Practical adhesion measurements of protective coatings on bronze by three-point bending test

Journal of Coatings Technology and Research volume 16, pages 1465–1477 (2019)Cite this article

Abstract

When attempting to sufficiently protect outdoor bronze monuments from corrosion, searches for an effective solution are usually based on coating applications which have a high anticorrosive efficiency. In order to correctly assess the level of protection provided by such coatings, adherence (practical adhesion) measurements need to be performed for the proper evaluation of the deterioration of coating systems with aging. Although a coupled study of adherence with aging would be of great interest, very few such studies are available. In this work, a methodological approach is proposed for the evaluation of coatings applied to metallic cultural heritage monuments of, based on the use of a three-point bending test. Adherence characterization of different protective coatings has been performed both on bare and on traditionally black-patinated bronze coupons (Cu–Sn alloy with 5.9 wt% Sn), which were used as basic model substrates. The investigated coatings were Incralac®, silane, sol–gel oxysilane, and a silane-modified polymethacrylate (an adhesion promoter for fluoropolymer). The results of measurements which were obtained before and after accelerated aging in concentrated acid rain made it possible to more easily differentiate between the various adherence levels of different coating systems. Coupled with adherence measurements, the results of systematic optical and SEM observation of the different failure morphologies are also presented. In the case of the coated bare alloy, adhesive failures were mainly observed. The silane (PropS-SH) coating showed the best adherence. In the case of the patinated bronze test specimens, only cohesive failures occurred. Adherence is directly related to the cohesion of the black patina rather than that of the applied coating. It was observed that aging reduces the level of the adherence.

This is a preview of subscription content, access via your institution.

Access options

Buy single article

Instant access to the full article PDF.

USD 39.95

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

References

  1. Texier, A, Azema, A, “Open Air Metal—Outdoor Metallic Sculpture from the 19th to the Early 20th Century: Identification, Conservation, Restoration.” Int. Conf. 2014 SF-IIC/ICOMOS, p 288, Paris (2015)

  2. Pilz, M, Römich, H, “Sol–Gel Derived Coating for Outdoor Bronze Conservation.” J. Sol-Gel Sci. Technol., 8 1071–1075 (1997). https://doi.org/10.1007/BF02436986

    Google Scholar 

  3. Brunoro, G, Frignani, A, Colledan, A, Chiavari, C, “Organic Films for Protection of Copper and Bronze Against Acid Rain Corrosion.” Corros. Sci., 45 2219–2231 (2003). https://doi.org/10.1016/S0010-938X(03)00065-9

    Article  Google Scholar 

  4. Kosec, T, Legat, A, Milošev, I, “The Comparison of Organic Protective Layers on Bronze and Copper.” Prog. Org. Coat., 69 199–206 (2010). https://doi.org/10.1016/J.PORGCOAT.2010.04.010

    Article  Google Scholar 

  5. Chiavari, C, Balbo, A, Bernardi, E, Martini, C, Bignozzi, MC, Abbottoni, M, Monticelli, C, “Protective Silane Treatment for Patinated Bronze Exposed to Simulated Natural Environments.” Mater. Chem. Phys., 141 502–511 (2013). https://doi.org/10.1016/J.MATCHEMPHYS.2013.05.050

    Article  Google Scholar 

  6. Floch, V, Doleyres, Y, Amand, S, Aufray, M, Pébère, N, Verchère, D, “Adherence Measurements and Corrosion Resistance in Primer/Hot-Dip Galvanized Steel Systems.” J. Adhes., 89 339–357 (2013). https://doi.org/10.1080/00218464.2013.757510

    Article  Google Scholar 

  7. Olivier, MG, Romano, AP, Vandermiers, C, Mathieu, X, Poelman, M, “Influence of the Stress Generated During an Ageing Cycle on the Barrier Properties of Cataphoretic Coatings.” Prog. Org. Coat., 63 323–329 (2008). https://doi.org/10.1016/j.porgcoat.2008.01.018

