Abstract
Magnetron-sputter deposition was used to produce a Ti-48Al-8Cr-2Ag (at.%) coating on a cast alloy substrate with the same composition. The oxidation behaviour of the cast Ti-48Al-8Cr-2Ag alloy and its sputtered coating was investigated in air at 1000°C. The resulting scale structures were analyzed in great detail by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The nanocrystalline coating showed higher oxidation rate than the cast alloy, because an outer TiO2 layer formed over a finegrain Al2O3 scale on the coating. The oxidation mechanism was discussed.
Similar content being viewed by others
References
Becker S, Rahmel A and Schorr M 1992 Oxid Met. 38 425
Brady M P, Smialke J L and Humphray D L 1997a Acta Metall. Meter. 45 2371
Brady M P, Smialke J L and Smith J 1997b Acta Metall. Meter. 45 2357
Dettenwanger F, Schumann E, Ruhle M, Rakowski J and Meier G H 1998 Oxid Met. 50 269
Fukumoto M, Hara M and Nagataki T 2004 Oxid. Met. 61 1
Kim Y M 1989 J. Met. 42 24
Kim Y M 1995 J. Met. 47 38
Lou H Y, Zhu S L and Wang F H 1995 Oxid. Met. 48 317
Luthra K L 1991 Oxid.Met. 36 475
Marie-Pierre B, Benoit G and Pieere J 2003 Surf. Coat. Technol. 162 248
Nishimoto T, Izumi T, Shigenari and Natta T 2003 Intermetallics 11 225
Shemet V, Tyagi A K and Becker J S 2000 Oxid. Met. 54 211
Tang Z, Shemet V, Niewolak L and Quadakkers W J 2003 Intermetallics 11 1
Tang Z, Wang F H and Wu W T 1997 Oxid. Met 48 511
Wang F H, Lou H Y and Wu W T 1995 Oxid. Met. 43 395
Xiang Z D, Rose S R and Datta P K 2003 Mater Chem. Philos. 80 482
Xiong YM, Zhu S L, Wang F H and Lee C H 2008 Coat.Technol. Res. 5 93
Xi Y J, Wang F H and He L L 2004 Mater. Sci. Forum 461 1181
Yang S L, Wang F H, Sun Z M and Zhu S L 2002 Intermetallics 10 467
Zhu M, Li M S, Duo S W and Zhou Y C 2007 J. Mater. Sci. Technol. A23 373
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Xi, Y.J., Liu, Y.J. High temperature oxidation of Ti-48Al-8Cr-2Ag alloy with sputtered coating at 1000°C in air. Bull Mater Sci 34, 811–814 (2011). https://doi.org/10.1007/s12034-011-0199-9
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-011-0199-9