Abstract
Nanocrystalline NiO has been prepared successfully by a simple chemical route using NiCl2·6H2O and NaOH aqueous solution at a temperature of 70°C. The prepared material has been characterized from XRD, SEM, and M–H characteristics. It has been found that NiO nanocrystals have been formed which shows a superparamagnetic/superantiferromagnetic behaviour.
Similar content being viewed by others
References
Anderson P W 1950 Phys. Rev. 79 350
Biju V and Khadar M A 2001 Mater. Sci. Engg. A304–306 814
Bødker F, Hansen M F, Bender Koch C, Lefmann K and Mørup S 2000a Phys. Rev. B61 6826
Bødker F, Hansen M F, Koch C B and Mørup S 2000b J. Magn. Magn. Mater. 221 32
Chen Qi and Zhang Z John 1998 Appl. Phys. Lett. 73 3156
Deki S, Yanagimoto H, Hiraoka S, Akamatsu K and Gotoh K 2003 Chem. Mater. 15 4916
Eberhart J P 1989 Analyse Structurale et Chimiques des Matériaux (Paris: Ed. Dunod) 46 p. 407
Gleiter H 2000 Acta Mater. 48 1
Khadar M Abdul, Biju V and Akihisa Inoue 2003 Mater. Res. Bull. 38 1341
Kittel C 1974 Introduction to solid state physics (New Delhi: Wiley Eastern Private Limited) p. 570
Kodama R H, Makhlouf S A and Berkowitz A E 1997 Phys. Rev. Lett. 79 1393
McHenry M E and Laughlin D E 2000 Acta Mater. 48 223
Neel L 1961 C. R. Acad. Sci. Paris 252 4075, 253 9, 203, 1286
Neel L 1962 Low temperature physics (eds) C Dewitt et al (New York: Gordon and Breach) p. 413
Schuele W J and Deetscreek V D 1962 J. Appl. Phys. Suppl. 33 1136
Singer J R 1956 Phys. Rev. 104 929
Wang X, Li L, Zhang Y, Wang S, Zhang Z, Fei L and Qian Y 2006 Cryst. Growth & Des. 6 2163
Wildpaner V 1974 Zeitschrift fur Physik A Hadrons and Nuclei 270 215
Xu C, Hong K, Liu S, Wang G and Zhao X 2003 J. Cryst. Growth 255 308
Zhang X X, Tejada J, Hernandez J M and Ziolo R F 1997 Nanostruct. Mater. 9 301
Zheng Y and Zhang M 2007 Mater. Lett. 61 3967
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
SRIVASTAVA, N., SRIVASTAVA, P.C. Realizing NiO nanocrystals from a simple chemical method. Bull Mater Sci 33, 653–656 (2010). https://doi.org/10.1007/s12034-011-0142-0
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12034-011-0142-0