    Article  Google Scholar 

  8. Le Manchet, S, Landoulsi, J, Richard, C, Verchère, D, “Study of a Chromium-Free Treatment on Hot-Dip Galvanized Steel: Electrochemical Behaviour and Performance in a Saline Medium.” Surf. Coat. Technol., 205 475–482 (2010). https://doi.org/10.1016/j.surfcoat.2010.07.009

    Article  Google Scholar 

  9. Miszczyk, A, Darowicki, K, “Multispectral Impedance Quality Testing of Coil-Coating System Using Principal Component Analysis.” Prog. Org. Coat., 69 330–334 (2010). https://doi.org/10.1016/j.porgcoat.2010.07.003

    Article  Google Scholar 

  10. Bajat, JB, Popić, JP, Mišković-Stanković, VB, “The Influence of Aluminium Surface Pretreatment on the Corrosion Stability and Adhesion of Powder Polyester Coating.” Prog. Org. Coat., 69 316–321 (2010). https://doi.org/10.1016/j.porgcoat.2010.07.004

    Article  Google Scholar 

  11. Ramezanzadeh, B, Attar, MM, “An Evaluation of the Corrosion Resistance and Adhesion Properties of an Epoxy-Nanocomposite on a Hot-Dip Galvanized Steel (HDG) Treated by Different Kinds of Conversion Coatings.” Surf. Coat. Technol., 205 4649–4657 (2011). https://doi.org/10.1016/j.surfcoat.2011.04.001

    Article  Google Scholar 

  12. Akid, R, Gobara, M, Wang, H, “Corrosion Protection Performance of Novel Hybrid Polyaniline/Sol-Gel Coatings on an Aluminium 2024 Alloy in Neutral, Alkaline and Acidic Solutions.” Electrochim. Acta, 56 2483–2492 (2011). https://doi.org/10.1016/j.electacta.2010.12.032

    Article  Google Scholar 

  13. Bull, SJ, Berasetegui, EG, “Chapter 7: An Overview of the Potential of Quantitative Coating Adhesion Measurement by Scratch Testing.” Tribol. Int., 39 99–114 (2006). https://doi.org/10.1016/j.triboint.2005.04.013

    Article  Google Scholar 

  14. Mittal, KL, “Adhesion Measurement of Thin Films.” Electrocompon. Sci. Technol., 3 21–42 (1976). https://doi.org/10.1155/APEC.3.21

    Article  Google Scholar 

  15. Brown, SD, “Adherence Failure and Measurement: Some Troubling Questions.” In: Mittal, KL (ed.) Adhesion Measurement of Films and Coatings, pp. 15–39. VSP, Utrecht (1995)

    Google Scholar 

  16. I. 20502 Standard, Fine Ceramics (Advanced Ceramics, Advanced Technical Ceramics)—Determination of Adhesion of Ceramic Coatings by Scratch Testing, 2005

  17. Noh, SM, Lee, JW, Nam, JH, Park, JM, Jung, HW, “Analysis of Scratch Characteristics of Automotive Clearcoats Containing Silane Modified Blocked Isocyanates via Carwash and Nano-scratch Tests.” Prog. Org. Coat., 74 192–203 (2012). https://doi.org/10.1016/j.porgcoat.2011.12.009

    Article  Google Scholar 

  18. Malzbender, J, den Toonder, JMJ, Balkenende, AR, de With, G, “Measuring Mechanical Properties of Coatings: A Methodology Applied to Nano-particle-Filled Sol–Gel Coatings on Glass.” Mater. Sci. Eng. R Rep., (2002). https://doi.org/10.1016/s0927-796x(01)00040-7

    Google Scholar 

  19. I. 1518-1 Standard, Paints and Varnishes—Determination of Scratch Resistance—Part 1: Constant-Loading Method (2011)

  20. I. 1518-2 Standard, 2011 Paints and Varnishes—Determination of Scratch Resistance—Part 2: Variable-Loading Method (2011)

  21. Vaughn, GD, Frushour, BG, Dale, WC, “Scratch Indentation, A Simple Adhesion Test Method for Thin Films on Polymeric Supports.” J. Adhes. Sci. Technol., 8 635–650 (1994). https://doi.org/10.1163/156856194X00393

