Abstract
An attempt to develop a phosphorus-based flame-retardant UV-curable agent (UV-RA) for coating application led to the synthesis of a reactive compound which can be used as crosslinker along with UV-curable epoxy acrylate oligomer to form a coating. UV-RA was characterized via FTIR, NMR, hydroxyl, and iodine values. Study based on the effects of varying amount of UV-RA incorporated in the formulation was investigated by checking thermal, mechanical, and flame-retardant properties. An enhancement in all the properties was observed with an increase in concentration of UV-RA and each coating containing UV-RA successfully portrayed flame-retardant properties. The highest loss on ignition (LOI) value obtained was 27 while the initial and final degradation temperatures increased along with the char yield. The mechanical properties did not vary much except for the low values for 20UV-RA.
Similar content being viewed by others
References
Granzow, A, “Flame Retardation by Phosphorus Compunds.” Acc. Chem. Res., 5 (11) 177–183 (1978). https://doi.org/10.1177/0734904110395469
García, M, Hidalgo, J, Garmendia, I, “Composites: Part A Wood – Plastics Composites with Better Fire Retardancy and Durability Performance.” Compos Part A., 40 1772–1776 (2009). https://doi.org/10.1016/j.compositesa.2009.08.010
Mark, H, “Flammability,” Encyclo. Polym. Sci. Tech. Con., Wiley (2013).
Chambhare, SU, Lokhande, GP, Jagtap, RN, “UV-Curable Behavior of Phosphorus- and Nitrogen-Based Reactive Diluent for Epoxy Acrylate Oligomer Used for Flame-Retardant Wood Coating.” J. Coat. Technol. Res., 13 (4) 703–714 (2016). https://doi.org/10.1007/s11998-015-9777-x
Nelson, G, Kinson, P, Quinn, C, “Fire Retardant Polymers.” Ann. Review Mater. Sci., 4 391–414 (1974). https://doi.org/10.1146/annurev.ms.04.080174.002135
Bourbigot, S, Duquesne, S, “Fire Retardant Polymers: Recent Developments and Opportunities.” J. Mater. Chem., 17 2283–2300 (2007). https://doi.org/10.1039/b702511d
Bourbigot, S, Flambard, X, “Heat Resistance and Flammability of High Performance Fibres: A Review.” Fire Mater., 168 155–168 (2002). https://doi.org/10.1002/fam.799
Wang, Z, Han, E, Ke, W, “Influence of Nano-LDHs on Char Formation and Fire-Resistant Properties of Flame-Retardant Coating.” Prog. Org. Coat., 53 (1) 29–37 (2005). https://doi.org/10.1016/j.porgcoat.2005.01.004
Pearce, E, Liepins, R, “Flame Retardants.” Enviro. Health Persp., 11 59–69 (1975)
Troitzsch, J, “Overview of Flame Retardants,” Chem. Today., 16 (1998)
Chen, X, Hu, Y, Jiao, C, Song, L, “Thermal and UV-Curing Behavior of Phosphate Diacrylate Used for Flame Retardant Coatings.” Prog. Org. Coat., 59 (4) 318–323 (2007)
Maiti, S, Banerjee, S, Palit, S, “Phosphorus Containing Polymers.” Prog. Polym. Sci., 18 227–261 (1993)
Huang, W, Chen, K, Yeh, J, Chen, K, “Curing and Combustion Properties of a PU-Coating System with UV-Reactive Phosphazene.” J. App. Polym. Sci., 85 1980–1991 (2002). https://doi.org/10.1002/app.10776
Patil, DM, Phalak, GA, Mhaske, ST, “Design and Synthesis of Bio-Based UV Curable PU Acrylate Resin from Itaconic Acid for Coating Applications.” Des. Monomers Polym., 20 269–282 (2017). https://doi.org/10.1080/15685551.2016.1231045
Lokhande, G, Chambhare, S, Jagtap, R, “Synthesis and Properties of Phosphate-Based Diacrylate Reactive Diluent Applied to UV-Curable Flame-Retardant Wood Coating.” J. Coat. Technol. Res., 14 255–266 (2017). https://doi.org/10.1007/s11998-016-9849-6
