Chemical and electrochemical characterization of TiO2/Al2O3 atomic layer depositions on AZ-31 magnesium alloy

  • Published:
Journal of Coatings Technology and Research Aims and scope Submit manuscript

Abstract

In this study, innovative TiO2/Al2O3 mono/multilayers were applied by atomic layer depositions (ALD) on ASTM-AZ-31 magnesium/aluminum alloy to enhance its well-known scarce corrosion resistance. Four different configurations of ALD layers were tested: single TiO2 layer, single Al2O3 layer, Al2O3/TiO2 bilayer and Al2O3/TiO2/Al2O3/TiO2 multilayer deposited using Al[(CH3)]3 (trimethylaluminum, TMA), and TiCl4 and H2O precursors. All depositions were performed at 120°C to obtain an amorphous-like structure of both oxide layers. The four coatings were then investigated using different techniques, such as scanning electron microscope (SEM), stylus profilometer, glow discharge optical emission spectrometry (GDOES) and polarization curves in 0.05-M NaCl solution. The thickness of all the coatings was around 100 nm. The layers compositions were successfully investigated by the GDOES technique, although obtained data seem to be affected by substrate roughness and differences in sputtering rates between ceramic oxides and metallic magnesium alloy. Corrosion resistance showed to be strongly enhanced by the nanometric coatings, giving lower corrosion current densities in 0.05-M NaCl media with respect to the uncoated substrate (from 10−4 to 10−6 A/cm2 for the single layers and from 10−4 to 10−8 A/cm2 for the bi- and multilayers). All polarization curves on coated samples also showed a passive region, wider for the bi-layer (from −0.58 to −0.43 V with respect to Ag/AgCl) and multilayer (from −0.53 to −0.38 V with respect to Ag/AgCl) structures.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9

Similar content being viewed by others

References

  1. Pardo, A, Merino, MC, Coy, AE, Arrabal, R, Viejo, F, Matykina, E, “Effect of Mo and Mn Additions on the Corrosion Behaviour of AISI 304 and 316 Stainless Steels in H2SO4.” Corros. Sci., 50 823–834 (2008)

    Article  CAS  Google Scholar 

  2. Alvarez-Lopez, M, Pereda, MD, del Valle, JA, Fernandez-Lorenzo, M, Garcia-Alonso, MC, Ruano, OA, Escudero, ML, “Corrosion Behaviour of AZ31 Magnesium Alloy with Different Grain Sizes in Simulated Biological Fluids.” Acta Biomater., 6 1763–1771 (2010)

    Article  CAS  Google Scholar 

  3. Yang, L-J, Wei, U-H, Hou, L-F, Zhang, D, “Corrosion Behaviour of Die-Cast AZ91D Magnesium Alloy in Aqueous Sulphate Solutions.” Corros. Sci., 52 345–351 (2010)

    Article  CAS  Google Scholar 

  4. Song, G, StJohn, D, “Corrosion Resistance of Aged Die Cast Magnesium Alloy AZ91D.” Corros. Sci., 46 1381–1399 (2004)

    Article  CAS  Google Scholar 

  5. Jönsson, M, Persson, D, Leygraf, C, “Atmospheric Corrosion of Field-Exposed Magnesium Alloy AZ91D.” Corros. Sci., 50 1406–1413 (2008)

    Article  Google Scholar 

  6. Lindstreom, R, Johansson, LG, Thompson, GE, Skeldon, P, Svensson, JE, “Corrosion of Magnesium in Humid Air.” Corros. Sci., 46 1141–1158 (2004)

    Article  Google Scholar 

  7. Song, G, Johannesson, B, Hapugoda, S, StJohn, D, “Galvanic Corrosion of Magnesium Alloy AZ91D in Contact with an Aluminium Alloy, Steel and Zinc.” Corros. Sci., 46 955–977 (2004)

    Article  CAS  Google Scholar 

  8. Songa, RG, Blawert, C, Dietzel, W, Atrens, A, “A Study on Stress Corrosion Cracking and Hydrogen Embrittlement of AZ31 Magnesium Alloy.” Mater. Sci. Eng., 399 308–317 (2005)

    Article  Google Scholar 

  9. Martin, HJ, Horstemeyer, MF, Wang, PT, “Comparison of Corrosion Pitting Under Immersion and Salt-Spray Environments on an As-Cast AE44 Magnesium Alloy.” Corros. Sci., 52 3624–3638 (2010)