    Article  Google Scholar 

  22. Matthews, KHA, Coatings Tribology, Volume 56: Properties, Mechanisms, Techniques and Applications in Surface Engineering, 2nd ed. Elsevier Science, Amsterdam (2009)

    Google Scholar 

  23. Roche, AA, Dole, P, Bouzziri, M, “Measurement of the Practical Adhesion of Paint Coatings to Metallic Sheets by the Pull-Off and Three-Point Flexure Tests.” J. Adhes. Sci. Technol., 8 587–609 (1994). https://doi.org/10.1163/156856194X00366

    Article  Google Scholar 

  24. Genty, S, Sauvage, J-B, Tingaut, P, Aufray, M, “Experimental and Statistical Study of Three Adherence Tests for an Epoxy-Amine/Aluminum Alloy System: Pull-Off, Single Lap Joint and Three-Point Bending tests.” Int. J. Adhes. Adhes., 79 50–58 (2017). https://doi.org/10.1016/j.ijadhadh.2017.09.004

    Article  Google Scholar 

  25. Roche, AA, Behme, AK, Solomon, JS, “A Three-Point Flexure Test Configuration for Improved Sensitivity to Metal/Adhesive Interfacial Phenomena.” Int. J. Adhes., 2 249–254 (1982). https://doi.org/10.1016/0143-7496(82)90032-X

    Article  Google Scholar 

  26. Zucchi, F, Grassi, V, Frignani, A, Trabanelli, G, “Inhibition of Copper Corrosion by Silane Coatings.” Corros. Sci., 46 2856–2865 (2004). https://doi.org/10.1016/j.corsci.2004.03.019

    Article  Google Scholar 

  27. Monticelli, C, Grassi, V, Martini, C, Chiavari, C, Mavilia, G, Zanotto, F, Masi, G, Bernardi, E, “Protectiveness of Different Silane Coatings on Patinated Ancient and Modern Bronzes: Part 1.” In: EUROCORR 2017 20th ICC Process Saf. Congr. 2017, Eur. Fed. Corros. Event No. 417, Prague (Czech Republic), 2017: p. Paper n. 82171

  28. Masi, G, Martini, C, Bernardi, E, Bignozzi, MC, Monticelli, C, Balbo, A, Zanotto, F, Aufray, M, Josse, C, Esvan, J, Robbiola, L, “Protectiveness of Different Silane Coatings on Patinated Ancient and Modern Bronzes: Part 2.”, In: EUROCORR 2017 20th ICC Process Saf. Congr. 2017, Eur. Fed. Corros. Event No. 417, Prague (Czech Republic), 2017 Paper n. 95722

  29. Bescher, E, Mackenzie, JD, “Sol–Gel Coatings for the Protection of Brass and Bronze.” J. Sol-Gel Sci. Technol., 26 1223–1226 (2003)

    Article  Google Scholar 

  30. Ebnesajjad, S, “Applied Plastics Engineering Handbook.” In: Kutz, M (ed.) Applied Plastics Engineering Handbook. Elsevier Inc., Amsterdam (2011) https://doi.org/10.1016/c2010-0-67336-6

    Google Scholar 

  31. Picard, L, Phalip, P, Fleury, E, Ganachaud, F, “Chemical Adhesion of Silicone Elastomers on Primed Metal Surfaces: A Comprehensive Survey of Open and Patent Literatures.” Prog. Org. Coat., 80 120–141 (2015). https://doi.org/10.1016/j.porgcoat.2014.11.022

    Article  Google Scholar 

  32. Marabelli, M, Napolitano, G, “Nuovi sistemi protettivi applicabili su opere o manufatti in bronzo esposti all’aperto TT—New Protective Systems Applied to Outdoor Bronze Statuary or Artifacts.” Materiali e Strutture, 1–2 51–58 (1991)

