Abstract
The serrated flow during tensile testing of Al0.5CoCrFeNi high-entropy alloy at 200–500°C and strain rates of 10−2–10−4 s−1 was evaluated in this study. The temperature range of serration flow in the stress-strain curve changed as the strain rate increased. In addition, due to increased temperature and chromium enrichment of phase B2, the strength was considerably improved. Conversely, at 400–500°C, the elongation was significantly reduced while the strength increased from 300 MPa to 500 MPa to approximately 800 MPa. These changes were attributed to the precipitation of phase B2 and the enrichment of the B2 phase with Cr.
Similar content being viewed by others
References
J.W. Yeh, S.J. Lin, T.S. Chin, J.Y. Gan, S.K. Chen, T.T. Shun, C.H. Tsau, and S.Y. Chou, Metall. Mater. Trans. A 35, 2533–2536 (2004).
J.W. Yeh, S.K. Chen, S.J. Lin, J.Y. Gan, T.S. Chin, T.T. Shun, C.H. Tsau, and S.Y. Chang, Adv. Eng. Mater. 6(5), 299–303 (2004).
Y. Zhang, Y.J. Zhou, J.P. Lin, G.L. Chen, and P.K. Liaw, Adv. Eng. Mater. 10(6), 534–538 (2008).
R. Raghavan, K.C.H. Kumar, and B.S. Murty, J. Alloys Compd. 544(15), 152–158 (2012).
Y. Zhang, T.T. Zuo, Z. Tang, M.C. Gao, K.A. Dahmen, P.K. Liaw, and Z.P. Lu, Prog. Mater. Sci. 61, 1–93 (2014).
J. Antonaglia, X. Xie, Z. Tang, C.W. Tsai, J.W. Qiao, Y. Zhang, M.O. Laktionova, E.D. Tabachnikova, J.W. Yeh, O.N. Senkov, M.C. Gao, J.T. Uhl, P.K. Liaw, and K.A. Dahmen, JOM 66(10), 2002–2008 (2014).
M.A. Hemphill, T. Yuan, G.Y. Wang, J.W. Yeh, C.W. Tsai, A. Chuang, and P.K. Liaw, Acta Mater. 60(16), 5723–5734 (2012).
M. Gao, and D. Alman, Entropy 15(10), 4504–4519 (2013).
H. Moghanni, K. Dehghani, and A. Shafiei, J. Mater. Res. Technol. 16, 1069–1089 (2022).
M.H. Tsai, and J.W. Yeh, Mater. Res. Lett. 874, 1–17 (2014).
Z. Wu, H. Bei, G.M. Pharr, and E.P. George, Acta Mater. 81, 428–441 (2014).
A. Ghaderi, H. Moghanni, and K. Dehghani, J. Mater. Eng. Perform. 30, 1–9 (2021).
K.M. Youssef, A.J. Zaddach, C. Niu, D.L. Irving, and C.C. Koch, Mater. Res. Lett. 3(2), 95–99 (2014).
L.J. Santodonato, Y. Zhang, M. Feygenson, C.M. Parish, M.C. Gao, R.J. Weber, J.C. Neuefeind, Z. Tang, and P.K. Liaw, Nat. Commun. 6, 5964 (2015).
Z. Tang, T. Yuan, C.W. Tsai, J.W. Yeh, C.D. Lundin, and P.K. Liaw, Acta Mater. 99, 247–258 (2015).
B. Cantor, I.T.H. Chang, P. Knight, and A.J.B. Vincent, Mater. Sci. Eng. A 375–377, 213–218 (2004).
Y. Zhou, D. Zhou, X. Jin, L. Zhang, X. Du and B. Li, Sci. Rep. 8, Article number: 1236 (2018).
K. Zhang, and Z. Fu, Intermetallics 28, 34–39 (2012).
S. Chen, L. Yu, J. Ren, X. Xie, X. Li, Y. Xu, G. Zhao, P. Li, F. Yang, Y. Ren, and P.K. Liaw, Sci. Rep. 6, 29798 (2016).
C.J. Tong, Y.L. Chen, J.W. Yeh, S.J. Lin, S.-K. Chen, T.T. Shun, C.H. Tsau, and S.Y. Chang, Metall. Mater. Trans. A 36A, 881–893 (2005).
E. Pink, Acta Metall. 37(7), 1773–1781 (1989).
S.Y. Chen, X. Yang, K. Dahmen, P.K. Liaw, and Y. Zhang, Entropy 16(2), 870–884 (2014).
