. Photobiol. A. 152 207
Imahori H, Iijima H, Hayashi H, Toude Y, Umeyama T, Matano Y and Ito S 2011 ChemSusChem 4 797
Imahori H, Kang S, Hayashi H, Haruta M, Kurata H, Isoda S, Canton S E, Infahsaeng Y, Kathiravan A, Pascher T, Chábera P, Yartsev A P and Sundström V 2011 J. Phys. Chem. A 115 3679
Li Z H, Zhou X D, Wang D J, Zou X, Wang Y N and Zou G T 2007 Chem. Res. Chin. Univ. 28 1151
Pan K, Liu Z Y, Xu J J, Yu M, Wang D J, Bai Y B and Li T J 2004 Chem. Res. Chin. Univ. 25 934
Wang C, Yang G M, Li J, Mele G, Słota R, Broda M A, Duan M Y, Vasapollo G, Zhang X F and Zhang F X 2009 Dyes Pigm. 80 321
Meen T H, Water W, Chen W R, Chao S M, Ji L W and Huang C J 2009 J. Phys. Chem. Solids 70 472
Warnan J, Favereau L, Pellegrin Y, Blart E, Jacquemin D and Odobel F 2011 J. Photochem. Photobiol. A 226 9
Sule E E and Gulsah T 2011 Renew. Energy 36 1821
Gong Y L, Ren Y X, Yang Y, Bai Z C and Guo H T 2007 J. Chem. Ind. Eng. (China) 12 3185
Buntem R, Intasiri A and Lueangchaichaweng W 2010 J. Colloid Interface Sci. 347 8
Gong Y L, Li F H, Bai Z C and Yang Y 2010 Mater. Prot. (China) 43 37
Acknowledgements
This work was attached by the National Training Programs of Innovation and Entrepreneurship for Undergraduates (201410069022), Tianjin University of Commerce Training Programs of Innovation and Entrepreneurship for Undergraduates (2014090) and National Science Foundation of China (11272231).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
GONG, YL., LI, FH., LU, F. et al. Studies on the preparation and the photoelectrochemical properties of the nanoporous titania films attached with and without photosensitizer TCPP. Bull Mater Sci 38, 847–856 (2015). https://doi.org/10.1007/s12034-015-0950-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-015-0950-8