Evolution of Texture and Mechanical Properties of Pure Mg Processed by ECAP at Room Temperature
- 232 Downloads
Equal channel angular pressing (ECAP) was performed on extruded pure Mg, which was clad with a drilled pure Fe coat through an ECAP die to produce a pure Mg sample without obvious cracks at room temperature. After one-pass ECAP, the grain size decreased because of basal slip activation during the dynamic plastic deformation but the microstructure became inhomogeneous. The deformed texture was less scattered and inclined by ~20° from the normal direction toward the extruded direction, and low angle boundaries increased continuously. The mechanical properties decreased slightly as a result of the combined effect from a more refined microstructure and a weaker texture.
This research was completely supported by the National Natural Science Foundation of China (No. 51474152).
- 3.R.W.K. Honeycombe, The Plastic Deformation of Metals (London: Edward Arnold, 1968), p. 20.Google Scholar
- 5.A. Muralidhar, S. Narendranath, and H. Shivananda Nayaka, J. Mag. Alloys 1, 336 (2013).Google Scholar
- 14.A. Bhowmik, S. Biswas, and S.S. Dhinwal, Mater. Sci. Forum 702–703, 774 (2012).Google Scholar
- 26.M. Mabuchi, Y. Chino, and H. Iwasaki, Metall. Mater. Trans. 42, 1182 (2001).Google Scholar