Shang, D, Sun, X, Hang, J, “Flame Resistance, Physical and Mechanical Properties Of UV-Cured Hybrid Coatings Containing Low-Hydroxyl-Content Sols Via an Anhydrous Sol-Gel Process.” Prog. Org. Coat., 105 267–276 (2017). https://doi.org/10.1016/j.porgcoat.2017.01.015
Wang, P, Yang, F, Li, L, Cai, Z, “Flame Retardancy and Mechanical Properties of Epoxy Thermosets Modified with a Novel DOPO-Based Oligomer.” Polym. Degrad. Stab., 129 156–167 (2016). https://doi.org/10.1016/j.polymdegradstab.2016.04.005
Sonnier, R, Dumazert, L, Livi, S, “Flame Retardancy of Phosphorus-Containing Ionic Liquid Based Epoxy Networks.” Polym. Degrad. Stab., 134 186–193 (2016). https://doi.org/10.1016/j.polymdegradstab.2016.10.009
Jeng, RJ, Shau, SM, Lin, JJ, “Flame Retardant Epoxy Polymers Based on All Phosphorus-Containing Components.” Eur. Polym. J., 38 683–693 (2012). https://doi.org/10.1016/S0014-3057(01)00246-4
Wang S, Xu C, Liu Y, et al., "Vanillin-Derived High-Performance Flame Retardant Epoxy Resins: Facile Synthesis and Properties." (2017). https://doi.org/10.1021/acs.macromol.7b00097
Chen, X, Jiao, C, “Thermal Degradation Characteristics of a Novel Flame Retardant Coating Using TG-IR Technique.” Polym Degrad Stab, 93 2222–2225 (2008). https://doi.org/10.1016/j.polymdegradstab.2008.09.005
Quin, L, Ye, L, Xu, G, Liu, J, Polym Degrad Stab, 96 1118–1124 (2011)
Chuan, S, Ying, L, Polymer (Guildf), 43 4277–4284 (2002)
Choia, J, Seob, J, Khanc, S, Prog. Org. Coat., 71 110–116 (2011)
Liu Y, Hsiue G, Lan C, Chiu Y, 8-Flame-Retardant Polyurethanes from Phosphorus-Containing. 1769–1780 (1996)
Liu, YL, Hsiue, GH, Lan, CW, Chiu, YS, “Phosphorus-Containing Epoxy for Flame Retardance: IV. Kinetics and Mechanism of Thermal Degradation.” Polym Degrad Stab, 56 291–299 (1997). https://doi.org/10.1016/S0141-3910(96)00177-2
Banerjee, S, Palit, SK, Maiti, S, “Phosphorus Containing Polymers. 3. Polyimidophosphonates.” J Polym Sci Part A - Polym Chem, 32 219–227 (1994)
Castilla, E, Martín, N, Pardo, L, “Minimum Phi-Divergence Estimators for Multinomial Logistic Regression with Complex Sample Design.” AStA Adv Stat Anal, 102 381–411 (2018). https://doi.org/10.1007/s10182-017-0311-6
Liu YL, Hsiue GH, Chiu YS, et al., "Synthesis and Flame-retardant Properties of Phosphorus-containing Polymers Based on Poly(4-hydroxystyrene)." J Appl Polym Sci, 59:1619–1625 (1996). https://doi.org/10.1002/(SICI)1097-4628(19960307)59:10<1619::AID-APP14>3.0.CO;2-R
Liu Y, Hsiue G, Chiu Y, Properties of Phosphate-Based Epoxy Resins. Phosphate-based Epoxy Resins 565–574 (1996)
Chao, P, Li, Y, Gu, X, et al., “Novel Phosphorus-Nitrogen-Silicon Flame Retardants and Their Application in Cycloaliphatic Epoxy Systems.” Polym Chem, 6 2977–2985 (2015). https://doi.org/10.1039/c4py01724b
Qian, X, Song, L, Bihe, Y, et al., “Organic/Inorganic Flame Retardants Containing Phosphorus, Nitrogen and Silicon: Preparation and Their Performance on the Flame Retardancy of Epoxy Resins as a Novel Intumescent Flame Retardant System.” Mater Chem Phys, 143 1243–1252 (2014). https://doi.org/10.1016/j.matchemphys.2013.11.029
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Mulge, S., Mestry, S., Naik, D. et al. Phosphorus-containing reactive agent for UV-curable flame-retardant wood coating. J Coat Technol Res 16, 1493–1502 (2019). https://doi.org/10.1007/s11998-019-00224-3
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11998-019-00224-3