    Google Scholar 

  33. Weil, PD, “A review of the history and practice of patination.” In: Floyd Brown, B, N.B. of S. United States. (Eds.), Corros. Met. Artifacts a Dialog between Conservators. Archaeologists and Corrosion, pp. 77–92. Scientists, NBS Special Publication 479, Washington D.C. (1977)

  34. Masi, G, Josse, C, Esvan, J, Chiavari, C, Bernardi, E, Martini, C, Bignozzi, MC, Monticelli, C, Zanotto, F, Balbo, A, Svara Fabjan, E, Kosec, T, Robbiola, L, “Evaluation of the Protectiveness of an Organosilane Coating on Patinated Cu–Si–Mn Bronze for Contemporary Art.” Prog. Org. Coat., 127 286–299 (2019). https://doi.org/10.1016/j.porgcoat.2018.11.027

    Article  Google Scholar 

  35. Chiavari, C, Bernardi, E, Martini, C, Passarini, F, Ospitali, F, Robbiola, L, “The Atmospheric Corrosion of Quaternary Bronzes: The Action of Stagnant Rain Water.” Corros. Sci., 52 3002–3010 (2010). https://doi.org/10.1016/j.corsci.2010.05.013

    Article  Google Scholar 

  36. Chiavari, C, Bernardi, E, Balbo, A, Monticelli, C, Raffo, S, Bignozzi, MC, Martini, C, “Atmospheric Corrosion of Fire-Gilded Bronze: Corrosion and Corrosion Protection During Accelerated Ageing Tests.” Corros. Sci., 100 435–447 (2015). https://doi.org/10.1016/J.CORSCI.2015.08.013

    Article  Google Scholar 

  37. Sidot, E, Kahn-Harari, A, Cesari, E, Robbiola, L, “The Lattice Parameter of α-Bronzes as a Function of Solute Content: Application to Archaeological Materials.” Mater. Sci. Eng. A, 393 147–156 (2005). https://doi.org/10.1016/J.MSEA.2004.10.001

    Article  Google Scholar 

  38. Ropret, P, Kosec, T, “Raman Investigation of Artificial Patinas on Recent Bronze—Part I: Climatic Chamber Exposure.” J. Raman Spectrosc., 43 1578–1586 (2012). https://doi.org/10.1002/jrs.4068

    Article  Google Scholar 

  39. Masi, G, Esvan, J, Josse, C, Chiavari, C, Bernardi, E, Martini, C, Bignozzi, MC, Gartner, N, Kosec, T, Robbiola, L, “Characterisation of Typical Patinas Simulating Bronze Corrosion in Outdoor Conditions.” Mater. Chem. Phys., 200 308–321 (2017). https://doi.org/10.1016/j.matchemphys.2017.07.091

    Article  Google Scholar 

  40. Deanin, RD, Orroth, SA, Eliasen, RW, Greer, TN, “Mechanism of Ultraviolet Degradation and Stabilization in Plastics.” Polym. Eng. Sci., 10 228–234 (1970). https://doi.org/10.1002/pen.760100408

    Article  Google Scholar 

  41. Khramov, AN, Voevodin, NN, Balbyshev, VN, Donley, MS, “Hybrid Organo-Ceramic Corrosion Protection Coatings with Encapsulated Organic Corrosion Inhibitors.” Thin Solid Films, 447–448 549–557 (2004). https://doi.org/10.1016/j.tsf.2003.07.016

    Article  Google Scholar 

  42. Khramov, AN, Voevodin, NN, Balbyshev, VN, Mantz, RA, “Sol–Gel-Derived Corrosion-Protective Coatings with Controllable Release of Incorporated Organic Corrosion Inhibitors.” Thin Solid Films, 483 191–196 (2005). https://doi.org/10.1016/j.tsf.2004.12.021

    Article  Google Scholar 

  43. Monticelli, C, Grassi, V, Mavilia, G, Zanotto, F, “Entrapment of Corrosion Inhibitors in Silane Coatings to Improve Bronze Corrosion Protection.” In: EUROCORR 2017 20th ICC Process Saf. Congr. 2017, Eur. Fed. Corros. Event No. 417, Prague (Czech Republic), 2017 Paper n. 82386