    Article  CAS  Google Scholar 

  10. Wang, X, Zhu, L, Li, W, Liu, H, Li, Y, “Effects of Half-Wave and Full-Wave Power Source on the Anodic Oxidation Process on AZ91D Magnesium Alloy.” Appl. Surf. Sci., 255 5721–5728 (2009)

    Article  CAS  Google Scholar 

  11. Galio, AF, Lamaka, SV, Zheludkevich, ML, Dick, LFP, Müller, IL, Ferreira, MGS, “Inhibitor-Doped Sol–Gel Coatings for Corrosion Protection of Magnesium Alloy AZ31.” Surf. Coat. Technol., 204 1479–1486 (2010)

    Article  CAS  Google Scholar 

  12. Angelini, E, Grassini, S, Rosalbino, F, Fracassi, F, d’Agostino, R, “Electrochemical Impedance Spectroscopy Evaluation of the Corrosion Behaviour of Mg Alloy Coated with PECVD Organosilicon Thin Film.” Prog. Org. Coat., 46 107–111 (2003)

    Article  CAS  Google Scholar 

  13. Lei, T, Ouyang, C, Tang, W, Li, LF, Zhou, LS, “Preparation of MgO Coatings on Magnesium Alloys for Corrosion Protection.” Surf. Coat. Technol., 204 3798–3803 (2010)

    Article  CAS  Google Scholar 

  14. Ardelean, H, Frateur, I, Marcus, P, “Corrosion Protection of Magnesium Alloys by Cerium, Zirconium and Niobium-Based Conversion Coatings.” Corros. Sci., 50 1907–1918 (2008)

    Article  CAS  Google Scholar 

  15. Suntola, T, Antson, J, US Patent 4,058,430, 1977

  16. Ahonen, M, Pessa, M, Suntola, T, “A Study of ZnTe Films Grown on Glass Substrates Using an Atomic Layer Evaporation Method.” Thin Solid Films, 65 301–307 (1980)

    Article  CAS  Google Scholar 

  17. Lappalainen, R, Jokinen, J, Li, W-M, Ritala, M, Leskeh, M, Soininen, E, “Complementary Analysis of ALE-Grown SrS Based Thin Film Electroluminescent Structures with Ion Beam Methods.” Nucl. Instr. Meth. Phys. Res. B, 132 685–696 (1997)

    Article  CAS  Google Scholar 

  18. Lua, J, Aarik, J, Sundqvist, J, Kukli, K, Harsta, A, Carlsson, J-O, “Analytical TEM Characterization of the Interfacial Layer Between ALD HfO2 Film and Silicon Substrate.” J. Cryst. Growth, 273 510–514 (2005)

    Article  Google Scholar 

  19. Matero, R, Ritala, M, Leskelä, M, Salo, T, Aromaa, J, Forsén, O, “Atomic Layer Deposited Thin Films for Corrosion Protection.” J. Phys. IV France, 9 493–499 (1999)

    Article  CAS  Google Scholar 

  20. Bedair, SM, In: Bloor, D, Brook, RS, Flemings, MC, Mahajan, S (eds.) The Encyclopedia of Advanced Materials, Vol. 1, pp. 141–153. Pergamon, Oxford, 1994

    Google Scholar 

  21. Niisto, L, “Atomic Layer Epitaxy.” Curr. Opin. Solid State Mater. Sci., 3 147–152 (1998)

    Article  Google Scholar 

  22. Ritala, M, “Advanced ALE Processes of Amorphous and Polycrystalline Films.” Appl. Surf. Sci., 112 223–230 (1997)

    Article  CAS  Google Scholar 

  23. Leskelä, M, Ritala, M, “Atomic Layer Deposition (ALD): From Precursors to Thin Film Structures.” Thin Solid Films, 409 138–146 (2002)

    Article  Google Scholar 

  24. ASM Handbook, Vol. 4, Heat Treating. ASM International, pp. 2010–2030 (1991)

  25. Hoivik, ND, Elam, JW, Linderman, RJ, Bright, VM, George, SM, Lee, YC, “Atomic Layer Deposited Protective Coatings for Micro-Electromechanical Systems.” Sens. Actuators A, 103 100–108 (2003)

    Article  Google Scholar 

  26. Shan, CX, Hou, X, Choy, KL, “Corrosion Resistance of TiO2 Films Grown on Stainless Steel by Atomic Layer Deposition.” Surf. Coat. Technol., 202 2399–2402 (2008)

