The organic binder CMC (carboxymethyl cellulose) was modified with nano-CaCO3 and then used to improve the compressive strength of preheated and fired pellets. SEM (scanning electron microscope) data on modified CMC (CCMC) showed that the nano-CaCO3 compactly coated the CMC surface. Studies of preheated and fired pellets’ compressive strength revealed that the CCMC has excellent bonding properties for pellets and could increase the pellet compressive strength beyond that afforded by CMC. SEM studies of pellets showed that CCMC improves the strength of preheated pellets by compacting particles and reducing pores; the increase in fired pellet strength was attributed to CCMC facilitating the bridging, bonding and recrystallization of the magnetite and hematite during pelletization.
Similar content being viewed by others
References
T.C. Eisele and S.K. Kawatra, Miner. Process. Extr. Metall. Rev. 24, 1 (2003).
S.J. Ripke and S.K. Kawatra, Miner. Metall. Process. 21, 65 (2004).
S.K. Kawatra and S.J. Ripke, Int. J. Miner. Process. 65, 141 (2002).
U. Srivastava, S.K. Kawatra, and T.C. Eisele, Metall. Mater. Trans. B Process. Metall. Mater. Process. Sci. 44, 1000 (2013).
G. Qiu, T. Jiang, H. Li, and D. Wang, Colloids Surf. A Physicochem. Eng. Asp. 224, 11 (2003).
S.P.E. Forsmo, A.J. Apelqvist, B.M.T. Björkman, and P.O. Samskog, Powder Technol. 169, 147 (2006).
X. Fan, G. Yang, X. Chen, X. He, X. Huang, and L. Gao, Powder Technol. 267, 11 (2014).
S. Lu, Z. Yuan, and C. Zhang, Powder Technol. 340, 17 (2018).
O. Sivrikaya and A.I. Arol, Powder Technol. 210, 23 (2011).
A.R. Firth, Miner. Process. Ext. Metall. 116, 93 (2007).
Y. Yang, F. Meng, T. Jiang, Y. Guo, G. Li, Q. Li, and Q. Zheng, J. Iron. Steel Res. Int. 16, 332 (2009).
G. Qiu, T. Jiang, K. Fa, D. Zhu, and D. Wang, Powder Technol. 139, 1 (2004).
H.Q. Wu, J. Tian, L.H. Xu, S. Fang, Z.Y. Zhang, and R. Chi, Miner. Eng. 127, 42 (2018).
S. Lu, Z. Yuan, J. Liu, J. Lu, L. Li, and H. Hao, Powder Technol. 301, 1183 (2016).
Z. Yuan, S. Lu, J. Liu, P. Gao, J. Lu, and L. Li, Powder Technol. 312, 38 (2017).
O. Sivrikaya and A.I. Arol, Ironmak. Steelmak. 40, 1 (2013).
J.R. Wynnyckyj and T.Z. Fahidy, Metall Mater Trans B Process Metall Mater Process Sci 5, 991 (1974).
S. Dwarapudi, T.K. Ghosh, A. Shankar, V. Tathavadkar, D. Bhattacharjee, and R. Venugopal, Int. J. Miner. Process. 99, 43 (2011).
Acknowledgements
The authors acknowledge the Fundamental Research Funds for the Central Universities (N170104018), the China Postdoctoral Science Foundation (2017M621153), the National Nature Science Foundation of China (51704057) and the Postdoctoral Science Foundation of Northeastern University (20170312).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Lu, J., Zhao, X., Yuan, Z. et al. Characterization of the Bonding Effect of Nano-CaCO3 Modified CMC on Magnetite Concentrate Pellets. JOM 71, 2549–2555 (2019). https://doi.org/10.1007/s11837-019-03537-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-019-03537-1