  44. Bernardi, E, Chiavari, C, Lenza, B, Martini, C, Morselli, L, Ospitali, F, Robbiola, L, “The Atmospheric Corrosion of Quaternary Bronzes: The Leaching Action of Acid Rain.” Corros. Sci., 51 159–170 (2009). https://doi.org/10.1016/J.CORSCI.2008.10.008

    Article  Google Scholar 

Download references

Acknowledgments

This work was performed within the scope of the M-Era.Net European project BIMPACT, which was supported by national funding organizations (MIZS-Slovenia, MIUR-Italy, RMP-France). Special thanks are due to Nina Gartner for her constant administrative help during the implementation of this project.

Author information

Authors and Affiliations

  1. CIRIMAT, Université de Toulouse, CNRS, INP- ENSIACET 4 allée Emile Monso - BP44362, 31030, Toulouse Cedex 4, France

    Maëlenn Aufray

  2. Centre de Microcaractérisation Raimond Castaing (CNRS UMS 3623), Université Fédérale de Toulouse, 31000, Toulouse, France

    Claudie Josse

  3. Centro di Studi sulla Corrosione e Metallurgia “A. Daccò”, Università di Ferrara, 44121, Ferrara, Italy

    Andrea Balbo & Cecilia Monticelli

  4. Slovenian National Building and Civil Engineering Institute, Dimičeva 12, 1000, Ljubljana, Slovenia

    Erika Švara Fabjan, Luka Škrlep, Tadeja Kosec & Nina Gartner

  5. Dipartimento di Ingegneria Industriale, Università di Bologna, viale del Risorgimento 4, 40136, Bologna, Italy

    Carla Martini

  6. Dipartimento di Ingegneria Civile, Chimica, Ambientale e dei Materiali, Università di Bologna, Via Terracini, 28, 40131, Bologna, Italy

    Giulia Masi & Maria Chiara Bignozzi

  7. Dipartimento di Beni Culturali, Università di Bologna, Via degli Ariani, 1, 48121, Ravenna, Italy

    Cristina Chiavari

  8. Dipartimento di Chimica Industriale “Toso Montanari”, Università di Bologna, Viale del Risorgimento 4, 40136, Bologna, Italy

    Elena Bernardi

  9. TRACES Lab, CNRS (UMR5608), Université Toulouse, 31058, Toulouse, France

    Luc Robbiola

  10. GEIDA, Zapoge 37, 1217, Vodice, Slovenia

    Marija Babnik, Teja Koršič & Marko Kete

Authors
  1. Maëlenn Aufray
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Claudie Josse
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Andrea Balbo
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Cecilia Monticelli
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Erika Švara Fabjan
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Luka Škrlep
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Tadeja Kosec
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. Nina Gartner
    View author publications

    You can also search for this author in PubMed Google Scholar

  9. Carla Martini
    View author publications

    You can also search for this author in PubMed Google Scholar

  10. Giulia Masi
    View author publications

    You can also search for this author in PubMed Google Scholar

  11. Cristina Chiavari
    View author publications

    You can also search for this author in PubMed Google Scholar

  12. Elena Bernardi
    View author publications

    You can also search for this author in PubMed Google Scholar

  13. Maria Chiara Bignozzi
    View author publications

    You can also search for this author in PubMed Google Scholar

  14. Luc Robbiola
    View author publications

    You can also search for this author in PubMed Google Scholar

  15. Marija Babnik
    View author publications

    You can also search for this author in PubMed Google Scholar

  16. Teja Koršič
    View author publications

    You can also search for this author in PubMed Google Scholar

  17. Marko Kete
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding authors

Correspondence to Maëlenn Aufray or Luc Robbiola.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and Permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Aufray, M., Josse, C., Balbo, A. et al. Practical adhesion measurements of protective coatings on bronze by three-point bending test. J Coat Technol Res 16, 1465–1477 (2019). https://doi.org/10.1007/s11998-019-00230-5

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11998-019-00230-5

Keywords

search

Navigation