    Article  CAS  Google Scholar 

  27. Guzman, L, Marin, E, Paussa, L, Isomaki, N, Fedrizzi, L, “Protection of Silver Surfaces Against Tarnishing by Means of Alumina/Titania-Nanolayers.” Surf. Coat. Technol. (2011). doi:10.1016/j.surfcoat.2011.03.101

  28. Marin, E, Lanzutti, A, Guzman, L, Fedrizzi, L, “Atomic Layer Depositions: State of the Art and Research/Industrial Perspectives.” Corros. Rev. (2011). doi: 10.1515/CORROSRE.2011.0010.R1

  29. Shan, CX, Hou, X, Choy, KL, Choquet, P, “Improvement in Corrosion Resistance of CrN Coated Stainless Steel by Conformal TiO2 Deposition.” Surf. Coat. Technol., 202 2147–2151 (2008)

    Article  CAS  Google Scholar 

  30. Marin, E, Guzman, L, Lanzutti, A, Fedrizzi, L, Saikkonen, M, “Chemical and Electrochemical Characterization of Hybrid PVD/ALD Hard Coatings on Tool Steel.” Electrochem. Commun., 11 2060–2063 (2009)

    Article  CAS  Google Scholar 

  31. Guzman, L, Marin, E, Lanzutti, A, Borin, A, Magnan, M, Malinen, V, Fedrizzi, L, Proceedings of “E-MRS Spring Meeting,” 2009

  32. Dabosi, FJP, Morancho, R, Pounteau, D, US Patent 4980203, 1990

  33. Díaz, B, Härkönen, E, Swiatowska, J, Maurice, V, Seyeux, A, Marcus, P, Ritala, M, “Low-Temperature Atomic Layer Deposition of Al2O3 Thin Coatings for Corrosion Protection of Steel: Surface and Electrochemical Analysis.” Corros. Sci., 53 2168–2175 (2011)

    Article  Google Scholar 

  34. Aarik, J, Aidla, A, Mändar, H, Uustare, T, “Atomic Layer Deposition of Titanium Dioxide from TiCl4 and H2O: Investigation of Growth Mechanism.” Appl. Surf. Sci., 172 148–158 (2001)

    Article  CAS  Google Scholar 

  35. Shimizu, K, Brown, GM, Habazaki, H, Kobayashi, K, Skeldon, P, Thompson, GE, Wood, GC, “Influence of Surface Roughness on the Depth Resolution of GDOES Depth Profiling Analysis.” Surf. Interf. Anal., 27 153–156 (1999)

    Article  CAS  Google Scholar 

  36. Payling, R, Jones, DG, Bengtson, A, Glow Discharge Optical Emission Spectrometry. John Wiley, Chichester, 1997

    Google Scholar 

  37. Granados-Aplizar, B, Muscat, AJ, “Surface Reactions of TiCl4 and Al(CH3)3 on GaAs(100) During the First Half-Cycle of Atomic Layer Deposition.” Surf. Sci., 605 1243–1248 (2011)

    Article  Google Scholar 

  38. Ghosh, MK, Choi, CH, “Initial Adsorption Mechanisms of TiCl4 on OH/Si (100)-2 Χ 1.” Chem. Phys. Lett., 457 69–73 (2008)

    Article  CAS  Google Scholar 

  39. Dobrzanski, LA, Lukaszkowicz, K, Zarychta, A, Cunha, L, “Corrosion Resistance of Multilayer Coatings Deposited by PVD Techniques onto the Brass Substrate.” J. Mater. Process. Technol., 164–165 816–821 (2005)

    Article  Google Scholar 

  40. Gray, JE, Luan, B, “Protective Coatings on Magnesium and Its Alloys—A Critical Review.” J. Alloys Compd., 336 88–113 (2002)

    Article  CAS  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. University of Udine, via Cotonificio 108, 33100, Udine, Italy

    E. Marin, A. Lanzutti, L. Guzman & L. Fedrizzi

Authors
  1. E. Marin
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. A. Lanzutti
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. L. Guzman
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. L. Fedrizzi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to E. Marin.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Marin, E., Lanzutti, A., Guzman, L. et al. Chemical and electrochemical characterization of TiO2/Al2O3 atomic layer depositions on AZ-31 magnesium alloy. J Coat Technol Res 9, 347–355 (2012). https://doi.org/10.1007/s11998-011-9372-8

Download citation

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11998-011-9372-8

Keywords

Search

Navigation