S.Y. Chen, X. Xie, B.L. Chen, J.W. Qiao, Y. Zhang, Y. Ren, K.A. Dahmen, and P.K. Liaw, JOM 67(10), 2314–2320 (2015).
H.Y. Diao, R. Feng, K.A. Dahmen, and P.K. Liaw, Curr. Opin. Solid State Mater. Sci. 21(5), 252–266 (2017).
X.F. Wang, Y. Zhang, Y. Qiao, and G.L. Chen, Intermetallics 15(3), 357–362 (2007).
O.N. Senkov, G.B. Wilks, D.B. Miracle, C.P. Chuangd, and P.K. Liaw, Intermetallics 18, 1758–1765 (2010).
B. Gludovatz, A. Hohenwarter, D. Catoor, E.H. Chang, E.P. George, and R.O. Ritchie, Science 345(6201), 1153–1158 (2014).
X.Y. Fang, D.Q. Yi, and J.F. Nie, Metall. Mater. Trans. A 40, 2761–2771 (2009).
S. Niu, H. Kou, Y. Zhang, J. Wang, and J. Li, Mater. Sci. Eng. A Struct. Mater. Prop. Microstruct. Process. 702, 96–103 (2017).
J. Brechtl, S.Y. Chen, X. Xie, Y. Ren, J.W. Qiao, P.K. Liaw, and S.J. Zinkle, Int. J. Plast. 115, 71–92 (2019).
M.S. Bijnavandi, A. Ghaderi, and K. Dehghani, J. Mater. Eng. Perform. 25, 1–8 (2023).
H.Y. Yasuda, K. Shigeno, and T. Nagase, Scr. Mater. 108, 80–83 (2015).
L. Guo, J. Gu, X. Gong, K. Li, S. Ni, Y. Liu, and M. Song, Micron 126, 102739 (2019).
S. Chen, X. Xie, W. Li, R. Feng, B. Chen, J. Qiao, Y. Ren, Y. Zhang, K.A. Dahmen, and P.K. Liaw, Mater. Chem. Phys. 210, 20–28 (2018).
E.D. Tabachnikova, A.V. Podolskiy, M.O. Laktionova, N.A. Bereznaia, M.A. Tikhonovsky, and A.S. Tortika, Alloys Compd. 698, 501–509 (2017).
C.M. Lin, and H.L. Tsai, Intermetallics 256, 288–294 (2011).
Z. Tang, M.C. Gao, H. Diao, T. Yang, J. Liu, T. Zuo, Y. Zhang, Z. Lu, Y. Cheng, Y. Zhang, K.A. Dahmen, P.K. Liaw, and T. Egami, JOM 65, 1848–1858 (2013).
D. Wu, R.S. Chen, and E.H. Han, Mater. Sci. Eng. A 532, 267–274 (2012).
Y. Cai, C. Tian, S. Fu, G. Han, C. Cui, and Q. Zhang, Mater. Sci. Eng. A 638(25), 314–321 (2015).
P. Rodriguez, Bull. Mater. Sci. 6, 653–663 (1984).
R.P. Singh, and R.D. Doherty, Metall. Trans. A 23, 321–334 (1992).
P.G. McCormick, Acta Metall. 20(3), 351–354 (1972).
J.C. Rao, H.Y. Diao, V. Ocelík, D. Vainchtein, C. Zhang, C. Kuo, Z. Tang, W. Guo, J.D. Poplawsky, Y. Zhou, P.K. Liaw, and JTh.M. De Hosson, Acta Mater. 131(1), 206–220 (2017).
C.C. Hsieh and W. Wu, Int. Sch. Res. Not. 2012, Article ID 732471.
W.R. Wang, W.L. Wang, S.C. Wang, Y.C. Tsai, C.H. Lai, and J.W. Yeh, Intermetallics 26, 44–51 (2012).
E.J. Pickering, R. Muñoz-Moreno, H.J. Stone, and N.G. Jones, Scr. Mater. 113, 106–109 (2016).
F. Otto, A. Dlouhý, K.G. Pradeep, M. Kuběnová, D. Raabe, G. Eggeler, and E.P. George, Acta Mater. 112, 40–52 (2016).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
On behalf of all authors, the corresponding author states that there is no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Ghaderi, A., Dehghani, K. Mechanical Behavior of Al0.5CoCrFeNi HEA During Warm Deformation. JOM 76, 1962–1972 (2024). https://doi.org/10.1007/s11837-024-06378-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-024-06378-9