Abstract
6-(3-triethoxysilylpropyl)amino-1, 3, 5-triazine-2, 4-dithiol monosodium (TES) was used to fabricate self-assembled film on corona pretreated acrylonitrile–butadiene–styrene (ABS) resin surface. The self-assembled film modified ABS resin was treated by electroless copper plating. Orthogonal test was carried out to study optimal condition of the process. The surface appearance, plating rate and thickness of electroless copper films were investigated to determine the optimal time of corona-discharge, self-assembly and electroless copper plating. SEM results indicated that porous morphology appeared on ABS resin surface modified by TES self-assembled film and the surface roughness also increased. The adhesion test showed that the adhesion property between ABS resin and copper was excellent. The surface of electroless copper film had high brightness under the optimal condition of 1 min corona-discharge, 30 min self-assembly and 10 min electroless copper plating. The electroless-copper plating temperature was 55 ∼ 60°C and pH was 13 ∼ 13·5.
Similar content being viewed by others
References
Ali A E H and Aal A A 2009 Polym. Adv. Technol. 20 729
Charbonnier M, Romand M, Harry E and Alami M 2001 J. Appl. Electrochem. 31 57
Charbonnier M, Goepfert Y, Romand M and Leonard D 2004 J. Adhesion 80 1103
Chen H Y, Zhu Y L and Li C Q 2008 Mater. Res. Appl. 2 261
Garcia A, Berthelot T, Viel P, Mesnage A, Roussel S and Palacin S 2010 ACS Appl. Mater. Inter. 2 1177
Harper C A and Petrie E M 2003 Plastics Materials and Processes: A Concise Encyclopedia (New York: John wiley & sons. Inc.)
Kumar A, Biebuyck H A, Abbott N L and Whitesides G M 1992 J. Am. Chem. Soc. 114 9188
Laibinis P E and Whitesides GM 1992 J. Am. Chem. Soc. 114 9022
Lee S, Park S S and Lee H K 2007 Macromol. Symp. 249–250 586
Li Z, Li N, Yin L, He Y and Wang Z 2009 Electrochem. Solid St. 12 92
Nicolas D D, Pascu M, Vasile C and Poncin E F 2006 Surf. Coat. Technol. 200 4257
Nuzzo R G, Dubois L H and Allara D L 1992 J. Am. Chem. Soc. 112 558
Paunovic M 2010 Modern Electroplating Fifth edition 433 (New York: John wiley & sons. Inc.)
Wang F, Li Y N,Wang Y B and Cao Z 2011 Nanoscale Res. Lett. 6 483
Wang G X, Li N, Hu H L and Yu Y C 2006 Appl. Surf. Sci. 253 480
Zhang J Y, Esrom H, Kogelschatz U and Emig G 1994 J. Adhes. Sci. Technol. 8 1179
Acknowledgments
The authors gratefully acknowledge the project supported by the NationalNatural Science Foundation of China (GrantNo. 21203152) and Undergraduate Scientific and Technological Innovation Project (No. 1201210712133).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
ZHANG, H.N., WANG, J., SUN, F.F. et al. Study of electroless copper plating on ABS resin surface modified by heterocyclic organosilane self-assembled film. Bull Mater Sci 37, 71–76 (2014). https://doi.org/10.1007/s12034-014-0615-z
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-014-0615-z